Preparation of nanocrystalline TiAl powder by the HDDR process using mechanical grinding in a hydrogen atmosphere

Scripta Metallurgica et Materialia - Tập 31 - Trang 1271-1275 - 1994
K. Aoki1, Y. Itoh1, T. Masumoto1
1Institute for Materials Research, Tohoku University, Sendai 980-77, Japan

Tài liệu tham khảo

Kawabata, 1989, High Temperature Ordered Intermetallic Alloys III, Vol.133, 329 Vasudevan, 1989, Scr.Metall., 23, 467, 10.1016/0036-9748(89)90434-1 Semitatin, 1992, Metall.Trans., 23A, 1719, 10.1007/BF02804366 Imayev, 1992, Acta Metall.Mater., 40, 589, 10.1016/0956-7151(92)90408-7 Vujic, 1988, Metall.Trans., 19A, 2445, 10.1007/BF02645472 Nakamura, 1988, Powder.Metall., 31, 201, 10.1179/pom.1988.31.3.201 Chu, 1991, Scr.Metall.Mater, 25, 641, 10.1016/0956-716X(91)90106-B Christman, 1991, Scr.Metall.Mater., 25, 767, 10.1016/0956-716X(91)90222-M Takeshita, 1989, 551 Harris, 1991, J.Less.Common Met., 172–174, 1273, 10.1016/S0022-5088(06)80037-8 McGuiness, 1992, J.Alloys and Comp., 184, 243, 10.1016/0925-8388(92)90498-X Hosomi, 1994, TETSU-TO-HAGANE, 80, 83, 10.2355/tetsutohagane1955.80.1_83