High immobilization of soil cesium using ball milling with nano-metallic Ca/CaO/NaH2PO4: implications for the remediation of radioactive soils
Tóm tắt
This report shows that cesium can be immobilized in soils with an efficiency of 96.4% by ball milling with nano-metallic Ca/PO4. In Japan, the major concern on 137Cs deposition and soil contamination due to the emission from the Fukushima Daiichi nuclear power plant showed up after a massive quake on March 11, 2011. The accident rated 7, the highest possible on the international nuclear event scale, released 160 petabecquerels (PBq) of iodine 131I and 15 PBq of 137Cs according to the Japanese Nuclear and Industrial Safety Agency. Both 137Cs and 131I radioactive nuclides are increasing cancer risk. Nonetheless, 137Cs, with a half-life of about 30 years compared with 8 days for 131I, is a major threat for agriculture and stock farming and, in turn, human life for decades. Therefore, in Japan, the 137Cs fixation and immobilization in contaminated soil is the most important problem, which should be solved by suitable technologies. Ball milling treatment is a promising treatment for the remediation of cesium-contaminated soil in dry conditions. Here, we studied the effect, factors and mechanisms of soil Cs immobilization by ball milling with the addition of nano-metallic Ca/CaO/NaH2PO4, termed “nano-metallic Ca/PO4.” We used scanning electron microscopy combined with electron dispersive spectroscopy (SEM/EDS) and X-ray diffraction. Results show that immobilization efficiency increases from 56.4% in the absence of treatment to 89.9, 91.5, and 97.7 when the soil is ball-milled for 30, 60 and 120 min, respectively. The addition of nano-metallic Ca/PO4 increased the immobilization efficiency to about 96.4% and decreased the ball milling time. SEM/EDS analysis allows us to observe that the amount of Cs decreased on soil particle surface. Use of nano-metallic Ca/PO4 over a short milling time also decreases Cs leaching. Therefore, ball milling with nano-metallic Ca/PO4 treatment may be potentially applicable for the remediation of radioactive Cs-contaminated soil in dry conditions.
Tài liệu tham khảo
Birke V (2002) Reductive dehalogenation of recalcitrant polyhalogenated pollutants using ball milling. In: Gavaskar R, Chen ASC (eds) Remediation of chlorinated and recalcitrant compounds-2002. Battelle Press, Columbus, OH
Caschili S, Delogu F, Concas A, Pisu M, Cao G (2006) Mechanically induced self propagating reactions: analysis of reactive substrates and degradation of aromatic sulfonic pollutants. Chemosphere 63:987–995
Concas A, Lai N, Pisu M, Cao G (2006) Modeling of combination processes in Spex mixer/mill. Chem Eng Sci 61:3746–3760
Ganjidoust H, Hassan A, Ashkiki AR (2009) Cement base solidification/stabilization of heavy metal contaminated soils with objective of achieving high compressive strength of the final matrix. Trans A Civil Eng 16:107–115
Ghaffar A, Tabata M, Mazher F, Mashiatu A (2011) High dechlorination of PCBs catalysed by carbon under mild conditions. Environ Chem Lett. doi:10.1007/s10311-011-0339-x
JIS A 1203-1999 (1999) Test method for water content of soils. Japanese Industrial Standard Committee, Tokyo
JIS M 8856-1998 (1998) Methods for chemical analysis of high-alumina raw material for ceramics. Japanese Industrial Standard Committee, Tokyo
Krivenko PV, Skurchinskaya JV, Lavrinenko LV, Dhir RK, Jones MR (1993) Environmentally safe immobilization of alkali metal radioactive waste, concrete 2000. E&FN Spon, London, pp 1579–1589
Lair GJ, Gerzabek MH, Haberhauer G (2007) Sorption of heavy metals on organic and inorganic soil constituents. Environ Chem Lett 5:23–27
