Influence of pre-heat treatment and different light-curing units on Vickers hardness of a microhybrid composite resin
Tóm tắt
The aim of this study was to evaluate the hardness of a dental composite resin submitted to temperature changes before photo-activation with two light-curing unite (LCUs). Five samples (4 mm in diameter and 2 mm in thickness) for each group were made with pre-cure temperatures of 37, 54, and 60°C. The samples were photo-activated with a conventional quartz-tungsten-halogen (QTH) and blue LED LCUs during 40 s. The hardness Vickers test (VHN) was performed on the top and bottom surfaces of the samples. According to the interaction between light-curing unit and different pre-heating temperatures of composite resin, only the light-curing unit provided influences on the mean values of initial Vickers hardness. The light-curing unit based on blue LED showed hardness mean values more homogeneous between the top and bottom surfaces. The hardness mean values were not statistically significant difference for the pre-cure temperature used. According to these results, the pre-heating of the composite resin provide no influence on Vickers hardness mean values, however the blue LED showed a cure more homogeneous than QTH LCU.
Tài liệu tham khảo
R. L. Bowen, J. Am. Dent. Assoc. 66, 57 (1963).
A. Peutzfeldt, Eur. J. Oral. Sci. 105, 97 (1997).
A. Peutzfeldt, A. Sahafi, and E. Asmussen, Dent. Mater. 16, 330 (2000).
U. Lohbauer, C. Rahiotis, N. Kramer, A. Petschelt, and G. Eliades, Dent. Mater. 21, 608 (2005).
F. A. Rueggeberg, Quitessence Int. 24, 391 (1993).
W. D. Cook, and P. M. Standish, Aust. Dent. J. 28, 307 (1983).
J. Friedman, and R. Hassan, J. Prosthet. Dent. 52, 504 (1984).
M. Takamizu, B. K. Moore, J. C. Setcos, and R. W. Phillips, Oper. Dent. 13, 173 (1988)
R. G. Craig, and J. M. Powers, Restorative Dental Materials, 11th ed. (St. Louis, 2002).
A. Schattenberg, D. Lichtenberg, E. Stender, B. Willershausen, and C. P. Ernst, Dent. Maler. 24, 1043 (2008).
K. Fujita, N. Nishiyama, K. Nemoto, T. Okada, and T. Ikemi, Dent. Mater. 24, 403 (2005).
J. W. Stansbury, J. Esthet. Dent. 12, 300 (2000).
R. J. Blankenau, W. P. Kelsey, G. L. Powell, G. O. Shearer, W. W. Barkmeier, and W. T. Cavel, Am. J. Dent. 4, 40 (1991).
J. L. Ferracane, J. C. Mitchem, J. R. Condon, and R. Todd, J. Dent. Res. 76, 1508 (19917).
A. N. S. Rastelli, D. P. Jacomassi, and V. S. Bagnato, Laser Phys. 18, 1074 (2008).
P. Keogh, N. J. Ray, C. D. Lynch, F. M. Burke, and A. Hannigan, Eur. J. Prosthodont. Rest. Dent. 12, 177 (2004).
S. Imazato, J. F. McCabe, H. Tarumi, A. Ehara, and S. Ebisu, Dent. Mater. 17, 178 (2001).
J. L. Ferracane, Dent. Mater. 1, 11 (1985).
J. L. Ferracane and E. H. Greener, J. Dent. Res. 63, 1093 (1984).
L. G. Lovell, H Lu, J. E. Elliot, J. W. Stansbury, and C. N. Bowman, Dent. Mater. 17, 504 (2001).
J. Friedman, Contemp. Esthet. Restorat. Pract. 7, 46 (2003).
G. Freedman and I. Krejci, Compendium 25, 95 (2004).
J. Friedman, US Patent 6236020 (2001).
L. Littlejohn, S. C. Greer, A. D. Puckett, and J. Firtchie, J. Dent Res. 82 (Spec. Iss. A), 0944 (2003).
International Organization for Standardization, ISO 4049, Dentistry—Polymer—Based Filling, Restorative and Luting Materials, 3rd ed. (ISO, Geneva, 2000).
L. Wang, P. H. P. D’Alpino, L. G. Lopes, and J. C. Pereira, J. Appl. Oral Sci. 11, 162 (2003).
F. A. Rueggeberg and R. G. Craig, J. Dent. Res. 67, 932 (1988).
A. Peutzfeldt and E. Asmussen, J. Dent. Res. 84, 659 (2005).
J. Manhart, K. H. Kunzelmann, H. Y. Chen, and R. Hickel, J. Biomed. Mater. Res. (ApplBiomater). 53, 353 (2000).
J. Yearn, Int. Dent. J. 35, 218 (1985).
C. Hasler, B. Zimmerli, and A. Lussi, Operat. Dent. 31, 354 (2006).
A. Lindberg, A. Peutzfeldt, and J. W. V. Dijken, Clin. Oral. Invest. 9, 71 (2005).
D. A. M. P. Malta, A. A. M. Kreidler, G. E. Villa, M. F. de Andrade, C. R. Fontana, and R. F. Z. Lizarelli, Laser Phys. Lett. 4, 153 (2007).
Z. Tarle, A. Meniga, A. Knezevic, J. Sutalo, M. Ristic, and G. Pichler, J. Oral Rehabil. 29, 662 (2002).
D. L. Hussey, P. A. Biagionit, and J. Lamey, J. Dent. 23, 267 (1995).
S. Bouillaguet, G. Caillot, J. Forchelet, M. L. Cattani, J. C. Wataha, and I. Krejci, J. Biomed. Mater. Res. Part. B: Appl. Biomater. B 72, 260 (2005).
A. N. S. Rastelli, D. P. Jacomassi, and V. S. Bagnato. Laser Phys. 18, 1003 (2008).
E. K. Hansen and E. Asmussen, Scand. J. Dent. Res. 101, 62 (1993).
A. C. Obici, M. A. C. Sinhoreti, E. Frollini, L. Correr-Sobrinho, M. F. Góes, and G. E. P. Henriques, Polymer. Testing. 25, 282 (2006).
L. C. Ramp, J. C. Broome, and M. H. Ramp, Am. J. Dent. 19, 31 (2006).
P. C. G. Silva, S. T. Porto-Neto, R. F. Z. Lizarelli, and V. S. Bagnato, Laser Phys. Lett. 5, 220 (2008).
H. Jelínková, T. Dolstálová, M. Nemec, P. Koranda, M. Miyagi, K. Iwai, Y.-W. Shi, and Y. Matsuura, Laser Phys. Lett. 4, 835 (2007).
J. E. Elliott, L. G. Lovell, and C. N. Bowman, Dent. Mater. 17, 221 (2001).
R. Trushkowsky, Dentistry Today/ the Nation’s Leading Clinical News Magazine for Dentists 21, (2002).
M. Trujillo, S. M. Newman, and J. W. Stansbury, Dent. Mater. 20, 766 (2004).
G. Freedman, Private Dentistry 8, 111 (2003).
M. Daronch, F. A. Rueggeberg, and M. F. De Goes, J. Dent. Res. 84, 663 (2005).