Influence of Solvents and Composition of Etch-and-Rinse and Self-Etch Adhesive Systems on the Nanoleakage within the Hybrid Layer

Journal of Contemporary Dental Practice - Tập 14 Số 4 - Trang 691-699 - 2013
João C. Ferreira1, Patrícia Pires, Álvaro Azevedo, Sofia Arantes‐Oliveira, Paulo Melo, Mário Jorge Silva
1Professor, Department of Operative Dentistry, Faculty of Dentistry University of Porto, Portugal, e-mail: [email protected].

Tóm tắt

ABSTRACT Aim The goal of this study was to evaluate nanoleakage within the hybrid layer yielded by etch-and-rinse and self-etch adhesive systems, with different solvents and compositions. Materials and methods Four adhesives were applied onto 20 human dentin disks: group A: Adper Scotchbond 1XT™ (3M ESPE), group B: One Coat Bond® (Coltène Whaledent), group C: AdheSE® (Ivoclar Vivadent) and group D: Xeno-V® (Dentsply). The samples were immersed in aqueous ammoniacal silver nitrate for 24 hour, prepared and observed under field-emission scanning electron microscopy with backscattered electrons. Microphotographs were scanned and data were processed. The mean value and standard deviation were calculated. KruskalWallis and Mann-Whitney tests were used (p < 0.05). Results All the adhesives showed nanoleakage within the hybrid layer: Adper Scotchbond 1XT™ (218.5 μm ± 52.6 μm), One Coat Bond® (139.6 μm ± 79.0 μm), AdheSE® (92.7 μm ± 64.8 μm) and Xeno-V® (251.0 μm ± 85.2 μm). AdheSE® yielded less nanoleakage than Adper Scotchbond-1XT™ (p = 0.003) and than Xeno-V® (p = 0.007). No other statistically significant differences were detected. Conclusion Two-step self-etch adhesive system (AdheSE®) might contribute for lower nanoleakage deposition and thus better performance in dentin adhesion. Clinical significance The two-step self-etch adhesive system showed the lowest nanoleakage deposition compared with the other adhesive systems evaluated, which seems to indicate a better behavior when a restoration is performed in dentin and possibly can lead to a durable adhesion along time. How to cite this article Ferreira JC, Pires PT, Azevedo AF, Oliveira SA, Melo PR, Silva MJ. Influence of Solvents and Composition of Etch-and-Rinse and Self-Etch Adhesive Systems on the Nanoleakage within the Hybrid Layer. J Contemp Dent Pract 2013;14(4):691-699.

Từ khóa


Tài liệu tham khảo

Yuan Y, Shimada Y, Ichinose S, Tagami J., 2007, Dent Mater, 23:, 561, 10.1016/j.dental.2006.03.015

Yuan Y, Shimada Y, Ichinose S, Tagami J. Qualitative analysis of adhesive interface nanoleakage using FE-SEM/EDS. Dent Mater 2007;23:561-569.

Sano H, Takatsu T, Ciucchi B, Horner JA, Matthews WG, Pashley DH., 1995, Oper Dent, 20:, 18

Sano H, Takatsu T, Ciucchi B, Horner JA, Matthews WG, Pashley DH. Nanoleakage: leakage within the hybrid layer. Oper Dent 1995;20:18-25.

Cavalheiro A., 2004, Iowa: University of Iowa, 6

Cavalheiro A. Effect of primer apllication on dentin permeability. Iowa: University of Iowa 2004;6-8

Uno S, Finger WJ., 1996, Oper Dent, 21:, 31

Uno S, Finger WJ. Effect of mode of conditioning treatment on efficacy of dentin bonding. Oper Dent 1996;21:31-35.

Tay FR, Pashley DH, Yiu C, et al., 2004, Am J Dent, 17:, 182

Tay FR, Pashley DH, Yiu C, et al. Nanoleakage types and potential implications: evidence from unfilled and filled adhesives with the same resin composition. Am J Dent 2004;17:182-190.

Prati C, Chersoni S, Acquaviva GL, et al., 2005, Clin Oral Investig, 9:, 1, 10.1007/s00784-004-0273-4

Prati C, Chersoni S, Acquaviva GL, et al. Permeability of marginal hybrid layers in composite restorations. Clin Oral Investig 2005;9:1-7.

Suppa P, Breschi L, Ruggeri A, et al., 2005, J Biomed Mater Res B Appl Biomater, 73:, 7

Suppa P, Breschi L, Ruggeri A, et al. Nanoleakage within the hybrid layer: A correlative FEISEM/TEM investigation. J Biomed Mater Res B Appl Biomater 2005;73:7-14.

