Microstructures of Niobium Components Fabricated by Electron Beam Melting

Springer Science and Business Media LLC - Tập 2 Số 3 - Trang 183-189 - 2013
E. Martínez1, L. E. Murr1, Jennifer Hernandez1, Xiao Pan2, Krista Amato1, P. Frigola3, César Terrazas4, Sara M. Gaytan4, Emmanuel Rodriguez4, Francisco Medina4, Ryan B. Wicker4
1Department of Metallurgical and Materials Engineering The University of Texas at El Paso, El Paso, TX 79968 USA
2School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, Liaoning, China
3Radiabeam Technologies, Santa Monica, CA, 90404, USA
4W.M. Keck Center for 3D Innovation, The University of Texas at El Paso, El Paso, TX 79968, USA

Tóm tắt

Từ khóa


Tài liệu tham khảo

H. Jiang, T.R. Bieler, C. Compton, T.C. Grimm, Evaluation of recrystallization textures from cold rolling textures with reversed rolling in high purity niobium. TMS Lett. 1(8), 177–178 (2004)

S.R. Agnew, F. Zeng, G.R. Myneni, Ultrasonic velocity and texture of high RRR niobium. Mater. Tech. 7–8, 38–44 (2003)

K.T. Hartwig, J. Wang, D.C. Baars, T.R. Bieler, S.N. Mathaudhu, R.E. Barber, Microstructural retirement of niobium for superconducting RF cavities. IEEE Trans. Appl. Supercond. 17(2), 1305–1309 (2007)

L.E. Murr, E. Martinez, S.M. Gaytan, D.A. Ramirez, J. Hernandez, Contributions of light microscopy to contemporary materials characterization : the new directional solidification. Metallogr. Microstruct. Anal. 1, 45–58 (2012)

L.E. Murr, E. Martinez, S.M. Gaytan, D.A. Ramirez, J. Hernandez, K.N. Amato, P.W. Shindo, F.R. Medina, R.B. Wicker, Metal fabrication by additive manufacturing using laser and electron beam melting technologies. J. Mater. Sci. Technol. 28(1), 1–14 (2012)

L.E. Murr, E. Martinez, K.H. Amato, S.M. Gaytan, J. Hernandez, D.A. Ramirez, P.W. Shindo, F. Medina, R.B. Wicker, Fabrication of metal and alloy components by additive manufacturing : examples of 3D materials science. J. Mater. Res. Technol. 1(1), 24–54 (2012)

L.E. Murr, Electron and Ion Microscopy and Microanalysis (Marcel Dekker, New York, 1990)

H. Conrad, S. Feuerstein, L. Rice, Effects of grain size on the dislocation density and flow stress of niobium. Mater. Sci. Eng. 2, 157–168 (1967)