Fine structure in quenched Fe-Al-C steels

Springer Science and Business Media LLC - Tập 3 - Trang 2163-2169 - 1972
R. Oshima1, CM. Wayman1
1Department of Metallurgy and Mining Engineering, University of Illinois at Urbana-Champaign, Urbana

Tóm tắt

The origin of “extra” spots in electron diffraction patterns taken from retained austenite and martensite in Fe-7 pct Al-2 pct C has been investigated. The present interpretation differs from that of previous investigators. It is concluded that a high density of fine carbide precipitates 50Å in diameter is responsible for the extra reflections. The precipitates have the perovskite structure and grow epitaxially in the austenite during quenching. When martensite forms at a lower temperature, the precipitates are transformedin situ.

Tài liệu tham khảo

M. Watanabe and C. M. Wayman:Met. Trans., 1971, vol. 2, p. 2221. M. Watanabe and C. M. Wayman:Met. Trans., 1971, vol. 2, p. 2229. Z. Nishiyama and M. Doi:Nippon Kinzoku Gakkai-Shi, 1944, vol. 8, p. 305. Z. Nishiyama, K. Shimizu, and M. Harada:Trans. J. Inst. Metals, 1970, vol. 11, p. 152. T. Tadaki, K. Shimizu, and T. Watanabe:Trans. J. Inst. Metals, in press. K. Löhberg and W. Schmidt:Arch. Eisenhüttenw., 1937, vol. 12, p. 607. L. S. Palatnik, I. A. Tananko, and Yu. G. Bobro:Sov. Phys. Cryst., 1964, vol. 9, p. 163. P. B. Hirsch,et ai:Electron Microscopy of Thin Crystals, Butterworth, p. 490, 1965. A. J. Bradley and A. H. Jay:Proc. Roy. Soc, 1932, vol. A136, p. 210. A. Lawley and R. W. Cahn:J. Phys. Chem. Solids, 1961. vol. 20, p. 204. M. Fallot:Ann. Phys., 1936, vol. 6, p. 356. H. Saito:Nippon Kinzoku Gakkai-Shi, 1950, vol. 14, p. 1. C. J. Smithells:Metal Reference Book, Butterworth, p. 593, 1962. P. L. Gruzin, V. G. Kostogonov, and P. A. Platanov:Dokl. Akad. Nauk SSSR, 1955, vol. 100, p. 1069. I. N. G. Frantsevich and I. I. Kovenskii:Dopov. Akad. Nauk Ukr., 1961, p. 1169.