Inclusion Compound of Poly(vinyl alcohol) with Multivalent Molybdenum Coordination Compound
Tóm tắt
An inclusion compound of Mo(VI,V,IV) complexes and poly(vinyl alcohol) (PVA) that contains some carbonyl groups was prepared by a photoelectron transfer reaction between PVA and 12-molybdophosphoric acid (PMo12). A dark-blue film was obtained when the aqueous solution of PMo12 and PVA was irradiated with UV light. The film exhibited the characteristic electron spin resonance (ESR) signal of Mo(V). The existence of Mo(VI,V,IV) complexes was supported by XPS analysis of the film. Furthermore, the infrared (IR) and ultraviolet–visible (UV–Vis) spectra of the film showed weak absorption bands at 1710 cm−1 and 300–314 nm that are consistent with carbonyl groups, which presumably are a result of partial oxidation of secondary hydroxyl groups on PVA. Differential scanning calorimetry (DSC) of the dark-blue film exhibited a peak at 220.3°C that is different from PMo12 and PVA. Except for the IR absorption at 1710 cm−1, the wavelengths and shapes of the other IR bands were similar to those of PVA. The UV–Vis spectrum of the film showed a new absorption band at 742–770 nm. In addition, the XRD spectrum of the film, the diffraction angles, and the crystalline sites were different from that in PMo12 or PVA. However, the peak shape was similar to that of PVA. In summary, the DSC, IR, UV–Vis, and XRD data support a Mo(VI,V,IV) complex that is included into the spiral tube structure of PVA, which contains some carbonyl groups.
Tài liệu tham khảo
X. Cheng, Q. Meng, and H. Yan, Introduction to Supermolecule Chemistry (Chinese Petroleum and Chemical Press, Beijing, 1996), pp. 4.
X. Cheng, Y. Su, and H. Guan, Preprint of 6th Pacific Polymer Conference, Guangzhou, China, Dec. 1999, p. 337.
X. Cheng, Y. Su, and H. Guan, J. Molecular Sci. 16(2), 118 (2000).
S. Katsuki. Surface 25(1), 28 (1987).
H. Taketa, S. Katsuki, T. Sciyama, and N. Yamazoe, J. Phys. Chem. 90, 2959 (1986).
T. Yamase, R. Sasahi, and T. Ikawa, J. Chem. Soc. Dalton Trans, p. 628 (1981).
T. Yamase, Org. Syn. Chem. Soc. 43(3), 249 (1985).
C. Cheng and Y. Su, Acta Inorg. Chem. 7(2), 212 (1991).
K. Wang, C. Luo, and X. Zhou, Modern Instrumental Analysis for Polymers (Qing Hua University Press, Beijing, 1989), p. 31.
T. Yamase, J. Chem. Soc., Dalton Trans., p. 283 (1978).
C. Cheng, Physical Chemistry of Surfaces (Science Technique Reference Press, Beijin, 1995), p. 668.
T. H. Fleisch and G. J. Mains, J. Chem. Phys. 7(6), 780 (1982).
Wuhan University, Analytical Chemistry (People Education Press, Beijing, 1977), p. 113.
G. Xu, Materials Structure, Vol. II (People Education Press, Beijing, 1961), p. 451.
D. Braun, Pure Appl. Chem. 26, 173 (1973).
F. Cramer and S. Li, Inclusion Complexes (Science Press, Beijing, 1963), pp. 6, 9.
Z. Zhao, X. Zhou, S. Zhang, and W. Zhao, Instrumental Analysis (Higher Education Press, Beijing, 1990), p. 153.
C. Paul and Z. Hiemem, Principles of Colloid and Surface Chemistry (Marcel Dekker, New York, 1977), p. 78.
C. Cheng and Y. Su, Fujian Shifang Daxue Xuebao 6(3), 7 (1990).
K. Takemoto, M. Miyata, and K. Kimura, Inclusion Compounds (Tokyo Kagaku Toujin, 1989), pp. 1, 11–12, 185.