Oxygen vacancy-rich, Ru-doped In2O3ultrathin nanosheets for efficient detection of xylene at low temperature

Journal of Materials Chemistry C - Tập 6 Số 15 - Trang 4156-4162
Jin Wang1,2,3,4,5, Juan Su4,6,7,8, Hui Chen1,2,3,4,5, Xiaoxin Zou1,2,3,4,5, Guodong Li1,2,3,4,5
1Changchun 130012
2College of Chemistry
3Jilin University
4P. R. China
5State Key Laboratory of Inorganic Synthesis and Preparative Chemistry, College of Chemistry, Jilin University, Changchun 130012, P.R. China
6School of Chemistry and Chemical Engineering, Shanghai Jiao Tong University, Shanghai 200240, P. R. China
7Shanghai 200240
8Shanghai Jiao Tong University

Tóm tắt

The xylene sensing performance of In2O3has been enhanced greatly by doping ruthenium into In2O3nanosheets at low working temperature.

Từ khóa


Tài liệu tham khảo

Sui, 2017, ACS Appl. Mater. Interfaces, 9, 1661, 10.1021/acsami.6b11754

Brigo, 2013, J. Mater. Chem. C, 1, 4252, 10.1039/c3tc30426d

Zhang, 2014, J. Mater. Chem. A, 2, 20450, 10.1039/C4TA04396K

Kim, 2016, ACS Appl. Mater. Interfaces, 8, 34603, 10.1021/acsami.6b13930

Zhang, 2017, J. Mater. Chem. A, 5, 10387, 10.1039/C6TA11208K

Kim, 2017, ACS Appl. Mater. Interfaces, 9, 32034, 10.1021/acsami.7b10294

Jeong, 2017, ACS Appl. Mater. Interfaces, 9, 41397, 10.1021/acsami.7b13998

Kim, 2015, ACS Appl. Mater. Interfaces, 7, 17199, 10.1021/acsami.5b04066

Poloju, 2017, J. Mater. Chem. C, 5, 2662, 10.1039/C6TC05095F

Gao, 2017, Sens. Actuators, B, 253, 1152, 10.1016/j.snb.2017.06.177

Wang, 2016, J. Mater. Chem. C, 4, 295, 10.1039/C5TC02792F

Woo, 2014, ACS Appl. Mater. Interfaces, 6, 22553, 10.1021/am506674u

Rai, 2016, J. Mater. Chem. A, 4, 264, 10.1039/C5TA08873A

Huang, 2016, Sens. Actuators, B, 235, 86, 10.1016/j.snb.2016.05.060

Wang, 2017, ACS Sens., 2, 648, 10.1021/acssensors.7b00028

Wang, 2018, Sens. Actuators, B, 255, 159, 10.1016/j.snb.2017.08.054

Wang, 2013, J. Mater. Chem. A, 1, 8653, 10.1039/c3ta11506b

Yu, 2016, J. Alloys Compd., 682, 352, 10.1016/j.jallcom.2016.05.053

Cao, 2015, RSC Adv., 5, 6054

Wang, 2017, ACS Appl. Mater. Interfaces, 9, 16335, 10.1021/acsami.7b04395

Roso, 2016, J. Mater. Chem. C, 4, 9418, 10.1039/C6TC03218D

Sui, 2017, Mol. Catal., 435, 174, 10.1016/j.mcat.2017.03.033

Gaudet, 2005, Chem. Mater., 17, 1570, 10.1021/cm048129l

Chen, 2017, ACS Appl. Mater. Interfaces, 9, 4692, 10.1021/acsami.6b13520

Wang, 2017, J. Mater. Chem. C, 5, 3254, 10.1039/C7TC00226B

Salanov, 2010, Kinet. Catal., 51, 416, 10.1134/S0023158410030158

Tripathy, 2014, Angew. Chem., Int. Ed., 53, 12605, 10.1002/anie.201406324

Skarzewski, 1992, Org. Prep. Proced. Int., 24, 623, 10.1080/00304949209356237

Arends, 2004, Top. Organomet. Chem., 11, 277, 10.1007/b94652

Barsan, 2001, J. Electroceram., 7, 143, 10.1023/A:1014405811371

Thông tin
Thông tin xuất bản

Journal of Materials Chemistry C

Tập 6 Số 15

4156-4162

Thông tin tác giả