Iron-Catalyzed Boron Removal from Molten Silicon in Ammonia
Tóm tắt
A high-temperature process of refining metallurgical-grade silicon to solar-grade silicon was developed. In this gas purging treatment, boron impurity in silicon reacts with ammonia and the products are removed as volatiles at high temperature. 1 mass pct metallic iron was added to molten silicon as a catalyst, improving the boron removal ratio from 14 to 80 pct at 1723 K (1450 °C). At 1823 K (1550 °C), this reaction could reduce boron concentration from more than 120 ppmw to <1 ppmw within 6 hours, meeting the purity requirement of solar-grade silicon. Nickel was tested in place of iron but showed no catalytic effect on boron removal. The result confirmed the catalytic role of iron in boron removal from molten silicon in ammonia. Possible mechanisms of catalysis, influence from iron concentration, and temperature effect on the catalytic reaction were explored. An apparent activation energy of 329 ± 129 kJ mol−1 was calculated from experimental data.
Tài liệu tham khảo
J. Safarian, G. Tranell, M. Tangstad, Energy Procedia 20, 88–97 (2012)
D. Lynch, JOM 61, 41–48 (2009)
M. Johnston, L. Khajavi, M. Li, S. Sokhanvaran, M. Barati, JOM 64, 935–45 (2012)
Y. Wang, X. Ma, K. Morita, Metall. Mater. Trans. B 45B, 334–37 (2014)
H. Theuerer, Trans. AIME 206, 1316–19 (1956)
H. Nishimoto, Y. Kang, T. Yoshikawa, K. Morita, High Temp. Mater. Process. (Lond.) 31, 471–77 (2012)
J.J. Wu, W.H. Ma, B. Yang, Y.N. Dai, K. Morita, Trans. Nonferr. Metal. Soc. 19, 463–67 (2009)
A. Yvon, E. Fourmond, C. Ndzogha, Y. Delannoy and C. Trassy: Proceedings of EPM 2003 4th International Conference on Electromagnetic Processing of Materials, 2003, pp. 125–30.
E.F. Nordstrand, M. Tangstad, Metall. Mater. Trans. B 43B, 814–22 (2012)
C.P. Khattak, D.B. Joyce, F. Schmid, Sol. Energy Mater. Sol. Cells 74, 77–89 (2002)
C. Khattak, D. Joyce and F. Schmid: Report No. NREL/SR-520-30716, National Renewable Energy Laboratory, Salem, Massachusetts, 2001.
K. Tang, S. Andersson, E. Nordstrand, M. Tangstad, JOM 64, 952–56 (2012)
N. Nakamura, H. Baba, Y. Sakaguchi, Y. Kato, Mater. Trans. 45, 858–64 (2004)
P.G. Ho, M. James: Report No. SAND99-1047, Sandia National Labs., Albuquerque, 1999.
J.A. Van Den Avyle, P. Ho and J.M. Gee: Report No. SAND2000-0821, Sandia National Labs., Albuquerque, 2000.
F.L. Riley, J. Am. Ceram. Soc. 83, 245–65 (2000)
B.R. Bathey, M.C. Cretella, J. Mater. Sci. 17, 3077–96 (1982)
T. Yoshikawa, K. Morita, JOM 64, 946–51 (2012)
T. Yoshikawa, K. Morita, J. Cryst. Growth 311, 776–79 (2009)
T. Yoshikawa, K. Morita, Metall. Mater. Trans. B 36B, 731–36 (2005)
H. Bielawa, O. Hinrichsen, A. Birkner, M. Muhler, Angew. Chem. Int. Ed. 40, 1061–63 (2001)
N.D. Spencer, R.C. Schoonmaker, G.A. Somorjai, J. Catal. 74, 129–35 (1982)
P. Stoltze, Phys. Scr. 36, 824 (1987)
M. Bowker, I. Parker, K. Waugh, Appl. Catal. 14, 101–18 (1985)
W.-S. Seo, K. Koumoto, S. Arai, J. Am. Ceram. Soc. 81, 1255–61 (1998)
A.J. Moulson, J. Mater. Sci. 14, 1017–51 (1979)
W. Kaiser, C. Thurmond, J. Appl. Phys. 30, 427–31 (1959)
W.G. Bessler, M. Vogler, H. Störmer, D. Gerthsen, A. Utz, A. Weber, E. Ivers-Tiffée, PCCP 12, 13888–903 (2010)
H. Zhu, R.J. Kee, V.M. Janardhanan, O. Deutschmann, D.G. Goodwin, J. Electrochem. Soc. 152, A2427–40 (2005)
Z. Yuan, W. Huang, K. Mukai, Appl. Phys. A 78, 617–22 (2004)
M. Tanahashi, T. Fujisawa, C. Yamauchi, J. Min. Mater. Process. Inst. Jpn. 114, 807–12 (1998)
S.V. Lukin, V.I. Zhuchkov, N.A. Vatolin, J. Less-Common Met. 67, 399–405 (1979)
R. Speiser, D.R. Poirier, K. Yeum, Scr. Metall. 21, 687–92 (1987)
A. Zaitsev, N.Y. Zaitseva, A. Kodentsov, Metall. Mater. Trans. B 34B, 887–98 (2003)
C. Ji, R. Yu, S. Liu, Can. Metall. Q. 27, 41–47 (1988)
J. Garandet, Int. J. Thermophys. 28, 1285–303 (2007)
H. Kodera, Jpn. J. Appl. Phys. 2, 212 (1963)
Y. Wang and K. Morita: J. Sustain. Metall., vol. 1, pp. 126–33.
K. Tang, E.J. Øvrelid, G. Tranell, M. Tangstad, JOM 61, 49–55 (2009)
Q. Wang, D.-G. Li, K. Wang, Z.-Y. Wang, J.-C. He, Scr. Mater. 56, 485–88 (2007)
T. Kobayashi, M. Tokiwai, J. Alloys Compd. 197, 7–16 (1993)