Nanostructured Metal Oxides and Sulfides for Lithium–Sulfur Batteries

Advanced Materials - Tập 29 Số 20 - 2017
Xue Liu1,2, Jia‐Qi Huang1, Qiang Zhang1, Liqiang Mai2
1Beijing Key Laboratory of Green Chemical Reaction Engineering and Technology, Department of Chemical Engineering, Tsinghua University, Beijing 100084, P.R. China
2State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, International School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, P. R. China

Tóm tắt

Lithium–sulfur (Li–S) batteries with high energy density and long cycle life are considered to be one of the most promising next‐generation energy‐storage systems beyond routine lithium‐ion batteries. Various approaches have been proposed to break down technical barriers in Li–S battery systems. The use of nanostructured metal oxides and sulfides for high sulfur utilization and long life span of Li–S batteries is reviewed here. The relationships between the intrinsic properties of metal oxide/sulfide hosts and electrochemical performances of Li–S batteries are discussed. Nanostructured metal oxides/sulfides hosts used in solid sulfur cathodes, separators/interlayers, lithium‐metal‐anode protection, and lithium polysulfides batteries are discussed respectively. Prospects for the future developments of Li–S batteries with nanostructured metal oxides/sulfides are also discussed.

Từ khóa


Tài liệu tham khảo

10.1038/nchem.2085

10.1038/nmat3191

10.1021/ar3001348

10.1021/cr500062v

10.1557/mrs.2014.86

10.1039/c2cs35256g

10.1557/mrs.2014.84

10.1002/adma.201405115

10.1016/j.ensm.2015.09.007

10.1002/aenm.201500212

10.1002/aenm.201500408

10.1016/j.jpowsour.2012.12.102

10.1039/C5EE01388G

10.1021/jz401763d

10.1021/ac2032244

10.1021/jp500382s

10.1021/ja2121926

10.1149/1.1806394

10.1149/1.2937304

10.1039/c3ta11045a

10.1038/srep10848

10.1002/advs.201500213

10.1002/adma.201504526

10.1002/adma.201504117

10.1021/cr500177a

10.1038/ncomms5565

10.1002/aenm.201501333

10.1039/c002639e

10.1002/chem.201301689

10.1021/am402970x

10.1038/nmat2460

10.1021/am4000535

10.1007/s12274-012-0279-1

10.1021/nl304795g

10.1021/nl2027684

10.1002/anie.201205292

10.1016/j.jpowsour.2008.12.149

10.1002/adma.201402488

10.1038/ncomms4410

10.1039/c3ee24324a

10.1002/smll.201501467

10.1002/adma.201502668

10.1002/anie.201411109

10.1002/adfm.201303296

10.1021/nn304037d

10.1016/j.ensm.2015.08.004

10.1016/j.nanoen.2015.05.006

10.1021/am5075562

10.1002/adfm.201503726

10.1016/j.nanoen.2015.09.001

10.1007/s12274-016-1027-8

10.1002/anie.201505444

10.1038/ncomms8760

10.1021/nl200658a

10.1021/ja206955k

10.1021/nn403237b

10.1002/adfm.201504294

10.1038/ncomms6002

10.1002/adma.201401243

10.1002/admi.201400227

10.1002/adfm.201302631

10.1002/adma.201502467

10.1021/am501627f

10.1021/nn401228t

10.1039/C5TA04255K

10.1021/nl403130h

10.1021/nn203436j

10.1002/adma.201402569

10.1002/anie.201605676

10.1038/ncomms5759

10.1021/nl502331f

10.1021/acs.nanolett.5b04166

10.1149/1.1710895

10.1038/ncomms1293

10.1016/j.jpowsour.2009.02.038

10.1039/C5EE03902A

10.1021/jp304380j

10.1088/0957-4484/27/4/045403

10.1038/ncomms2327

10.1039/c3nr01393f

10.1016/j.jelechem.2014.11.007

10.1007/s10008-013-2203-3

10.1039/C5RA13823J

10.1021/nn501308m

10.1038/srep22990

10.1002/aenm.201501480

10.1038/srep13340

Liang X. H., 2014, Int. J. Electrochem. Sci., 9, 6677, 10.1016/S1452-3981(23)10920-5

