High-Temperature Fatigue of a Hybrid Aluminum Metal Matrix Composite
Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science - Tập 45 - Trang 501-509 - 2013
Tóm tắt
An aluminum metal matrix composite (MMC) brake drum was tested in fatigue at room temperature and extreme service temperatures. At room temperature, the hybrid composite did not fail and exceeded estimated vehicle service times. At higher temperatures (62 and 73 pct of the matrix eutectic), fatigue of a hybrid particle/fiber MMC exhibited failure consistent with matrix overloading. Overaging of the A356 matrix coupled with progressive fracture of the SiC particles combined to create the matrix overload condition. No evidence of macro-fatigue crack initiation or growth was observed, and the matrix–particle interface appeared strong with no debonding, visible matrix phases, or porosity. An effective medium model was constructed to test the hypothesis that matrix overloading was the probable failure mode. The measured particle fracture rate was fit using realistic values of the SiC Weibull strength and modulus, which in turn predicted cycles to failure within the range observed in fatigue testing.
Tài liệu tham khảo
M. D. Rafiquzzaman (2008) J Solid Mech Mater Eng 2:47–57.
D.J. Lloyd (1994) Int Mater Rev 39:1–23.
J. N. Hall, J. W. Jones and A. K. Sachdev (1994) Mater Sci Eng A 183:69–80.
Y. Ochi, K. Masaki, T. Matsumura and M. Wadasako (2007) Mater Sci Eng A 468:230–36.
A. E. Herr, S. Canumalla and R. N. Pangborn (1995) Mater Sci Eng A 200: 181–91.
T. S. Srivatsan and M. Al-Hajri (2002) Composites B 33:391–404.
H. Z. Ding, H. Biermann and O. Hartmann (2002) Compos Sci Technol 62:2189–99.
J. D. Eshelby (1957) Proc R Soc Lond 241:376–96.
J. D. Eshelby (1959) Proc R Soc Lond 252:561–69.
L. M. Brown and D. R. Clarke (1975) Acta Metall 23:821–30.
S. F. Corbin and D. S. Wilkinson (1994) Acta Metall Mater 42:1311–18.
C. W. Nan and D. R. Clarke (1996) Acta Mater 44:3801–11.
M. Kero, T. Hewer, and J. Zills: SAE Technical Paper 2012-01-1922, 2012.
J. G. Kaufman, Properties of Aluminum Alloys: Tensile, Creep and Fatigue Data at High and Low Temperatures, ASM International, Materials Park, OH, 1999, p. 257.
A. Mkaddem and M. El Mansori (2009) Mater Des 30:3518–24.
L. L. Snead, T. Nozawa, Y. Katoh, T. S. Byun, S. Kondo and D. A. Petti (2007) J Nucl Mater 371:329–77.
M.E. Fitzpatrick: Residual Stress. Vii, 2006, vols. 524–525, pp. 769–74.