Mechanical and Electrical Properties of the Ternary Ag–Sb–Zn System
Tóm tắt
This paper presents comparative review of experimental and thermodynamic assessment of ternary Ag–Sb–Zn system. Isothermal section of the Ag–Sb–Zn system at 300 °C has been calculated by CALPHAD method using thermodynamic parameters from literature. Microstructural analysis of a number of alloys was carried out by scanning electron microscopy and optical microscopy, whereas chemical composition of observed phases was analyzed using energy-dispersive X-ray spectroscopy. Hardness of selected alloys from four vertical sections was determined using Brinell hardness test and additionally by micro Vickers hardness test. Electrical conductivity of a number of alloys in the ternary Ag–Sb–Zn system was experimentally determined. Good overall agreement between experimental and calculated values was obtained.
Tài liệu tham khảo
V. Buchtovà, D. Živković, J. Vreštàl, D. Manasijević, A. Kroupa, Monatsh. Chem. 136, 1939 (2005)
I. Krastev, A. Zielonka, J. Appl. Electrochem. 32(10), 1141 (2002)
C. Xu, D. Yi, C. Wu, H. Liu, W. Li, Mater. Sci. Eng., A 538, 202 (2012)
H.-J. Wu, S.-W. Chen, Acta Mater. 59, 6463 (2011)
D. Jendrzejczyk-Handzlik, D. Živković, W. Gierlotka, D. Manasijević, K. Fitzner, D. Minić, J. Min. Metall. B 43(2), 161 (2007)
Z.H. Long, S.X. Zhou, H.S. Liu, Z.P. Jin, Thermochim. Acta 498(1–2), 22 (2010)
J. Liu, C. Guo, C. Li, Z. Du, Thermochim. Acta 539, 44 (2012)
D. Živković, D. Minić, D. Manasijević, J. Šestak, Ž. Živković, J. Min. Metall. B 47(1), 23 (2011)
V. Ćosović, N. Talijan, D. Živković, D. Minić, Ž. Živković, J. Min. Metall. B 48(1), 131 (2012)
M. Peng, Z. Qiao, A. Mlkula, CALPHAD 20(1), 69 (1996)
R. Schmid Fetzer, Ternary Alloys, vol. 2 (VCH-Verlagsgesellschaft, Weinheim, 1988), pp. 556–557
A. Mikula, Metall. Trans. B 23, 601 (1992)
F. Kohler, Monatsh. Chem. 91, 738 (1960)
C. Colinet, Dissertation, University of Grenoble, France, 1967
M. Hillert, CALPHAD 4(1), 1 (1980)
G.W. Toop, Trans. Met. Soc. AIME 233, 850 (1965)
N. Saunders, A.P. Miodownik, CALPHAD, (A Comprehensive Guide) (Elsevier, London, 1998)
H.L. Lukas, S.G. Fries, B. Sundman, Computational Thermodynamics: CALPHAD Method (Cambridge University Press, Cambridge, 2007)
A.T. Dinsdale, A. Kroupa, J. Vizdal, J. Vrestal, A. Watson, A. Zemanova (eds.), COST 531 Database for Lead-Free Solders, vol. 1 (COST Office, Belgium, 2008)
A.T. Dinsdale, SGTE Unary Database, Version 4.4. (2002), http://www.sgte.org. Accessed 12 March 2013