Oxidation Behavior of Thermal Barrier Coatings with a TiAl3 Bond Coat on γ-TiAl Alloy
Tóm tắt
The thermal barrier coatings investigated in this paper included a TiAl3 bond coat and a yttria partially stabilized zirconia (YSZ) layer. The TiAl3 bond coat was prepared by deposition of aluminum by cold spray, followed by a heat-treatment. The YSZ layer was prepared by air plasma spray. The isothermal and cyclic oxidation tests were conducted at 900 °C for 1000 h and 500 cycles to test the oxidation resistance of the thermal barrier coatings. The microstructure and composition of the γ-TiAl alloy with and without the thermal barrier coatings after oxidation were investigated. The results showed that a dense TGO layer about 5 μm had grown between the YSZ layer and the TiAl3 bond coat. The TGO had good adhesion to both the YSZ layer and the bond coat even after the TiAl3 bond coat entirely degraded into the TiAl2 phase, which decreased the inward oxygen diffusion. Thus, the thermal barrier coatings improved the oxidation resistance of γ-TiAl alloy effectively.
Tài liệu tham khảo
H. Clemens and H. Kestler, Processing and Applications of Intermetallic γ-TiAl-Based Alloys, Adv. Eng. Mater., 2000, 2(9), p 551-570
K. Kothari, R. Radhakrishnan, and N.M. Wereley, Advances in Gamma Titanium Aluminides and Their Manufacturing Techniques, Prog. Aerosp. Sci., 2012, 55, p 1-16
S. Becker, A. Rahmel, M. Schorr, and M. Schütze, Mechanism of Isothermal Oxidation of the Intel-Metallic TiAl and of TiAl Alloys, Oxid. Met., 1992, 38(5–6), p 425-464
A. Rahmel, M. Schütze, and W. Quadakkers, Fundamentals of TiAl Oxidation-A Critical Review, Mater. Corros., 1995, 46(5), p 271-285
M. Schmiedgen, P. Graat, B. Baretzky, and E. Mittemeijer, The Initial Stages of Oxidation of γ-TiAl: An X-Ray Photoelectron Study, Thin Solid Films, 2002, 415(1), p 114-122
M. Yoshihara and Y.-W. Kim, Oxidation Behavior of Gamma Alloys Designed for High Temperature Applications, Intermetallics, 2005, 13(9), p 952-958
Q.M. Wang, K. Zhang, J. Gong, Y.Y. Cui, C. Sun, and L.S. Wen, NiCoCrAlY Coatings with and Without an Al2O3/Al Interlayer on an Orthorhombic Ti2AlNb-Based Alloy: Oxidation and Interdiffusion Behaviors, Acta Mater., 2007, 55(4), p 1427-1439
J. Gao, Y. He, and W. Gao, Oxidation Behavior of γ-Tial Based Alloy with Al2O3-Y2O3 Composite Coatings Prepared by Electrophoretic Deposition, Surf. Coat. Technol., 2011, 205(19), p 4453-4458
V. Gauthier, F. Dettenwanger, and M. Schütze, Oxidation Behavior of γ-TiAl Coated with Zirconia Thermal Barriers, Intermetallics, 2002, 10(7), p 667-674
R. Braun, C. Leyens, and M. Fröhlich, Performance of Thermal Barrier Coatings on γ-TiAl, Mater. Corros., 2005, 56(12), p 930-936
T. Izumi, T. Nishimoto, and T. Narita, Superior Long-Term Oxidation Resistance of Ni-Al Coated TiAl Alloys, Intermetallics, 2005, 13(7), p 727-732
H.-P. Xiong, W. Mao, Y.-H. Xie, W.-L. Ma, Y.-F. Chen, X.-H. Li, J.-P. Li, and Y.-Y. Cheng, Liquid-Phase Siliconizing by Al-Si Alloys at the Surface of a TiAl-Based Alloy and Improvement in Oxidation Resistance, Acta Mater., 2004, 52(9), p 2605-2620
C.H. Koo and T.H. Yu, Pack Cementation Coatings on Ti3Al-Nb Alloys to Modify the High-Temperature Oxidation Properties, Surf. Coat. Technol., 2000, 126(2–3), p 171-180
Z.D. Xiang, S. Rose, and P.K. Datta, Pack Deposition of Coherent Aluminide Coatings on Gamma-TiAl for Enhancing Its High Temperature Oxidation Resistance, Surf. Coat. Technol., 2002, 161(2–3), p 286-292
