Microstructure analysis of 8 μm electrolytic Cu foil in plane view using EBSD and TEM
Tóm tắt
With the lightening of the mobile devices, thinning of electrolytic copper foil, which is mainly used as an anode collection of lithium secondary batteries, is needed. As the copper foil becomes ultrathin, mechanical properties such as deterioration of elongation rate and tear phenomenon are occurring, which is closely related to microstructure. However, there is a problem that it is not easy to prepare and observe specimens in the analysis of the microstructure of ultrathin copper foil. In this study, electron backscatter diffraction (EBSD) specimens were fabricated using only mechanical polishing to analyze the microstructure of 8 μm thick electrolytic copper foil in plane view. In addition, EBSD maps and transmission electron microscopy (TEM) images were compared and analyzed to find the optimal cleanup technique for properly correcting errors in EBSD maps.
Tài liệu tham khảo
A. Ibanez, E. Fatas, Mechanical and structural properties of electrodeposited copper and their relation with the electrodeposition parameters, Surf. Coat. Technol. b1), 7–16 (2005)
A.J. Schwartz, M. Kumar, B.L. Adams et al., Electron backscatter diffraction in materials science, 2nd edn. (Springer, New York, 2009)
E.D.A.X. Insight, Step Size Selection for EBSD Mapping 16(1), 3 (2018)
F.J. Humphreys, Characterisation of fine-scale microstructures by electron backscatter diffraction (EBSD). Scr. Mater. 51, 771–776 (2004)
G. Nolze, Image distortions in SEM and their influences on EBSD measurements. Ultramicroscopy 107, 172–183 (2007)
J.H. Kang, S.H. Kim, Sample preparation for EBSD analysis: Tips for metals with delicate surfaces. Korean J. Met. Mater. 48(8), 730–740 (2010)
J.K. Park, Principle and applications of lithium secondarybatteries (Wiley-VCH, Weinheim, 2012)
J.P. Pender, G. Jha, D.H. Youn et al., Electrode degradation in lithium-ion batteries. ACS Nano 14, 1243–1295 (2020)
K.D. Kepler, J.T. Vaughey, M.M. Thackeray, Copper-tin anodes for rechargeable lithium batteries: an example of the matrix effect in an intermetallic system. J. Power Sources 81–82, 383–387 (1999)
M.M. Nowell, R.A. Witt, B. True, EBSD sample preparation: Techniques, Tips, and Tricks. Microsc. Microanal. 11(S02), 504–505 (2005)
M.N. Obrovac, V.L. Checrier, Alloy negative electrodes for Li-ion batteries. Chem. Rev. 114, 11444–11502 (2014)
R. Borah, F.R. Hughson, J. Johnston, et al., On battery materials and methods, Mater. Today Adv., 6, Article 1000046 (2020)
S.H. Kim, Y. Rhyim, Serial sectioning and reconstruction techniques for three-dimensional microscopy of metallic materials. Korean J. Met. Mater. 54(9), 698–710 (2016)
S.I. Wright, B.L. Adams, Automatic analysis of electron backscatter diffraction patterns. Metall. Trans. A 23, 759–767 (1992)
S.I. Wright, M.M. Nowell, EBSD image quality mapping. Microsc. Microanal. 12(1), 72–84 (2006)
S.I. Wright, M.M. Nowell, S.P. Lindeman et al., Introduction and comparison of new EBSD post-processing methodologies. Ultramicroscopy 159, 81–94 (2015)
T.H. Courtney, Mechanical behavior of materials, 2nd edn. (McGraw-Hill, New York, 2000)
T. Hatano, Y. Kurosawa, J. Miyake, Effect of material processing on fatigue of FPC rolled copper foil. J. Elec. Mater. 29(5), 611–616 (2000)
T.G. Woo, I.S. Park, K.W. Seol, Effect of additives on the elongation and surface properties of copper foils. Elec. Mater. Lett. 9(3), 341–345 (2013)
T.G. Woo, The effects of Bis(3-Sulfo-Propyl)di-Sulfide (SPS) additives on the surface morphology and mechanical properties of electrolytic copper foil. Korean J. Met. Mater. 54(9), 681–687 (2016)
V. Randle, O. Engler, Introduction to texture analysis: Macrotexture, microtexture, and orientation mapping, 2nd edn. (CRC Press, New York, 2010)