Investigation into the Structure and Oxidation Mechanism of FeAlCr/Al2O3 Detonation Spraying Coatings
Tóm tắt
The oxidation resistance of detonation spraying coatings of the FeAlCr/Al2O3 powder fabricated by mechanically assisted self-propagating high-temperature synthesis using aluminothermic reactions of oxide reduction is investigated. The powder has a sufficiently homogeneous composite structure consisting of chromium-alloyed ordered B2-FeAl and fine inclusions of α-Cr2O3 and α-Al2O3. The detonation coatings sprayed on stainless steel substrates have a typical layered structure without cracks and spalling. The coating thickness is 250–300 μm, and microhardness is in a range of 5.9–6.1 GPa. Coatings of the synthesized powder mainly inherit its structure and phase composition, although certain aluminum and chromium oxidation occurs when spraying. The features of the cyclic and isothermal oxidation of coatings in air in a temperature range of 900–1000°C are studied. It is established that the oxidation resistance of detonation coatings of the synthesized powder after oxidation in air for 48 h at 950°C is close that of coatings formed from the FeAl‒FexAly powder with an aluminum content of 45 wt %. At the same time, the linear thermal expansion coefficient (LTEC) of FeAlCr/Al2O3 coatings is closer to the LTEC of the base material, while their creep resistance is higher when compared the latter due to the presence of fine refractory oxide inclusions. It is assumed that α-Cr, Cr2O3, and numerous fine alumina inclusions present in the synthesized powder (and which form when spraying) accelerate the protective film, formation suppressing hematite nucleation and growth at early oxidation stages at temperatures up to 950°C.
Tài liệu tham khảo
Stoloff, N.S., Iron aluminides: present status and future, Mater. Sci. Eng. A, 1998, vol. 258, pp. 1–14.
Kang, B.S.J. and Cisloiu, R., Evaluation of fracture behaviour of iron aluminides, Theor. Appl. Fract. Mech., 2006, vol. 45, pp. 25–40.
Kuc, D., Niewielski, G., Jablonska, M., and Bednarczyk, I., Deformability and recrystallization of Fe–Al intermetallic phase—base alloy, JAMME, 2007, vol. 20, pp. 143–146.
Sikka, V.K., Welsch, G., and Desai, P.D., Oxidation and Corrosion of Intermetallic Alloys, West Lafayette, Indiana: Metal Information Analysis Centre, 1996.
Stott, F.H., Grabke, H.J., and Schutze, M., Oxidation-Sulphidation of Iron Aluminides. Oxidation of Intermetallics, Weinheim: Wiley, 1997.
Klower, J., Grabke, H.J., and Schutze, M., High Temperature Corrosion Behaviour of Iron Aluminides and Iron Aluminium–Chromium Alloys. Oxidation of Intermetallics, Weinheim: Wiley, 1997.
Morris, D.G., Muñoz-Morris, M.A., and Chao, J., Development of high strength, high ductility and high creep resistant iron aluminide, Intermetallics, 2004, vol. 12, pp. 821–826.
Tortorelli, P.F., DeVan, J.H., Goodwin, G.M., and Howell, M., Elevated Temperature Coatings. Science and Technology, Warrendale, PA: TMS, 1995.
Pint, B.A., Tortorelli, P.F., and Wright, I.G., Oxidation of Intermetallics, New York: Wiley, 1996.
Subramanian, R., Iron-aluminide–Al2O3 composites by in situ displacement reactions: processing and mechanical properties, Mater. Sci. Eng. A, 1998, vol. 254, pp. 119–128.
Grabke, H.J. and Schutze, M., Oxidation of Intermetallics, New York: Wiley, 2007.
Tortorelli, P.F. and DeVan, J.H., Compositional Influences of the High Temperature Corrosion Resistance of Iron Aluminides, in Processing, Properties, and Applications of Iron Aluminides, Warrendale, PA: The Minerals, Metals and Materials Society, 1994.
DeVan, J.H., Oxidation Behaviour of Fe 3 Al and Derived Aluminum Alloys. Oxidation of High Temperature Intermetallics, Warendale: TMS, 1989.
