Photoluminescence properties of Ca2Al2O5:RE3+ (RE = Eu, Dy and Tb) phosphors for solid state lighting

Luminescence - Tập 32 Số 7 - Trang 1361-1364 - 2017
A.N. Yerpude1, V. R. Panse2, S.J. Dhoble3, N.S. Kokode4, Mudavath Srinivas5
1Department of Physics, N. H. College, Bramhapuri, Dist-Chandrapur, India
2Department of Physics, Late. B. S. Arts, N. G. Sci, A. G. Commerce College Sakharkherda, India
3Department of Physics, R.T.M. Nagpur University, Nagpur, India
4N. H. College, Bramhapuri, Dist-Chandrapur, India
5Department of Physics, Uni. College of Science, Osmania University, Hyderabad, India

Tóm tắt

AbstractCa2Al2O5:Eu3+, Ca2Al2O5:Dy3+ and Ca2Al2O5:Tb3+ phosphors were synthesized using a combustion synthesis method. The prepared phosphors were characterized by X‐ray powder diffraction for phase purity, by scanning electron microscopy for morphology, and by photoluminescence for emission and excitation measurements. The Ca2Al2O5:Eu3+ phosphors could be efficiently excited at 396 nm and showed red emission at 594 nm and 616 nm due to 5D0 → 7F1 and 5D0 → 7F2 transitions. Dy3+‐doped phosphors showed blue emission at 482 nm and yellow emission at 573 nm. Ca2Al2O5:Tb3+ phosphors showed emission at 545 nm when excited at 352 nm. Concentration quenching occurred in both Eu3+ and Dy3+phosphors at 0.5 mol%. Photoluminescence results suggested that the aluminate‐based phosphor could be a potential candidate for application in environmentally friendly based lighting technologies.

Từ khóa


Tài liệu tham khảo

10.1016/j.saa.2009.08.011

10.1039/C5DT00875A

10.1016/j.ijleo.2015.11.030

10.1016/j.ijleo.2016.02.031

10.1016/j.physb.2014.05.070

10.1016/j.jlumin.2013.07.035

10.1016/j.jlumin.2012.01.031

10.1007/s00339-016-9733-3

10.1016/j.jlumin.2012.04.037

10.1016/S1002-0721(14)60165-4

10.1039/c1jm13351a

10.1557/mrs2009.28

10.1016/j.ijleo.2012.11.064

10.1016/j.jallcom.2010.01.039

10.5185/amlett.2013.2416

10.1016/j.ijleo.2015.04.042

10.1007/s12034-013-0504-x

10.1002/bio.3049

Thông tin
Thông tin xuất bản

Luminescence

Tập 32 Số 7

1361-1364

Thông tin tác giả