Tay FR, Pashley DH, Yoshiyama M., 2002, J Dent Res, 81:, 472, 10.1177/154405910208100708

Tay FR, Pashley DH, Yoshiyama M. Two modes of nanoleakage expression in single-step adhesives. J Dent Res 2002;81:472-476.

Schneider H, Frohlich M, Erler G, Engelke C, Merte K., 2000, J Biomed Mater Res, 53:, 86, 10.1002/(SICI)1097-4636(2000)53:1<86::AID-JBM12>3.0.CO;2-Z

Schneider H, Frohlich M, Erler G, Engelke C, Merte K. Interaction patterns between dentin and adhesive on prepared class V cavities in vitro and in vivo. J Biomed Mater Res 2000;53:86-92.

Carrilho MR, Carvalho RM, Tay FR, Pashley DH., 2004, Am J Dent, 17:, 104

Carrilho MR, Carvalho RM, Tay FR, Pashley DH. Effects of storage media on mechanical properties of adhesive systems. Am J Dent 2004;17:104-108.

Hashimoto M, Ohno H, Sano H, Kaga M, Oguchi H., 2003, J Biomed Mater Res B Appl Biomater, 66:, 324

Hashimoto M, Ohno H, Sano H, Kaga M, Oguchi H. Degradation patterns of different adhesives and bonding procedures. J Biomed Mater Res B Appl Biomater 2003;66:324-330.

Oliveira SS, Marshall SJ, Habelitz S, Gansky SA, Wilson RS, Marshall GW, Jr., 2004, Eur J Oral Sci, 112:, 376, 10.1111/j.1600-0722.2004.00142.x

Oliveira SS, Marshall SJ, Habelitz S, Gansky SA, Wilson RS, Marshall GW, Jr. The effect of a self-etching primer on the continuous demineralization of dentin. Eur J Oral Sci 2004;112:376-383.

Reis AF, Bedran-Russo AK, Giannini M, Pereira PN., 2007, J Oral Rehabil, 34:, 213, 10.1111/j.1365-2842.2006.01656.x

Reis AF, Bedran-Russo AK, Giannini M, Pereira PN. Interfacial ultramorphology of single-step adhesives: nanoleakage as a function of time. J Oral Rehabil 2007;34:213-221.

Malacarne J, Carvalho RM, de Goes MF, et al., 2006, Dent Mater, 22:, 973, 10.1016/j.dental.2005.11.020

Malacarne J, Carvalho RM, de Goes MF, et al. Water sorption/solubility of dental adhesive resins. Dent Mater 2006;22:973-980.

Carvalho RM, Chersoni S, Frankenberger R, Pashley DH, Prati C, Tay FR., 2005, Biomaterials, 26:, 1035, 10.1016/j.biomaterials.2004.04.003

Carvalho RM, Chersoni S, Frankenberger R, Pashley DH, Prati C, Tay FR. A challenge to the conventional wisdom that simultaneous etching and resin infiltration always occurs in selfetch adhesives. Biomaterials 2005;26:1035-1042.

Lopes GC, Baratieri LN, de Andrada MA, Vieira LC., 2002, Quintessence Int, 33:, 213

Lopes GC, Baratieri LN, de Andrada MA, Vieira LC. Dental adhesion: present state of the art and future perspectives. Quintessence Int 2002;33:213-224.

Cho BH, Dickens SH., 2004, Dent Mater, 20:, 107, 10.1016/S0109-5641(03)00071-X

Cho BH, Dickens SH. Effects of the acetone content of single solution dentin bonding agents on the adhesive layer thickness and the microtensile bond strength. Dent Mater 2004;20:107-115.

Mohan B, Kandaswamy D., 2005, Quintessence Int, 36:, 511

Mohan B, Kandaswamy D. A confocal microscopic evaluation of resin-dentin interface using adhesive systems with three different solvents bonded to dry and moist dentinan in vitro study. Quintessence Int 2005;36:511-521.

Perdigao J, Frankenberger R., 2001, Quintessence Int, 32:, 385

Perdigao J, Frankenberger R. Effect of solvent and rewetting time on dentin adhesion. Quintessence Int 2001;32:385-390.

Pereira GD, Paulillo LA, De Goes MF, Dias CT., 2001, J Adhes Dent, 3:, 257

Pereira GD, Paulillo LA, De Goes MF, Dias CT. How wet should dentin be? Comparison of methods to remove excess water during moist bonding. J Adhes Dent 2001;3:257-264.

