Novel MgO–SnO2 Solid Superbase as a High-Efficiency Catalyst for One-Pot Solvent-Free Synthesis of Polyfunctionalized 4H-pyran Derivatives
Tóm tắt
We report for the first time the hydrothermal synthesis of MgO–SnO2 solid superbase using P123 as template. The basicity of the materials was determined by two approaches of Hammett indicators method and temperature-programmed desorption using CO2 as adsorbate (CO2-TPD). It was found that Mg/Sn molar ratio has an effect on MgO–SnO2 basicity, and superbasicity was observed only at Mg/Sn molar ratio of 1. With variation of Mg/Sn molar ratio, superbase strength (H
-) was in the 26.5–33.0 range, showing superbasic value up to 0.939 mmol/g. The structure and texture of the as-prepared materials were studied by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), and N2 physio-adsorption methods. We detected particles of spherical morphology having diameter of ca. 150 nm. N2 adsorption–desorption results suggested that the materials are of mesoporous structure, having specific surface area of 115.2 m2/g and average pore diameter of 6 nm. The superbase was found to exhibit excellent catalytic activity towards the one-pot synthesis of polyfunctionalized 4H-pyrans through the condensation of aldehydes, malononitrile, and an active methylene compound. Its excellent catalytic efficiency is related to its superbasicity of the MgO–SnO2. The results provide a new route for the design and preparation of composite oxide superbases. Furthermore, the solid superbases will facilitate a strategy for high-efficiency synthesis of polyfunctionalized 4H-pyrans. Novel MgO–SnO2 solid superbase was prepared using P123 as template. Its superbase strength was in the 26.5–33.0 range, showing superbasic sites up to 0.939 mmol/g. The material is of mesoporous structure,(having specific surface area of 115.2 m2/g and average pore diameter of 6 nm. It was found to exhibit excellent catalytic activity towards the one-pot solvent-free synthesis of polyfunctionalized 4H-pyrans through the condensation of aldehydes, malononitrile, and an active methylene compound. The results provide a new route for the design and preparation of composite oxide superbases.
Tài liệu tham khảo
Tanabe K, Misono M, Ono Y, Hattori H (1989) New solid acids and bases. Their catalytic properties, University of Tokyo, Tokyo, p 3
Hattori H (1995) Chem Rev 95:537
Wei YD, Zhang SG, Li GX, Yin SY, Au CT (2011) Chin J Catal 32:891
Bota RM, Houthoofd K, Grobet PJ, Jacobs PA (2010) Catal Today 152:99
Gorzawski H, Hoelderich WF (1999) Appl Catal A: Gen 179:131
Sun N, Klabunde KJ (1999) J Catal 185:506
Li X, Lu GZ, Guo YL, Guo Y, Wang YQ, Zhang ZG, Liu XH, Wang YS (2007) Catal Commun 8:1969
Sun LB, Yang J, Kou JH, Gu FN, Chun Y, Wang Y, Zhu JH, Zou ZG (2008) Angew Chem Int Ed 47:3418
Wang Y, Huang WY, Chun Y, Xia JR, Zhu JH (2001) Chem Mater 13:670
Yin SF, Xu BQ, Wang SJ, Au CT (2006) Appl Catal A: Gen 301:202
Tsuji H, Kabashima H, Kita H, Hattori H (1995) React Kinet Catal Lett 56:363
Sun LB, Kou JH, Chun Y, Yang J, Gu FN, Wang Y, Zhu JH, Zou ZG (2008) Inorg Chem 47:4199
Zhang SG, Wei YD, Yin SF, Au CT (2011) Catal Commun 12:712
Zhang SG, Wei YD, Yin SF, Luo SL, Au CT (2011) Appl Catal A: Gen 406:113
Zhang SG, Wei YD, Yin SF, Chao C, Luo SL, Au CT (2011) Catal Commun 12:1333
Zhu JH, Wang Y, Chun Y, Wang XS (1998) J Chem Soc Faraday Trans 94:1163
Liu Z, Dong L, Ji W, Chen Y (1998) J Chem Soc Faraday Trans 94:1137
Godinho KG, Walsh A, Watson GW (2009) J Phys Chem C 113:439
Chen HT, Xiong SJ, Wu XL, Zhu J, Shen JC (2009) Nano Lett 9:1926
Gonzalez R, Martin N, Seoane C, Marco JL, Albert A, Cano FH (1992) Tetrahedron Lett 33:3809
Liu Y, Zhang J, Xu W (2007) Curr Med Chem 14:2872
Wang JL, Liu D, Zhang ZJ, Shan S, Han X, Srinivasula SM, Croce CM, Alnemri ES, Huang Z (2000) Proc Natl Acad Sci 97:7124
Peng Y, Song G (2007) Catal Commun 8:111
Fotouhi L, Heravi MM, Fatehi A, Bakhtiari K (2007) Tetrahedron Lett 48:5379
Jin TS, Xiao JC, Wang SJ, Li TS, Song XR (2003) Synlett: 2001
Balalaie S, Sheikh-Ahmadi M, Bararjanian M (2007) Catal Commun 8:1724
Rad-Moghadam K, Youseftabar-Miri L (2011) Tetrahedron Lett 67:5693
Banerjee S, Horn A, Khatri H, Sereda G (2011) Tetrahedron Lett 52:1878
Lu GP, Cai C (2011) J Heterocyclic Chem 48:124
Babu NS, Pasha N, Rao KT, Prasad PS, Lingaiah N (2008) Tetrahedron Lett 49:2730
Walling C (1950) J Am Chem Soc 72:1164
Benesi HA (1956) J Am Chem Soc 78:5490
Benesi HA (1957) J Phys Chem 61:970
Sun NJ, Klabunde KJ (1999) J Catal 185:506
Gorzawski H, Hoelderich WF (1999) J Mol Catal A: Chem 144:181
Corma A, Iborra S (2006) Adv Catal 49:239
Kabashima H, Shibuya HT, Hattori H (2000) J Mol Catal A: Chem 155:23
Fotouhi L, Heravi MM, Fatehi A, Bakhtiari K (2007) Tetrahedron Lett 48:5379
Bayat M, Shiraz NZ, Asayesh SS (2010) J Heterocyclic Chem 47:857
Ye ZJ, Xu RB, Shao XS, Xu XY, Li Z (2010) Tetrahedron Lett 51:4991