Lichtfouse E, Schwarzbauer J, Robert D (2012) Social chemistry. Environ Chem Lett 10:1–4. doi:10.1007/s10311-011-0333-3
Lu L, Lai MO, Zhang S (1997) Diffusion in mechanical alloying. J Mater Process Tech 67:100–104
Ministry of Environment Government of Japan (2003) Matters providing for measurement method of soil elution test, Notification No. 18, March 6, 2003
Mitoma Y, Tasaka N, Takase M, Masuda T, Tashiro H, Naoyoshi E, Oki T (2006) Calcium-promoted catalytic degradation of PCDDs, PCDFs, and coplanar PCBs under a mild wet process. Environ Sci Technol 40:1849–1854
Mitoma Y, Miyata H, Egashira N, Simion A, Kakeda M, Simion C (2011) Mechanochemical degradation of chlorinated contaminants in fly ash with a calcium-based degradation reagent. Chemosphere 83:1326–1330
Monagheddu M, Mulas G, Doppiu S, Cocco G, Raccanelli S (1999) Reduction of polychlorinated dibenzodioxins and dibenzofurans in contaminated muds by mechanically induced combustion reactions. Environ Sci Technol 33:2485–2488
Montinaro S, Concas A, Pisu M, Cao G (2007) Remediation of heavy metals contaminated soils by ball milling. Chemosphere 67:631–639
Mulas G, Loiselle S, Schiffini L, Cocco G (1997) The Mechano- chemical self-propagating reactions between hexachlorobenzene and calcium hydride. J Solid State Chem 129:263–270
Nakayama S, Itoh K (2003) Immobilization of cesium to HZr2(PO4)3 using a autoclave. J Nuclear Sci Technol 40:631–633
Osmanlioglu AE (2002) Immobilization of radioactive waste by cementation with purified kaolina clay. Waste Manag 22:481–483
Patel P (2011) Post-fukushima radiation mapped: cesium in soil a problem for agriculture IEEE, Spectrum pp 1–2 (http://spectrum.ieee.org/energy/environment/postfukushima-radiationano-metallicapped/1)
Patricia M, Alicia FC (2008) Phosphates for Pb immobilization in soils: a review. Environ Chem Lett 6:121–133
Plecas IB, Pavlovic RS, Pavlovic SD (2003) Leaching of 60Co and 137Cs from spent ion exchange resins in cement–bentonite clay matrix. Bull Mater Sci 26:699–701
Polettini A, Pomi R, Sirini P, Testa (2001) Properties of Portland cement-stabilized MSWI fly ashes. J Hazard Mater 88:123–138
Saeki S, Kano J, Saito F, Shimme K, Masuda S, Inoue T (2001) Effect on dechlorination of PVC by mechanochemical treatment. J Mater Cycle Waste Manag 3:20–23
Sakr K, Sayed MS, Hafez MB (2003) Immobilization of radioactive waste in mixture of cement, clay and polymer. J Radio Nucl Chem 256:179–184
Schaffer GB, McCormick PG (1992) On the kinetics of mechanical alloying. Metall Trans A 23:1285–1290
Shi C, Day RL (1996) Alkali-slag cements for the solidification of radioactive wastes. In: Wiles, Gilliam (eds) Stabilization and solidification of hazardous, radioactive, and mixed wastes, vol 1240. American Society for Testing and Materials, ASTM STP, Philadelphia, pp 163–173
Skripkiunas G, Sasnauskas V, Dauksys M, Dauksys D (2007) Peculiarities of hydration of cement paste with addition of hydro sodalite. Mater Sci 25:627–635
Strkalj A, Malina J, Radenoic A (2009) Waste mould sand potential low-cost sorbent for nickel and chromium ions from aqueous solution. Mater Environ 56:118–125
Wu X, Yen S, Xiaodong S, Mingshu T (1991) Alkali-activated cement based radioactive waste forms. Cem Concr Res 21:16–20
Yasunari TJ, Stohl A, Hayano RS, Burkhart JF, Eckhardt S, Yasunari T (2011) Cesium137 deposition and contamination of Japanese soils due to the Fukushima nuclear accident. PNAS 108: 19530–19534. www.pnas.org/cgi/doi/10.1073/pnas.1112058108
Zhang Q, Matsumoto H, Saito F, Baron M (2002) Debromination of hexabromobenzene by its co-grinding with CaO. Chemosphere 48:787–793