V. Gauthier, F. Dettenwanger, M. Schütze, V. Shemet, and W. Quadakkers, Oxidation-Resistant Aluminide Coatings on γ-TiAl, Oxid. Met., 2003, 59(3–4), p 233-255
T. Sasaki, T. Yagi, T. Watanabe, and A. Yanagisawa, Aluminizing of TiAl-Based Alloy Using Thermal Spray Coating, Surf. Coat. Technol., 2011, 205(13–14), p 3900-3904
M.S. Chu and S.K. Wu, The Improvement of High Temperature Oxidation of Ti-50Al by Sputtering Al Film and Subsequent Interdiffusion Treatment, Acta Mater., 2003, 51(11), p 3109-3120
F.A. Varlese, M. Tului, S. Sabbadini, F. Pellissero, M. Sebastiani, and E. Bemporad, Optimized Coating Procedure for the Protection of TiAl Intermetallic Alloy against High Temperature Oxidation, Intermetallics, 2013, 37, p 76-82
M. Miyake, S. Tajikara, and T. Hirato, Fabrication of TiAl3 Coating on TiAl-Based Alloy by Al Electrodeposition from Dimethylsulfone Bath and Subsequent Annealing, Surf. Coat. Technol., 2011, 205(21–22), p 5141-5146
T.H. Van Steenkiste, J.R. Smith, and R.E. Teets, Aluminum Coatings via Kinetic Spray with Relatively Large Powder Particles, Surf. Coat. Technol., 2002, 154(2-3), p 237-252
B. Jodoin, L. Ajdelsztajn, E. Sansoucy, A. Zúñiga, P. Richer, and E.J. Lavernia, Effect of Particle Size, Morphology, and Hardness on Cold Gas Dynamic Sprayed Aluminum Alloy Coatings, Surf. Coat. Technol., 2006, 201(6), p 3422-3429
W.B. Choi, L. Li, V. Luzin, R. Neiser, T. Gnaupel-Herold, H.J. Prask, S. Sampath, and A. Gouldstone, Integrated Characterization of Cold Sprayed Aluminum Coatings, Acta Mater., 2007, 55(3), p 857-866
L. Kong, L. Shen, B. Lu, R. Yang, X. Cui, T. Li, and T. Xiong, Preparation of TiAl3-Al Composite Coating by Cold Spray and its High Temperature Oxidation Behavior, J. Therm. Spray Technol., 2010, 19(6), p 1206-1210
L. Kong, J. Qi, B. Lu, R. Yang, X. Cui, T. Li, and T. Xiong, Oxidation Resistance of TiAl3-Al Composite Coating on Orthorhombic Ti2AlNb Based Alloy, Surf. Coat. Technol., 2010, 204(14), p 2262-2267
M. Sujata, S. Bhargava, S. Suwas, and S. Sangal, On Kinetics of TiAl3 Formation During Reaction Synthesis from Solid Ti and Liquid Al, J. Mater. Sci. Lett., 2001, 20(24), p 2207-2209
F. Van Loo and G. Rieck, Diffusion in the Titanium-Aluminium System—I, Interdiffusion Between Solid Al and Ti or Ti-Al Alloys, Acta Metall., 1973, 21(1), p 61-71
S. Sampath and H. Herman, Rapid Solidification and Microstructure Development During Plasma Spray Deposition, J. Therm. Spray Technol., 1996, 5(4), p 445-456
J.A. Haynes, M.K. Ferber, W.D. Porter, and E.D. Rigney, Characterization of Alumina Scales Formed During Isothermal and Cyclic Oxidation of Plasma-Sprayed TBC Systems at 1150 °C, Oxid. Met., 1999, 52(1–2), p 31-76
C. Zhou, H. Xu, S. Gong, Y. Yang, and K. Young Kim, A Study on Aluminide and Cr-Modified Aluminide Coatings on TiAl Alloys by Pack Cementation Method, Surf. Coat. Technol., 2000, 132(2), p 117-123
A. Rabiei and A. Evans, Failure Mechanisms Associated with the Thermally Grown Oxide in Plasma-Sprayed Thermal Barrier Coatings, Acta Mater., 2000, 48(15), p 3963-3976
A. Evans, M. He, and J. Hutchinson, Mechanics-Based Scaling Laws for the Durability of Thermal Barrier Coatings, Prog. Mater Sci., 2001, 46(3), p 249-271
K. Schlichting, N. Padture, E. Jordan, and M. Gell, Failure Modes in Plasma-Sprayed Thermal Barrier Coatings, Mater. Sci. Eng., A, 2003, 342(1), p 120-130
D. Naumenko, V. Shemet, L. Singheiser, and W.J. Quadakkers, Failure Mechanisms of Thermal Barrier Coatings on Mcraly-Type Bondcoats Associated with the Formation of the Thermally Grown Oxide, J. Mater. Sci., 2009, 44(7), p 1687-1703