Prediction of static globularization of Ti-17 alloy with starting lamellar microstructure during heat treatment

Computational Materials Science - Tập 92 - Trang 224-230 - 2014
Jianwei Xu1, Weidong Zeng1, Zhiqiang Jia1, Xin Sun1, Jianhua Zhou2
1State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China
2Baoshan Iron & Steel Co., Ltd., Shanghai 200940, China

Tài liệu tham khảo

Freour, 2006, Scripta Mater., 54, 1475, 10.1016/j.scriptamat.2005.12.051 Shamblen, 1997, Metall. Mater. Trans. B, 28B, 899, 10.1007/s11663-997-0017-3 Wang, 2010, Mater. Sci. Eng. A, 527, 2559, 10.1016/j.msea.2010.01.034 Ma, 2012, Mater. Sci. Eng. A, 548, 6, 10.1016/j.msea.2012.03.022 Semiatin, 1999, Mater. Sci. Eng. A, 263, 257, 10.1016/S0921-5093(98)01156-3 Song, 2009, J. Alloys Compd., 480, 922, 10.1016/j.jallcom.2009.02.059 Stefansson, 2002, Metall. Mater. Trans. A, 33, 3527, 10.1007/s11661-002-0340-x Zherebtsov, 2011, Acta Mater., 59, 4138, 10.1016/j.actamat.2011.03.037 Park, 2012, Metall. Mater. Trans. A, 43, 977, 10.1007/s11661-011-1019-y Fan, 2012, J. Alloys Compd., 533, 1, 10.1016/j.jallcom.2012.03.113 Semiatin, 2005, Metall. Mater. Trans. A, 36, 1372, 10.1007/s11661-005-0229-6 Ramesh, 2007, J. Mater. Eng. Perform., 16, 703, 10.1007/s11665-007-9100-9 Ji, 2010, Comput. Mater. Sci., 48, 626, 10.1016/j.commatsci.2010.02.031 Reddy, 2008, Mater. Sci. Eng. A, 492, 276, 10.1016/j.msea.2008.03.030 Kapoor, 2005, J. Mater. Eng. Perform., 169, 199 Lin, 2008, J. Mater. Sci., 43, 5508, 10.1007/s10853-008-2832-6 Jalham, 2005, J. Mater. Process. Technol., 166, 392, 10.1016/j.jmatprotec.2004.08.028 Li, 2004, Acta Mater., 52, 299, 10.1016/j.actamat.2003.09.020 Bhadeshia, 1995, Mater. Sci. Technol., 11, 1046, 10.1179/mst.1995.11.10.1046 Wang, 2010, Mater. Sci. Eng. A, 527, 6193, 10.1016/j.msea.2010.06.059 Wang, 2009, Rare Met. Mater. Eng., 38, 398 Sun, 2011, Mater. Sci. Eng. A, 528, 8757, 10.1016/j.msea.2011.08.059 Eyercioglu, 2008, J. Mater. Process. Technol., 200, 146, 10.1016/j.jmatprotec.2007.09.085 Semiatin, 2007, Metall. Mater. Trans. A, 38A, 910, 10.1007/s11661-007-9088-7 Xu, 2014, J. Alloys Compd., 603, 239, 10.1016/j.jallcom.2014.03.082