Failure analysis in a vehicle accident reconstruction
Tóm tắt
A metallurgical and mechanical failure analysis was applied as part of a vehicle accident reconstruction of a multi-vehicle collision. One of these vehicles was a coal-hauling tractor-trailer. Examination of the trailer involved in the incident revealed a fatigue fracture to a primary lateral stiffener, along with a significant misalignment of the stiffener. Stress and fatigue analysis indicated that the misalignment severely degraded the fatigue life of the stiffener. Evaluation of the structural dynamics of the trailer after the fatigue fracture indicated decreased lateral stability. The decreased stability caused by fracture of the lateral stiffener allowed rollover of the trailer to occur while negotiating a curve. The failure sequence developed in this investigation proved consistent with all physical damage observed on the trailer and with witness accounts of the incident. The failure scenario developed in this investigation is compared with other conclusions made by other investigators to show that those conclusions are not consistent with all of the available evidence.
Tài liệu tham khảo
J.H. Cleland and D.R.H. Jones: “Shear Failure of a Road-Vehicle Steering Shaft,” Eng. Fail. Anal., 1997, 4(1), pp. 81–88.
J.M. Henshaw, V. Wood, and A.C. Hall: “Failure of Automobile Seat Belts Caused by Polymer Degradation,” Eng. Fail. Anal., 1999, 6(1), pp. 13–25.
A.M. Heyes: “Automotive Component Failures,” Eng. Fail. Anal., 1998, 5(2), pp. 129–41.
T.J. Mackin, S.C. Noe, K.J. Ball, B.C. Bedell, D.P. Bim-Merle, M.C. Bingaman, D.M. Bomleny, G.J. Chemlir, D.B. Clayton, and H.A. Evans: “Thermal Cracking in Disc Brakes,” Eng. Fail. Anal., 2002, 9(1), pp. 63–76.
E. Makevet and I. Roman: “Failure Analysis of a Final Drive Transmission in Off-Road Vehicles,” Eng. Fail. Anal., 2002, 9(5), pp. 579–92.
F.S. Silva: “Analysis of a Vehicle Crankshaft Failure,” Eng. Fail. Anal., 2003, 10(5), pp. 605–16.
J. Vogwell: “Analysis of a Vehicle Wheel Shaft Failure,” Eng. Fail. Anal., 1998, 5(4), pp. 271–77.
S. Suresh: “Fatigue Crack Initiation in Ductile Solids,” Fatigue of Materials, Cambridge University Press, 1998, pp. 132–62.
J.A. Bannantine, J.J. Comer, and J.L. Handrock: Fundamental of Metal Fatigue Analysis, Prentice Hall, Englewood Cliffs, N.J., 1997.
N.E. Dowling: Mechanical Behavior of Materials, 2nd ed., Prentice Hall, London, 1999.
R. Eger and U. Kiencke: “Modeling of Rollover Sequences,” Control Eng. Pract., 2003, 11(2), pp. 209–16.
F. Momiyama, K. Kitazawa, K. Miyazaki, H. Soma, and T. Takahashi: “Gravity Center Height Estimation for the Rollover Compensation System of Commercial Vehicles,” JSAE Rev., 1999, 20(4), pp. 493–97.