Preparation and cycle performance at high temperature for Li[Ni0.5Co0.2Mn0.3]O2 coated with LiFePO4
Tóm tắt
Li[Ni0.5Co0.2Mn0.3]O2 coated with LiFePO4 was synthesized by a co-precipitation method. It consisted of the parent Li[Ni0.5Co0.2Mn0.3]O2 as the core and the LiFePO4 as the coating material, with an average particle diameter of 500 nm. The LiFePO4-coated Li[Ni0.5Co0.2Mn0.3]O2 showed no large initial capacity drop in the first cycle, which generally occurred with cathode materials bearing inactive coating layers such as Al2O3, ZnO, and MgO. Furthermore, it presented a remarkably improved cycle retention rate of over 89% until 400 cycles at 50 °C. We suggest that the LiFePO4 coating technique is a very effective tool to improve the cycle performance of Li[Ni0.5Co0.2Mn0.3]O2 at high temperatures.
Tài liệu tham khảo
Jang SB, Kang SH, Amine K, Bae YC, Sun YK (2005) Electrochim Acta 50:4168–4173. doi:10.1016/j.electacta.2005.01.037
Kim Y, Kim HS, Martin SW (2006) Electrochim Acta 52:1316–1322. doi:10.1016/j.electacta.2006.07.033
Kweon HJ, Park JJ, Seo JW, Kim GB, Jung BH, Lim HS (2004) J Power Sources 126:156–162. doi:10.1016/j.jpowsour.2003.08.037
Kannan AM, Manthiram A (2002) Electrochem Solid St 5:A167–A169. doi:10.1149/1.1482198
Sun YK, Lee YS, Yoshio M, Amine K (2002) Electrochem Solid St 5:A99–A102. doi:10.1149/1.1465375
Sun YK, Hong KJ, Prakash J (2003) J Electrochem Soc 150:A970–A972. doi:10.1149/1.1580819
Wang ZX, Liu LJ, Chen LQ, Huang XJ (2002) Solid State Ion 148:335–342. doi:10.1016/S0167-2738(02)00071-1
Kim WS, Kim SB, Heo YJ, Koh ST (2008) IMLB 2008(277)
Lee MH, Kang YJ, Myung ST, Sun YK (2004) Electrochim Acta 50:939–948. doi:10.1016/j.electacta.2004.07.038
Liu Z, Yu A, Lee JY (1999) J Power Sources 81–82:416–419. doi:10.1016/S0378-7753(99)00221-9
Zhang ZR, Gong ZL, Yang Y (2004) J Phys Chem B 108:17546–17552. doi:10.1021/jp046980h
Li J, Zhang ZR, Guo XJ, Yang Y (2006) Solid State Ion 177:1509–1516. doi:10.1016/j.ssi.2006.03.055