Halfa, H., Oxidation behavior of Fe 3 Al–5Cr–(0, 0.5, 1.5)Ti alloys at temperatures ranges from 800°C to 1200°C, JMMCE, 2010, vol. 9, pp. 775–786.
Doychak, J., Smialek, J.L., and Barrett, C.A., Oxidation of High Temperature Intermetallics, Warrendale, PA: The Minerals, Metals and Materials Society, 1989.
Smialek, J.L., Doychak, J., and Gaydosh, D.J., Oxidation behavior of FeAl + Hf, Zr, B, Oxid. Met., 1990, vol. 34, pp. 259–270.
Zhenyu Liu and Gao Wei, Effects of chromium on the oxidation performance of β-FeAlCr coatings, Oxid. Met., 2000, vol. 54, pp. 189–209.
Gang, Ji, Elkedim, O., and Grosdidier, T., Deposition and corrosion resistance of HVOF sprayed nanocrystalline iron aluminide coatings, Surf. Coat. Technol., 2005, vol. 190, pp. 406–416.
Guilemany, J.M., Lima, C.R.C., Cinca, N., and Miguel, J.R., Studies of Fe–40Al coatings obtained by high velocity oxy-fuel, Surf. Coat. Technol., 2006, vol. 201, pp. 2072–2079.
Guilemany, J. and Cinca, N., High-temperature oxidation of Fe–40Al coatings obtained by HVOF thermal spray, Intermetallics, 2007, vol. 15, pp. 1384–1394.
Guilemany, J.M., Cinca, N., Dosta, S., and Cano, I.G., FeAl and NbAl3 intermetallic–HVOF coatings: Structure and properties, J. Therm. Spray Technol., 2009, vol. 18, pp. 536–545.
Senderowski, C. and Bojar, Z., Gas detonation spray forming of Fe–Al coatings in the presence of interlayer, Surf. Coat. Technol., 2008, vol. 202, pp. 3538–3548.
Senderowski, C., Bojar, Z., Wolczynski, W., and Pawlowski, A., Microstructure characterization of D-gun sprayed Fe–Al intermetallic coatings. Intermetallics, 2010, vol. 18, pp. 1405–1409.
Vityaz, P.A., Letsko, A.I., Talako, T.L., and Parnitsky, N.M., Chromium alloyed FeAl-based powder for oxidation resistant coatings, Euro PM2015 Proc., 2015, paper 3213202 (6 p).
Vityaz, P.A., Letsko, A.I., Talako, T.L., and Parnitskii, N.M., Influence of the structural state of chromium on the oxidation resistance of the composite powder based on iron aluminide reinforced with Al2O3 inclusions, in Poroshkovaya metallurgiya: Respublikanskii mezhvedomstvennyi sbornik nauchnykh trudov (Powder Metallurgy: Collected Republican Interdepartmental Proc. of Scientific Works), Minsk: “Belaruskaya nauka”, 2014. no. 37, pp. 167–173.
Talako, T.L., Belyaev, A.V., Il’yushchenko, A.F., and Letsko, A.I., RB Patent 6545, 2004.
Letsko, A.I., Talako, T.L., Reutenok, Yu.A., and Parnitskii, N.M., RB Patent 19172, 2015.
Grabke, H.G., Oxidation of NiAl and FeAl, Intermetallics, 1999, vol. 7, pp. 1153 –1158.
Levashov, E.A., Fiziko-khimicheskie i tekhnologicheskie osnovy samorasprostranyayushchegosya vysokotemperaturnogo sinteza (Physicochemical and Process Foundations of Self-Propagating High-Temperature Synthesis), Moscow: BINOM, 1999.
Szczucka-Lasota, B., Formanek, B., Szymanski, K., Bierska, B., Oxidation of thermally sprayed coatings with FeAl intermetallic matrix, in: Proc. 12th Int. Sci. Conf. “Achievements in Materials and Manufacturing Engineering”, 2004, pp. 901–904.