Ritter AV, Bertoli C, Swift EJ, Jr., 2001, Am J Dent, 14:, 221

Ritter AV, Bertoli C, Swift EJ, Jr. Dentin bond strengths as a function of solvent and glutaraldehyde content. Am J Dent 2001;14:221-226.

Velazquez E, Vaidyanathan J, Vaidyanathan TK, Houpt M, Shey Z, Von Hagen S., 2003, Quintessence Int, 34:, 548

Velazquez E, Vaidyanathan J, Vaidyanathan TK, Houpt M, Shey Z, Von Hagen S. Effect of primer solvent and curing mode on dentin shear bond strength and interface morphology. Quintessence Int 2003;34:548-555.

Abdalla AI, Garcia-Godoy F., 2002, Am J Dent, 15:, 31

Abdalla AI, Garcia-Godoy F. Morphological characterization of single bottle adhesives and vital dentin interface. Am J Dent 2002;15:31-34.

Reis A, Loguercio AD., 2009, Oper Dent, 34:, 384, 10.2341/08-117

Reis A, Loguercio AD. A 36-month clinical evaluation of ethanol/water and acetone-based etch-and-rinse adhesives in non-carious cervical lesions. Oper Dent 2009;34:384-391.

Chersoni S, Suppa P, Breschi L, et al., 2004, Dent Mater, 20:, 796, 10.1016/j.dental.2003.11.010

Chersoni S, Suppa P, Breschi L, et al. Water movement in the hybrid layer after different dentin treatments. Dent Mater 2004;20:796-803.

Armstrong SR, Vargas MA, Chung I, et al., 2004, Oper Dent, 29:, 705

Armstrong SR, Vargas MA, Chung I, et al. Resin-dentin interfacial ultrastructure and microtensile dentin bond strength after five-year water storage. Oper Dent 2004;29:705-712.

Perdigao J, Lambrechts P, Van Meerbeek B, Vanherle G, Lopes AL., 1995, J Biomed Mater Res, 29:, 1111, 10.1002/jbm.820290911

Perdigao J, Lambrechts P, Van Meerbeek B, Vanherle G, Lopes AL. Field emission SEM comparison of four postfixation drying techniques for human dentin. J Biomed Mater Res 1995;29:1111-1120.

Tagami J, Nakajima M, Shono T, Takatsu T, Hosoda H., 1993, Am J Dent, 6:, 145

Tagami J, Nakajima M, Shono T, Takatsu T, Hosoda H. Effect of aging on dentin bonding. Am J Dent 1993;6:145-147.

Tay FR, Gwinnett AJ, Pang KM, Wei SH., 1995, J Dent Res, 74:, 1168, 10.1177/00220345950740050501

Tay FR, Gwinnett AJ, Pang KM, Wei SH. Variability in microleakage observed in a total-etch wet-bonding technique under different handling conditions. J Dent Res 1995;74:1168-1178.

Sano H, Yoshiyama M, Ebisu S, et al., 1995, Oper Dent, 20:, 160

Sano H, Yoshiyama M, Ebisu S, et al. Comparative SEM and TEM observations of nanoleakage within the hybrid layer. Oper Dent 1995;20:160-167.

Do Amaral RC, Stanislawczuk R, Zander-Grande C, Michel MD, Reis A, Loguercio AD., 2009, J Dent, 37:, 82, 10.1016/j.jdent.2008.09.010

Do Amaral RC, Stanislawczuk R, Zander-Grande C, Michel MD, Reis A, Loguercio AD. Active application improves the bonding performance of self-etch adhesives to dentin. J Dent 2009;37:82-90.

Ding PG, Wolff D, Pioch T, Staehle HJ, Dannewitz B., 2009, Dent Mater, 25:, 135, 10.1016/j.dental.2008.05.009

Ding PG, Wolff D, Pioch T, Staehle HJ, Dannewitz B. Relationship between microtensile bond strength and nanoleakage at the composite-dentin interface. Dent Mater 2009;25:135-141.

Spencer P, Wang Y., 2002, J Biomed Mater Res, 62:, 447, 10.1002/jbm.10364

Spencer P, Wang Y. Adhesive phase separation at the dentin interface under wet bonding conditions. J Biomed Mater Res 2002;62:447-456.

Tay FR, Gwinnett JA, Wei SH., 1996, Dent Mater, 12:, 236, 10.1016/S0109-5641(96)80029-7

Tay FR, Gwinnett JA, Wei SH. Micromorphological spectrum from overdrying to overwetting acid-conditioned dentin in waterfree acetone-based, single-bottle primer/adhesives. Dent Mater 1996;12:236-244.

