Polystyrene supportedt-butyl chromates: Effect of the degree of crosslinking on reactivity
Tóm tắt
Polystyrene supportedt-butyl chromate reagents were prepared using divinylbenzene as the crosslinking agent. The extent of crosslinking was varied from 2 to 20% (2, 5, 10, 15 and 20%). These polystyrene systems appeared to be amenable to structural variations for studying the effect of the nature and extent of crosslinking on the reactivity of the attached functional groups. Polystyrene supportedt-butyl chromates, having varying crosslink densities, were used to oxidise alcohols to the carbonyl compounds. Reagents prepared from 2% crosslinked resins gave better results. A regular decrease in the extent of functionalization was noticed as the degree of crosslinking was increased and the capacity of the functional group was found to be minimum for 20% crosslinked resin.
Tài liệu tham khảo
Cantow H J and Schuster R H 1982Polym. Bull. 8 225
Vrentas J S, Duda J L and Han A G 1984J. Appl. Polym. Sci. 29 399
Drtina G J, Heilmann S M, Moren D M, Rasmussen J K, Krepski L R, Smith H K, Pranis R A and Turek T C 1996Macromolecules 29 4486
Peterlin A 1979J. Polym. Sci. Polym. Phys. Ed. 17 1741
Grieg J A and Sherrington D C 1978Polymer 19 163
Sreekumar K and Pillai V N R 1989Macromolecules 22 3303
Sarti G C 1979Polymer 20 827
Periasami M, Mohanraj S and Ford W T 1984Brit. Polym. J. 16 179
Pillai V N R and Mutter M 1982Top. Curr. Chem. 106 119
Lloyd W G and Alfrey T 1962J. Polym. Sci. 62 301
Devaky K S, George B K and Pillai V N R 1990Indian. J. Chem. A29 1045
Morawetz H 1978J. Polym. Sci. Polym. Symp. 62 271
Mathew B and Pillai V N R 1993Indian J. Technol. 31 302
Aiswaryakumari K and Sreekumar K 1996J. Appl. Polym. Sci. 59 2039
Sophiamma P N and Sreekumar K 1996J. Appl. Polym. Sci. 62 1753
Sreekumar K and Pillai V N R 1989Proc. Indian. Acad. Sci. (Chem. Sci.) 101 335
Sreekumar K and Pillai V N R 1987Polymer 28 1599
Kau J I and Morawetz H 1972Polym. Prep. Polym. Chem. Div., Am. Chem. Soc. 13 879
Tomoi M, Gote M and Kakiuchi H 1987J. Polym. Sci. Polym. Chem. 25 77
Jayakumari V G and Pillai V N R 1991J. Appl. Polym. Sci. 42 583