Hot-cracks reduction during Laser Beam Welding in vacuum of conventionally cast Alloy-247 LC

El-Magd, 2009 Seidel, 2018, Additive Manufacturing of Powdery Ni-Based Superalloys Mar-M-247 and CM 247 LC in Hybrid Laser Metal Deposition, Metall and Mat Trans A, 49, 3812, 10.1007/s11661-018-4777-y Henderson, 2004, Nickel based superalloy welding practices for industrial gas turbine applications, Science and Technology of Welding and Joining, 9, 13, 10.1179/136217104225017099 Kou, 2003 Yan, 2014, Microstructure evolution and mechanical properties of Inconel 740H during aging at 750 °C, Mater. Sci. Eng. A, 589, 153, 10.1016/j.msea.2013.09.076 Tsai, 1999, Hot cracking susceptibility of fillers 52 and 82 in alloy 690 welding, Metall. Mater. Trans. A, 30, 417, 10.1007/s11661-999-0331-2 Dilthey, 2005 Cao, 2009, Effect of pre- and post-weld heat treatment on metallurgicaland tensile properties of Inconel 718 alloy butt joints weldedusing 4 kW Nd:YAG laser, J. Mater.Sci., 44, 4557, 10.1007/s10853-009-3691-5 Fink, 2014, Verbesserung der schweißtechnischen Verarbeitung von Nickel-Basis-Sandform- und -Schleudergusslegierungen, DVS-Berichte Band, 306, 295 Senger, 2020, Effect of the temperature gradient on the hot cracking susceptibility for electron beam welding of Alloy 247 LC, Materials Testing, 62, 7, 10.3139/120.111538 Reisgen, 2016, Laser beam welding under vacuum of high grade materials, Weld World, 60, 403, 10.1007/s40194-016-0302-3 Blumm, 1994 Bruegel, 2011 Radaj, 1992