Preparation and Properties of Inherently Black Polyimide Films with Extremely Low Coefficients of Thermal Expansion and Potential Applications for Black Flexible Copper Clad Laminates
Tóm tắt
In the current work, a series of black polyimide (PI) films with excellent thermal and dimensional stability at elevated temperatures were successfully developed. For this purpose, two aromatic diamines including 4,4′-iminodianline (NDA) and 2-(4-aminophenyl)-5- aminobenzimidazole (APBI) were copolymerized with pyromellitic dianhydride (PMDA) to afford PIs containing imino groups (–NH–) in the molecular structures. The referenced PI film, PI-ref, was simultaneously prepared from PMDA and 4,4′-oxydianiline (ODA). The introduction of imino groups endowed the PI films with excellent blackness and opaqueness with the optical transmittance lower than 2% at the wavelength of 600 nm at a thickness of 25 μm and lightness (L*) below 10 for the CIE (Commission International Eclairage) Lab optical parameters. Meanwhile, the introduction of rigid benzimidazole units apparently improved the thermal and dimensional stability of the PI films. The PI-d film based on PMDA and mixed diamines (NDA:APBI = 70:30, molar ratio) showed a glass transition temperature (Tg) of 445.5 °C and a coefficient of thermal expansion (CTE) of 8.9 × 10−6/K in the temperature range of 50 to 250 °C, respectively. It is obviously superior to those of the PI-a (PMDA-NDA, Tg = 431.6 °C; CTE = 18.8 × 10−6/K) and PI-ref (PMDA-ODA, Tg = 418.8 °C; CTE: 29.5 × 10−6/K) films.
Từ khóa
Tài liệu tham khảo
Ma, 2019, A review on high temperature resistant polyimide films bearing heterocyclic structures and their applications, Compos. Commun., 16, 84, 10.1016/j.coco.2019.08.011
Favvas, 2017, A review of the latest development of polyimide based membranes for CO 2 separations, React. Funct. Polym., 120, 104, 10.1016/j.reactfunctpolym.2017.09.002
Spechler, 2015, A Transparent, Smooth, Thermally Robust, Conductive Polyimide for Flexible Electronics, Adv. Funct. Mater., 25, 7428, 10.1002/adfm.201503342
Zhou, 2016, Flexible and highly fluorescent aromatic polyimide: Design, synthesis, properties, and mechanism, J. Mater. Chem. C, 4, 10509, 10.1039/C6TC03889A
Cai, 2019, Synthesis and characterization of triarylamine-based polyimides for electrochromic and optoelectronic conversion behaviors, J. Appl. Polym. Sci., 137, 48808, 10.1002/app.48808
Takizawa, 2018, Enhancing photoconductivity of aromatic polyimide films by incorporating fluorinated dianhydrides and main chain triphenylamine structure, Polymer, 157, 120, 10.1016/j.polymer.2018.10.025
Mi, 2018, Transparent and soluble polyimide films containing 4,4′-isopropylidenedicyclohexanol (Cis-HBPA) units: Preparation, characterization, thermal, mechanical, and dielectric properties, J. Polym. Sci. Part. A Polym. Chem., 56, 2115, 10.1002/pola.29172
Yang, 2015, Transient color changes in oxidative-stable fluorinated polyimide film for flexible display substrates, RSC Adv., 5, 57339, 10.1039/C5RA06066D
Yu, 2017, Structure-property relationship study of partially aliphatic copolyimides for preparation of flexible and transparent polyimide films, J. Macromol. Sci. A, 54, 97, 10.1080/10601325.2016.1261622
Tapaswi, 2014, Synthesis and characterization of highly transparent and hydrophobic fluorinated polyimides derived from perfluorodecylthio substituted diamine monomers, J. Polym. Sci. A Polym. Chem., 53, 479, 10.1002/pola.27461
Liu, 2015, Synthesis of organosoluble and light-colored cardo polyimides via aromatic nucleophilic substitution polymerization, Polym. Adv. Technol., 26, 1519, 10.1002/pat.3574
Qi, 2019, Comparative studies on structure-property relationships of the polyimide films derived from the dianhydride containing alicyclic cis-ethylenic double bond, Macromol. Res., 27, 703, 10.1007/s13233-019-7091-7
Ni, 2015, A review on colorless and optically transparent polyimide films: Chemistry, process and engineering applications, J. Ind. Eng. Chem., 28, 16, 10.1016/j.jiec.2015.03.013
