Extracting Al2O3 and TiO2 from Red Mud Smelting Separation Slag by Alkali and Acid Leaching Methods

Metals - Tập 13 Số 3 - Trang 552
Siwei Li1, Zhengqi Guo1, Jian Pan1, Deqing Zhu1, Tao Dong1, Shenghu Lu1
1School of Minerals Processing and Bioengineering, Central South University, Changsha, 410083, China

Tóm tắt

Recovery of valuable metals from red mud smelting separation slag is important for environmental protection and saving of natural resources. In this paper, we propose a recycling process of red mud smelting separation slag by mineral phase reconstruction conducted under an air atmosphere. In this process, NaOH and Ca(OH)2 roasting of Al2O3 and NaAlSiO4 was performed, and Al2O3 and SiO2 were converted into alkaline-soluble NaAlO2 and Ca2SiO4, respectively. In the consequent steps, more than 80% of Al2O3 was selectively dissolved into a leaching solution using a NaOH solution under 95 °C, and the obtained NaAlO2 solution can be used as a source for extracting alumina. Then, a 20 wt.% HCl solution was used to remove SiO2 from the residue, obtaining a SiO2-containing solution and a concentrated residue of undissolved TiO2 and CaO. Finally, this mineral phase reconstruction process can enable a higher metal leaching rate, and this study provides a novel, clean, and sustainable method for recycling valuable metals from red mud smelting separation slag.

Từ khóa


Tài liệu tham khảo

Khairul, 2019, The composition, recycling and utilization of Bayer red mud, Resour. Conserv. Recycl., 141, 483, 10.1016/j.resconrec.2018.11.006

Mukiza, 2019, Utilization of red mud in road base and subgrade materials: A review, Resour. Conserv. Recycl., 141, 187, 10.1016/j.resconrec.2018.10.031

Ghalehnovi, 2019, Effect of red mud (bauxite residue) as cement replacement on the properties of self-compacting concrete incorporating various fillers, J. Clean. Prod., 240, 118213, 10.1016/j.jclepro.2019.118213

(2022, December 12). Available online: https://international-aluminium.org/statistics/alumina-production/.

Wang, 2020, Comprehensive utilization status of red mud in China: A critical review, J. Clean. Prod., 289, 125136, 10.1016/j.jclepro.2020.125136

Liu, 2021, Treatment of Bayer-process red mud through Microbially induced carbonte precipitation, J. Mater. Civ. Eng., 33, 04021067, 10.1061/(ASCE)MT.1943-5533.0003691

Nie, 2019, Synergistic utilization of red mud for flue-gas desulfurization and fly ash-based geopolymer preparation, J. Hazard. Mater., 369, 503, 10.1016/j.jhazmat.2019.02.059

Huang, 2016, A perspective of stepwise utilization of Bayer red mud: Step two—Extracting and recovering Ti from Ti-enriched tailing with acid leaching and precipitate flotation, J. Hazard. Mater., 307, 318, 10.1016/j.jhazmat.2016.01.010

Wang, 2020, Applications of red mud as an environmental remediation material: A review, J. Hazard. Mater., 408, 124420, 10.1016/j.jhazmat.2020.124420

Liu, 2017, Sintered bayer red mud based ceramic bricks: Microstructure evolution and alkalis immobilization mechanism, Ceram. Int., 43, 13004, 10.1016/j.ceramint.2017.07.036

Ding, 2019, Iron extraction from red mud using roasting with sodium salt, Miner. Process. Extr. Metall. Rev., 42, 153

Shrey, 2018, Microwave Reduction of Red Mud for Recovery of Iron Values, J. Sustain. Metall., 4, 427, 10.1007/s40831-018-0183-3

Valeev, D., Zinoveev, D., Kondratiev, A., Lubyanoi, D., and Pankratov, D. (2019). Reductive Smelting of Neutralized Red Mud for Iron Recovery and Produced Pig Iron for Heat-Resistant Castings. Metals, 10.

Gao, 2021, Aluminum extraction technologies from high aluminum fly ash, Rev. Chem. Eng., 37, 885, 10.1515/revce-2019-0032

Kudyba, 2021, Aluminum recovery from white aluminum dross by a mechanically activated phase separation and remelting process, JOM, 73, 2625, 10.1007/s11837-021-04730-x

Zinoveev, D., Pasechnik, L., Fedotov, M., Dyubanov, V., Grudinsky, P., and Alpatov, A. (2021). Extraction of valuable elements from red mud with a focus on using liquid media—A review. Recycling, 6.

Bayca, 2018, Optimization of leaching parameters of aluminum hydroxide extraction from bauxite waste using the Taguchi method, Environ. Prog. Sustain. Energy, 37, 196, 10.1002/ep.12654

Pasechnik, 2020, A promising process for transformation of hematite to magnetite with simultaneous dissolution of alumina from red mud in alkaline mediumAutoclave hydrometallurgical processing of alumina production red mud, Hydrometallurgy, 196, 105438, 10.1016/j.hydromet.2020.105438

Li, 2020, A new route for separation and recovery of Fe, Al and Ti from red mud, Resour. Conserv. Recycl., 168, 105314, 10.1016/j.resconrec.2020.105314

Yang, 2019, Study on Mineralogical Characteristics of Secondary Aluminum Ash, Nonferrous Met. Eng., 9, 117

Sun, 2016, Optimization of reaction conditions and mechanism of desilication of high-alumina fly ash, Res. Environ. Sci., 29, 753

Guo, 2004, Ions dissolving-out characteristics of calcined coal gangues in alkaline solutions and its structure, J. Chin. Ceram. Soc., 32, 1230

Sitarz, 2000, The non-ring cations influence on silicooxygen ring vibrations, J. Mol. Struct., 555, 357, 10.1016/S0022-2860(00)00621-9

Jin, 2002, The structural change of diphasic mullite gel studied by XRD and IR spectrum analysis, J. Eur. Ceram. Soc., 22, 1307, 10.1016/S0955-2219(01)00447-2

Li, 2010, Investigation on the activation of coal gangue by a new compound method, J. Hazard. Mater., 179, 515, 10.1016/j.jhazmat.2010.03.033

Song, 2004, Study on structural characteristic and mechanical property of coal gangue in the activation process, J. Chin. Ceram. Soc., 32, 358

Guo, 2009, Structure and pozzolanic activity of calcined coal gangue during the process of mechanical activation, J. Wuhan Univ. Technol., 24, 326, 10.1007/s11595-009-2326-7

Brachhold, 2021, Investigation of the synthesis and the alkali corrosion of potassium aluminosilicates by XRD and NMR, Ceram. Int., 47, 33596, 10.1016/j.ceramint.2021.08.269

Gupta, 2020, Multinuclear MAS NMR characterization of fly-ash-based advanced sodium aluminosilicate geopolymer: Exploring solid-state reactions, Chemistryselect, 5, 4920, 10.1002/slct.202000203

Chun, 2014, Recovery of Alumina from Magnetic Separation Tailings of Red Mud by Na2CO3 Solution Leaching, Metall. Mater. Trans. B., 45, 827, 10.1007/s11663-014-0023-1

Thông tin
Thông tin xuất bản

Metals

Tập 13 Số 3

552

Thông tin tác giả