On solidification of hypereutectic Al-Si alloys
Tóm tắt
Precipitation of primary silicon was studied in Al-Si hypereutectic alloys with 15, 18, and 25 wt. % silicon content. The alloys were solidified with different cooling rates from different super heat temperatures. The liquidus and eutectic temperature were evaluated from the cooling curves. The liquidus temperature was found to decrease with cooling rate. The evaluation of microstructure showed that the fraction of primary silicon decreased with increasing the cooling rate and super heat temperature. Furthermore, the morphology of the primary silicon changed as an effect of cooling rate and super heat temperature.
Tài liệu tham khảo
Fredriksson H, Hillert M and Lang N, Inst. Metals J., 101(1973) 285.
Atasoy O A, Yilmaz F and Elliott R, Cryst. Growth J., 66 (1984) 137.
West R and Fredriksson H, Mater. Sci. J., 20 (1985) 1061.
Martiez M A, Pract. Met., 28 (1991) 25.
Wang W, Bian X and Qin J, Mater. Sci. lett. J., 19 (2000) 1583.
Gabathuler J, Steeb S and Lamparter P, Z. Naturforsch., 34a (1979) 1305.
Wang W, Bian X and Qin J and Syliusarenko S I, Metall. Mater. Trans. A, 31a (2000) 2163.
Lang G, Aluminium 48(1972) 664.
Prigunova A G, Met. Phys. Adv. Tech., 17 (1999) 1103.
Fredriksson H and Rogberg B, Metals science, 8 (1979) 685.
Lockowandt C, Löth K, Ekbom L, Eliasson A and Jarfors A E W, in Proc. 8th European Symp. Materials Fluid Science, Brussels, Belgium(1992) 383.
El-Benawy T and Fredriksson H, Mater. Trans., JIM, 41 (2000) 507.
Steen H A H and Hellawell A, Acta Metall., 20 (1972) 370.
Fjellstedt J, On the crystallization of Al-base alloys, Ph D thesis, Royal Institute of Technology (KTH), Sweden(2001).
Sadigh B, Dzugutor M and Elliot S R, Phys. Rev. B, 59 (1999) 1.
Allen D R, Gremaud M and Perepezko J H, Mater. Sci. Eng., A226–227 (1997) 173.