Jung, 2017, Correlation of stress and optical properties in highly transparent polyimides for future flexible display, Macromol. Res., 25, 971, 10.1007/s13233-017-5126-5
Zin, 2018, Polyimide for silicon solar cells with double-sided textured pyramids, Solar Energy Mater. Solar Cells, 183, 200, 10.1016/j.solmat.2018.03.015
Gao, 2015, LTPS TFT process on polyimide substrate for flexible AMOLED, J. Disp. Technol., 11, 666, 10.1109/JDT.2015.2419656
Maceiras, 2015, Enhanced charge-transfer emission in polyimides by cyano-groups doping, J. Phys. Chem. B, 119, 5685, 10.1021/acs.jpcb.5b00845
Tseng, 2018, Phosphinated polyimide hybrid films with reduced melt-flow and enhanced adhesion for flexible copper clad laminates, Prog. Org. Coat., 124, 92, 10.1016/j.porgcoat.2018.04.037
Zhang, 2017, Preparation and properties of heat-sealable polyimide films with comparable coefficient of thermal expansion and good adhesion to copper matrix, Express Polym. Lett., 11, 983, 10.3144/expresspolymlett.2017.93
Lee, 2017, Polyimide–epoxy composites with superior bendable properties for application in flexible electronics, J. Electron. Mater., 46, 4740, 10.1007/s11664-017-5382-3
Zhang, 2018, Conductive mechanism of carbon black/polyimide composite films, J. Polym. Eng., 38, 147, 10.1515/polyeng-2016-0273
Kwon, 2014, Fabrication of polyimide composite films based on carbon black for high-temperature resistance, Polym. Compos., 35, 2214, 10.1002/pc.22886
Atar, 2015, Atomic-oxygen-durable and electrically-conductive CNT-POSS-Polyimide flexible films for space applications, ACS Appl. Mater. Interf., 7, 12047, 10.1021/acsami.5b02200
Okafor, 2015, Electrochemical behavior of multifunctional graphene-polyimide nanocomposite film in two different electrolyte solutions, J. Appl. Polym. Sci., 132, 42673, 10.1002/app.42673
Yoonessi, 2017, Fabrication of graphene–polyimide nanocomposites with superior electrical conductivity, ACS Appl. Mater. Interf., 9, 43230, 10.1021/acsami.7b12104
Zhang, 2019, Molecular design, synthesis and characterization of intrinsically black polyimide films with high thermal stability and good electrical properties, J. Polym. Res., 26, 171, 10.1007/s10965-019-1835-0
Yen, 2012, Solution-processable triarylamine-based electroactive high performance polymers for anodically electrochromic applications, Polym. Chem., 3, 255, 10.1039/C1PY00346A
Seo, 2019, Polyimide/organosilicate nanocomposites: Residual stress behavior on Si wafer for multichip packaging, Mater. Lett., 247, 171, 10.1016/j.matlet.2019.03.106
Huangfu, M., Zhang, Y., Zhang, X., Liu, J., Liu, Y., Guo, Y., Huang, Q.Y., and Zhang, X. (2019). Preparation and thermal evaluation of novel polyimide protective coatings for quartz capillary chromatographic columns operated over 320 °C for high-temperature gas chromatography analysis. Polymers, 11.
Chern, 1998, High subglass transitions appearing in the rigid polyimides derived from the novel 1,6-bis(4-aminophenyl)diamantane, Macromolecules, 31, 1898, 10.1021/ma970712i
Song, 2014, Negative in-plane CTE of benzimidazole-based polyimide film and its thermal expansion behavior, Polymer, 55, 3242, 10.1016/j.polymer.2014.05.041
Choi, 2008, Soluble polyimides from unsymmetrical diamine containing benzimidazole ring and trifluoromethyl pendent group, Polymer, 49, 2644, 10.1016/j.polymer.2008.04.019
Wang, 2009, Synthesis and characterization of thermally stable, high-modulus polyimides containing benzimidazole moieties, J. Polym. Sci. A Polym. Chem., 47, 2024, 10.1002/pola.23306
Lian, 2018, Synthesis of superheat-resistant polyimides with high Tg and low coefficient of thermal expansion by introduction of strong intermolecular interaction, Macromolecules, 51, 10127, 10.1021/acs.macromol.8b02282
Chung, 2001, Soluble polyimides containing benzimidazole rings for interlevel dielectrics, Chem. Mater., 13, 2801, 10.1021/cm000838l