Mechanical strength and fatigue lifetime of WC-Co cemented carbide in relation to the effectively loaded volume and surface

Jayatilaka, 1977, Statistical approach to brittle fracture, J. Mater. Sci., 12, 1426, 10.1007/BF00540858 Danzer, 1992, A general strength distribution function for brittle materials, J. Eur. Ceram. Soc., 10, 461, 10.1016/0955-2219(92)90021-5 Quinn, 2003, Weibull strength scaling for standardized rectangular flexure specimens, J. Am. Ceram. Soc., 86, 508, 10.1111/j.1151-2916.2003.tb03329.x Larsson, 2004, X-ray diffraction determination of residual stresses in functionally graded WC-co composites, Int. J. Refract. Met. Hard Mater., 22, 177, 10.1016/j.ijrmhm.2004.06.002 Yang, 2014, Vol. 13, 257 Jonke, 2016, Strength of WC-co hard metals as a function of the effectively loaded volume, Int. J. Refract. Met. Hard Mater. Klünsner, 2019, Fatigue behaviour of WC-co hard metal under stress ratio and effectively loaded volume relevant to metalworking tool failure, Int. J. Refract. Met. Hard Mater., 80, 97, 10.1016/j.ijrmhm.2019.01.003 U. Schleinkofer, H.G. Sockel, K. Görting, W. Heinrich, Fatigue of hard metals and cermets — new results and a better understanding, Int. J. Refract. Met. Hard Mater., Vol. 15, Issues 1–3, 1997, P 103–112, doi:https://doi.org/10.1016/S0263-4368(96)00043-1. Kursawe, 2001, On the influence of binder content and binder composition on the mechanical properties of hardmetals, Int. J. Refract. Met. Hard Mater., 19 DIN EN 843--5, 2021 Torres, 2014, Analysis on the mechanical strength of WC-co cemented carbides under uniaxial and biaxial bending, Mater. Des., 55, 851, 10.1016/j.matdes.2013.10.051 D. Munz, T. Fett, Mechanisches Verhalten keramischer Werkstoffe, Springer, ISBN: 978-3-642-51710-5, doi:https://doi.org/10.1007/978-3-642-51710-5. M. Peschkes, J. Höhbusch, H. Haensel, J. Scholten, Verbundprojekt: MPNet - Maritime Multiphasentransportnetzwerke - Fördertechnologie zum bedarfsgerechten Transport von Mehrphasengemischen, Vorhaben: Festigkeitsbewertung ausgewählter Komponenten vernetzter Mehrphasen-Transportsysteme bei Verwendung alternativer Werkstoffe : Laufzeit des Vorhabens: 01.06.2014–30.09.2017 : Schlussbericht : Projekt im Förderprogramm "Maritime Technologien" des BMWi, doi:https://doi.org/10.2314/GBV:1014401968. Torres, 2001, Fatigue mechanics of WC–Co cemented carbides, Int. J. Refract. Met. Hard Mater., 19, 341, 10.1016/S0263-4368(01)00032-4 ISO 20501:2019-03, 2017 ISO 3327:2009-10, Hardmetals - Determination of transverse rupture strength, doi:10.31030/1500054.