10.1016/j.energy.2014.08.029

10.1016/j.jpowsour.2015.05.010

10.1126/science.1239879

10.1016/S0167-5729(02)00100-0

10.1038/ncomms6682

10.1039/C5TA05507E

10.1002/anie.201506972

10.1002/aenm.201501636

10.1021/acsnano.5b07458

10.1016/j.matlet.2015.06.003

10.1016/j.electacta.2013.05.083

10.1016/j.jpowsour.2012.04.039

10.1021/jacs.5b07071

10.1016/j.jallcom.2015.07.264

10.1039/C2TA00105E

10.1016/j.ijhydene.2008.12.006

10.1039/C4NR07663J

10.1002/aenm.201200006

10.1016/j.ssi.2015.03.007

10.1039/c4ta00234b

Liang X. H., 2014, Energy Development, Pts 1–4, 952

10.1039/c4ra04015e

10.1039/c3ta12846f

10.1002/admi.201500048

10.1007/s10832-014-9973-6

10.1016/j.materresbull.2015.08.036

10.1021/acs.jpcc.5b08934

10.15541/jim20140671

10.1021/acsami.5b01412

10.1002/adma.201501082

10.1002/adma.201506111

10.1016/j.matlet.2014.08.115

10.1039/C5NR00166H

Liang X. H., 2015, Int. J. Electrochem. Sci., 10, 9333, 10.1016/S1452-3981(23)11181-3

10.1142/S1793604714500209

10.1002/adma.201103392

10.1002/aenm.201401986

10.1016/j.ensm.2015.09.008

10.1016/j.jpowsour.2016.09.044

10.1038/ncomms2163

10.1002/adma.201402893

10.1039/C3EE42223B

10.1039/C5TA04289E

10.1016/j.jpowsour.2013.11.090

10.1021/nn507178a

10.1002/adma.201404210

10.1002/adma.201302877

10.1088/2053-1583/2/2/024013

10.1002/adma.201603401

10.1002/smll.201503133

10.1021/cm500575q

10.1002/adma.201405637

10.1007/s11581-014-1263-4

10.1016/j.nanoen.2014.12.029

10.1007/s12274-015-0812-0

10.1016/j.electacta.2014.02.077

10.1039/C4EE01377H

10.1016/j.nanoen.2013.05.003

10.1039/C5TA01490E

10.1016/j.jpowsour.2015.11.109

10.1039/C5TA01378J

10.1039/C5CC00444F

10.1039/C5RA27635G

10.1002/aenm.201402273

10.1016/j.jpowsour.2016.07.056

10.1149/1.3148721

10.1016/j.ensm.2016.01.007

10.1038/ncomms8436

10.1021/ja312241y

10.1038/nmat4041

10.1021/am504345s

10.1039/C5TA03195H

10.1038/ncomms2513

10.1021/acsami.6b02612

10.1021/nl503125u

10.1038/nnano.2014.152

10.1038/ncomms9058

10.1021/acs.nanolett.6b01581

10.1002/adma.201601409

10.1021/acsnano.5b01990

10.1038/nnano.2016.32

10.1073/pnas.1518188113

10.1002/smll.201401837

10.1021/acs.accounts.5b00427

10.1002/adma.201506124

10.1016/j.jpowsour.2015.10.007

10.1021/acsnano.5b02166

10.1073/pnas.1600422113

10.1002/anie.201410174

10.1039/C5MH00246J

10.1039/C6TA01214K

10.1016/j.mseb.2015.12.002

Greenwood N. N., 2012, Chemistry of the Elements

10.1038/ncomms6017

10.1021/acs.nanolett.5b00367

10.1021/jp506288w

10.1021/ja504099w

10.1016/j.jpowsour.2016.04.139

10.1039/C5TA06348E

10.1016/j.jpowsour.2014.07.099

10.1007/s11581-013-1019-6

10.1149/2.1021514jes

10.3724/SP.J.1077.2013.13017

10.1021/acsami.6b06565

10.1039/C6NR05626A

10.1002/aenm.201402290

10.1002/adfm.201401501

10.1002/adma.201504765

10.1021/acsami.5b07468

10.1016/j.jpowsour.2015.02.140

10.1039/C4TA07101H

10.1038/ncomms9622

10.1021/nl404721h

10.1039/C4EE01382D

10.1038/ncomms4943

10.1038/ncomms6877

10.1039/c3ee00072a

10.1021/nl100504q

10.1039/c3ee43395a

10.1039/c3sc52789a

10.1002/aenm.201300655

10.1002/adfm.201400845

10.1002/advs.201500268

Yao H. B., 2014, Nat. Commun., 5, 9

10.1021/acs.nanolett.5b02818

10.1039/C4CC08980D

10.1088/2053-1583/2/1/014011

10.1016/j.nanoen.2016.04.053

10.1002/smll.201600809

10.1038/ncomms11203

10.1021/nl503730c

10.1038/nmat4551

10.1557/mrs.2012.194

Thông tin
Thông tin xuất bản

Advanced Materials

Tập 29 Số 20

Thông tin tác giả