Heat Sink Effect on 6061 Aluminum Alloy Welds with Different Partial Aging Conditions

Journal of Materials Engineering and Performance - Tập 29 - Trang 4339-4350 - 2020
C. M. Gómora1, R. R. Ambriz2, J. Zuno-Silva1, D. Jaramillo2
1Universidad Autónoma del Estado de Hidalgo, Escuela Superior de Ciudad Sahagún, Tepeapulco, Mexico
2Instituto Politécnico Nacional CIITEC-IPN, Ciudad de México, Mexico

Tóm tắt

Partially aged 6061 aluminum plates were welded by the gas metal arc welding process. During the welding process, a cooling system to act as a heat sink was used to extract the heat coming out from the welding process. To determine the experimental weld thermal cycles, K type thermocouples were placed at the heat affected zone. Finite element was used to compute the thermal distribution and isothermal sections generated by welding. The temperature measurements, Vickers microhardness profiles and tensile tests were observed to be related with the microstructural β″ to β′ phase transformation. The over-aging of the heat affected zone tends to diminish when the heat sink is used as compared with the reference welding condition. An increase on tensile strength (about 5.8%) and ductility (close to 29%), for welds performed in partial aging materials with respect to the welds with artificial aging condition (6061-T6 alloy) was also observed.

Tài liệu tham khảo

R.R. Ambriz and D. Jaramillo, Mechanical Behavior of Precipitation Hardened Aluminum Alloys: Light Metal Alloys Applications, W.A. Monteiro, Ed., Rijeka, Croatia, INTECH, 2014, p. 35–59 V. Malin, Study of Metallurgical Phenomena in the HAZ of 6061-T6 Aluminum Welded Joints, Weld. J., 1995, 74(9), p 305–318 F. Fadaeifard, K.A. Matori, F. Garavi, M. Al-Falahi, and G.V. Sarrigani, Effect of Post Weld Heat Treatment on Microstructure and Mechanical Properties of Gas Tungsten Arc Welded AA6061-T6 Alloy, Trans. Nonferrous Met. Soc., 2016, 26(12), p 3102–3114 R.R. Ambriz, G. Barrera, R. García, and V.H. López, The Microstructure and Mechanical Strength of Al-6061-T6 GMA Welds Obtained with the Modified Indirect Electric Arc Joint, Mater. Des., 2010, 31(6), p 2978–2986 J. Fathi, P. Ebrahimzadeh, R. Farasati, and R. Teimouri, Friction Stir Welding of Aluminum 6061-T6 in Presence of Watercooling: Analyzing Mechanical Properties and Residual Stress Distribution, Int. J. Lightweight Mater. Manuf., 2019, 2(2), p 107–115 X.H. Zeng, P. Xue, L.H. Wu, D.R. Ni, B.L. Xiao, K.S. Wang, and Z.Y. Ma, Microstructural Evolution of Aluminum Alloy During Friction Stir Welding Under Different Tool Rotation Rates and Cooling Conditions, J. Mater. Sci. Technol., 2019, 35(6), p 972–981 C. Rathinasuriyan and V.S. Senthil Kumar, Experimental Investigation of Weld Characteristics on Submerged Friction Stir Welded 6061-T6 Aluminum Alloy, J. Mech. Sci. Technol., 2017, 31(4), p 3925–3933 C.M. Gómora, R.R. Ambriz, F.F. Curiel, and D. Jaramillo, Heat Distribution in Welds of a 6061-T6 Aluminum Alloy Obtained by Modified Indirect Electric Arc, J. Mater. Process. Technol., 2017, 243(5), p 433–441 K. Easterling, Introduction to the Physical Metallurgy of Welding, Butterworth-Heinemann, Oxford, UK, 1992, p 21 K. Poorhaydari, B.M. Patchett, and D.G. Ivey, Estimation of Cooling Rate in the Welding of Plates with Intermediate Thickness, Weld. J., 2005, 84(10), p 149–155 O.R. Myhr, O. Grong, H.G. Fjaer, and C.D. Mariora, Modelling of the Microstructure and Strenght Evolution in