Cardoso MV, de Almeida Neves A, Mine A, et al., 2011, Aust Dent J, 56

Cardoso MV, de Almeida Neves A, Mine A, et al. Current aspects on bonding effectiveness and stability in adhesive dentistry. Aust Dent J 2011;56 Suppl 1:31-44.

Ramos L., 2004, Porto: Faculdade de Medicina Dentária da Universidade do Porto, 25

Ramos L. Estudo comparativo da infiltração marginal com duas “gerações” de adesivos: total-etch em sistema monofrasco versus sistema self-etching. Porto: Faculdade de Medicina Dentária da Universidade do Porto 2004;25-26, 67-72

Salz U, Zimmermann J, Zeuner F, Moszner N., 2005, J Adhes Dent, 7:, 107

Salz U, Zimmermann J, Zeuner F, Moszner N. Hydrolytic stability of self-etching adhesive systems. J Adhes Dent 2005;7:107-116.

Pashley DH, Tay FR, Breschi L, et al., 2011, Dent Mater, 27:, 1, 10.1016/j.dental.2010.10.016

Pashley DH, Tay FR, Breschi L, et al. State of the art etch-andrinse adhesives. Dent Mater 2011;27:1-16.

Reis AF, Arrais CA, Novaes PD, Carvalho RM, De Goes MF, Giannini M., 2004, J Biomed Mater Res B Appl Biomater, 71:, 90

Reis AF, Arrais CA, Novaes PD, Carvalho RM, De Goes MF, Giannini M. Ultramorphological analysis of resin-dentin interfaces produced with water-based single-step and two-step adhesives: nanoleakage expression. J Biomed Mater Res B Appl Biomater 2004;71:90-98.

Nikaido T, Kunzelmann KH, Ogata M, et al., 2002, J Adhes Dent, 4:, 31

Nikaido T, Kunzelmann KH, Ogata M, et al. The in vitro dentin bond strengths of two adhesive systems in class I cavities of human molars. J Adhes Dent 2002;4:31-39.

Van Meerbeek B, De Munck J, Yoshida Y, et al., 2003, Oper Dent, 28:, 215

Van Meerbeek B, De Munck J, Yoshida Y, et al. Buonocore memorial lecture. Adhesion to enamel and dentin: current status and future challenges. Oper Dent 2003;28:215-235.

Sano H, Yoshikawa T, Pereira PN, et al., 1999, J Dent Res, 78:, 906, 10.1177/00220345990780041101

Sano H, Yoshikawa T, Pereira PN, et al. Long-term durability of dentin bonds made with a self-etching primer, in vivo. J Dent Res 1999;78:906-911.

Chersoni S, Suppa P, Grandini S, et al., 2004, J Dent Res, 83:, 459, 10.1177/154405910408300605

Chersoni S, Suppa P, Grandini S, et al. In vivo and in vitro permeability of one-step self-etch adhesives. J Dent Res 2004;83:459-464.

Tay FR, Pashley DH, Suh BI, Carvalho RM, Itthagarun A., 2002, J Dent, 30:, 371, 10.1016/S0300-5712(02)00064-7

Tay FR, Pashley DH, Suh BI, Carvalho RM, Itthagarun A. Single-step adhesives are permeable membranes. J Dent 2002;30:371-382.

King NM, Tay FR, Pashley DH, et al., 2005, Am J Dent, 18:, 126

King NM, Tay FR, Pashley DH, et al. Conversion of one-step to two-step self-etch adhesives for improved efficacy and extended application. Am J Dent 2005;18:126-134.

Duarte S, Jr., Phark JH, Varjao FM, Sadan A., 2009, Dent Mater, 25:, 589, 10.1016/j.dental.2008.10.012

Duarte S, Jr., Phark JH, Varjao FM, Sadan A. Nanoleakage, ultramorphological characteristics, and microtensile bond strengths of a new low-shrinkage composite to dentin after artificial aging. Dent Mater 2009;25:589-600.

Hashimoto M, Ito S, Tay FR, et al., 2004, J Dent Res, 83:, 843, 10.1177/154405910408301104

Hashimoto M, Ito S, Tay FR, et al. Fluid movement across the resin-dentin interface during and after bonding. J Dent Res 2004;83:843-848.

Tagami J, Sugizaki J, Hosoda H., 1990, Shika Zairyo Kikai, 9:, 240

Tagami J, Sugizaki J, Hosoda H. Effect of various pretreatments for dentin bonding on dentin permeability. Shika Zairyo Kikai 1990;9:240-246.

Thông tin
Thông tin xuất bản

Journal of Contemporary Dental Practice

Tập 14 Số 4

691-699

Thông tin tác giả