One-Step, Vacuum-Assisted Construction of Micrometer-Sized Nanoporous Silicon Confined by Uniform Two-Dimensional N-Doped Carbon toward Advanced Li Ion and MXene-Based Li Metal Batteries

ACS Nano - Tập 16 Số 3 - Trang 4560-4577 - 2022
Yongling An1, Yuan Tian1, Chengkai Liu1, Shenglin Xiong2, Jinkui Feng1, Yitai Qian3
1Key Laboratory for Liquid−Solid Structural Evolution & Processing of Materials (Ministry of Education), School of Materials Science and Engineering, Shandong University, Jinan 250061, P.R. China
2School of Chemistry and Chemical Engineering, Shandong University, Jinan, 250100, P. R. China
3Hefei National Laboratory for Physical Science at Microscale, Department of Chemistry, University of Science and Technology of China, Hefei, 230026, P.R, China

Tóm tắt

Từ khóa


Tài liệu tham khảo

10.1126/science.abg7217

10.1038/s41565-021-00947-8

10.1038/s41560-021-00883-w

10.1039/D1EE00639H

10.1126/science.aal4373

10.1038/s41565-020-0690-9

10.1038/s41560-019-0398-y

10.1038/s41467-021-22662-7

10.1126/science.1209150

10.1038/nenergy.2016.113

10.1126/sciadv.aax0651

10.1039/C9EE02615K

10.1038/s41467-019-09510-5

10.1002/adma.202103095

10.1016/j.ensm.2020.07.006

10.1002/adma.202004577

10.1038/s41467-020-15217-9

10.1038/s41467-020-17686-4

10.1021/acsnano.9b07241

10.1002/aenm.201601481

10.1002/adfm.202101645

10.1016/j.ensm.2021.04.005

10.1002/adma.202003286

10.1002/adfm.201908721

10.1021/acsnano.0c08336

10.1002/adfm.202101487

10.1016/j.nanoen.2020.104568

10.1002/adma.201605650

10.1016/j.ensm.2018.09.019

10.1002/adma.202104416

10.1002/adfm.202005699

10.1038/s41467-019-13434-5

10.1021/acsenergylett.0c02487

10.1039/C6EE02685K

10.1021/acs.nanolett.1c00317

10.1021/acsnano.8b08821

10.1002/adma.201506111

10.1021/acsnano.8b02219

10.1016/j.nantod.2021.101094

10.1002/anie.202009180

10.1002/smll.201907164

10.1021/acs.chemrev.6b00075

10.1016/j.nanoen.2016.04.043

10.1021/acsenergylett.0c02629

10.1021/acsenergylett.1c00514

10.1021/acsnano.9b06653

10.1038/s41467-019-08383-y

10.1038/s41467-021-25334-8

10.1021/acs.nanolett.0c02880

10.1039/C8EE00239H

10.1039/D0EE03037F

10.1039/D0EE02230F

10.1002/aenm.202101544

10.1038/s41560-021-00833-6

10.1021/acsnano.0c00184

10.1002/anie.201702099

10.1016/j.mattod.2020.10.021

10.1126/science.abf1581

10.1038/s41586-019-1904-x

10.1021/acsnano.9b08141

10.1002/aenm.201903534

10.1021/acsnano.9b05599

10.1002/adfm.201908075

10.1002/adma.201901820

10.1002/aenm.202002529

10.1016/j.mattod.2021.11.021

10.1016/j.ensm.2021.06.019

10.1021/acsami.8b21893

10.1016/j.ensm.2019.10.017

10.1002/aenm.202003416

10.1002/adfm.202004189

10.1002/adma.202004128

10.1038/s41586-020-1972-y

10.1038/s41586-019-1481-z

Thông tin
Thông tin xuất bản

ACS Nano

Tập 16 Số 3

4560-4577

Thông tin tác giả