Al-Mg-Si Alloys during Multistage Thermal Processing, Acta Mater., 2004, 52(17), p 4997–5008 J. Goldak, A. Chakravarti, and M. Bibby, A New Finite Element Model for Welding Heat Sources, Metall. Trans. B, 1984, 15(6), p 299–305 K.C. Mills, Recommended Values of Thermophysical Properties for Selected Commercial Alloys, ASM International, Cleveland, 2002, p 64–67 “Standard Test Methods for Tension Testing Wrougth and Cast Aluminum- and Magnesium- Alloy Products,” ASTM B557-15, ASTM, 2015, p 1–16 ASM Handbook, Heat Treating, ASM International, United States of America, 1991, p 1897 G.A. Edwards, K. Stiller, G.L. Dunlop, and M.J. Couper, The Precipitation Sequence in Al-Mg-Si alloys, Acta Mater., 1998, 46(11), p 3893–3904 L.B. Ber, Accelerated Artificial Ageing Regimes of Commercial Aluminium Alloys. II: Al-Cu, Al-Zn-Mg-(Cu), Al-Mg-Si-(Cu) Alloys, Mater. Sci. Eng. A Struct., 2000, 280(1), p 91–96 L.B. Ber, Accelerated Artificial Ageing Regimes of Commercial Aluminum Alloys. I. Al-Cu-Mg Alloys, Mater. Sci. Eng. A Struct., 2000, 280(1), p 83–90 D. Maisonnette, M. Suery, D. Nelias, P. Chaudet, and T. Epicier, Effects of Heat Treatments on the Microstructure and Mechanical Properties of a 6061 Aluminium Alloy, Mater. Sci. Eng. A Struct., 2011, 528(6), p 2718–2724 W. Sha, Evaluation of Aging Precipitation Kinetics and Potential in Aluminum Alloys Using Indiscriminately Integrated Peak Areas in Calorimetry Curves, Metall. Mater. Trans. A, 2004, 35(9), p 3012–3015 M.J. Starink, The Determination of Activation Energy From Linear Heating Rate Experiments: A Comparison of the Accuracy of Isoconversion Methods, Thermochim. Acta, 2003, 404(1–2), p 163–176 S. Pogatscher, H. Antrekowitsch, T.E. Leitner, and P.J. Uggowitzer, Mechanisms Controlling the Artificial Aging of Al-Mg-Si Alloys, Acta Mater., 2011, 59(9), p 3352–3363 M. Murayama and K. Hono, Pre-Precipitate Clusters and Precipitation Processes in Al-Mg-Si Alloys, Acta Mater., 1999, 47(5), p 1537–1548 D. Yin, Q. Xiao, Y. Chen, H. Liu, D. Yi, B. Wang, and S. Pan, Effect of Natural Ageing and Pre-Straining on the Hardening Behaviour and Microstructural Response during Artificial Ageing of an Al-Mg-Si-Cu Alloy, Mater. Des., 2016, 95(4), p 329–339 J. Serrano Pérez, R.R. Ambriz, F.F. Curiel López, and D. Jaramillo Vigueras, Recovery of Mechanical Properties of a 6061-T6 Aluminum Weld by Heat Treatment After Welding, Metall. Mater. Trans. A, 2016, 47(6), p 3412–3422 N. Alatorre, R.R. Ambriz, B. Noureddine, A. Amrouche, A. Talha, and D. Jaramillo, Tensile Properties and Fusion Zone Hardening for GMAW and MIEA Welds of a 7075-T651 Alumium Alloy, Acta Metall. Sin., 2014, 27(4), p 694–704 P. Dong, D. Sun, and H. Li, Natural Aging Behaviour of Friction Stir Welded 6005A-T6 Aluminium Alloy, Mater. Sci. Eng. A Struct., 2013, 576(8), p 29–35 I. Kalemba, C. Hamilton, and S. Dymek, Natural Aging in Friction Stir Welded 7136-T76 Aluminum Alloy, Mater. Des., 2014, 60(8), p 295–301 J.C. Hou, H.J. Liu, and Y.Q. Zhao, Influences of Rotation Speed on Microstructures and Mechanical Properties of 6061-T6 Aluminum Alloy Joints Fabricated by Self-Reacting Friction Stir Welding Tool, Int. J. Adv. Manuf. Technol., 2014, 73(5), p 1073–1079 L. Zhou, G.H. Li, C.L. Liu, J. Wang, Y.X. Huang, J.C. Feng, and F.X. Meng, Microstructural Characteristics and Mechanical Properties of Al-Mg-Si Alloy Self-Reacting Friction Stir Welded Joints, Sci. Technol. Weld. Join., 2017, 22(8), p 438–445