Investigation on TIG cladding of copper alloy on steel plate

Science and Technology of Welding and Joining - Tập 13 Số 1 - Trang 10-16 - 2008
Shixiong Lv, Zhe Xu, H. T. Wang, Shiqin Yang

Tóm tắt

Tungsten inert gas cladding of steel substrate with copper alloy under different processing conditions was investigated with the particular emphasis on the influence of cladding current on the concentration and morphology of Fe solute in the cladding layer and the hardness of the Cu/Fe interface. The application of hot wire was helpful to some extent in improving the spreadability of the filler metal but tended to cause intensive transfer of Fe into the copper layer when the current was higher than 240 A. The increase in Fe concentration in the copper layer followed an exponential relation with the growth of welding current. The morphology of Fe in the copper layer depended on its concentration. The hardness of copper layer increased with the welding current and intensively depended on its Fe content. At a welding rate of 3000 mm min–1, the optimum cladding currents were 210–270 A for the use of cold wire and 210–240 A for the use of hot wire.

Từ khóa


Tài liệu tham khảo

Wang K., 2001, Trans. China Weld. Inst, 22, 69

10.1016/S0921-5093(01)01841-X

10.1016/S0921-5093(02)00451-3

10.1023/A:1004697518965

Jetline engineering: HWP-50D hot wire process, available at: www.jetline.com

10.1179/174329306X147553

10.1179/174329307X213828

10.1179/136217102225001359

10.1179/136217102225006778

10.1016/S0030-3992(99)00116-4

10.1016/S0924-0136(02)00235-2

10.1016/j.jmatprotec.2003.12.016

10.1016/j.msea.2006.03.096

10.1016/j.matdes.2004.07.021

10.1007/s10853-005-3655-3

10.1007/BF02664678

10.1007/BF02679014

Thông tin
Thông tin xuất bản

Science and Technology of Welding and Joining

Tập 13 Số 1

10-16

Thông tin tác giả