Experimental study on polishing performance of CeO2 and nano-SiO2 mixed abrasive
Applied Nanoscience - 2018
Tóm tắt
In this paper, superfine SiO2 nanoparticles are utilized as composite abrasive additive to improve the polishing property of CeO2, which is prepared through chemical precipitation method by rare-earth chloride as raw materials, silicofluoric acid as fluoride, Na2CO3 as modifier, and NH4HCO3 as precipitator. XRD, SEM, particle size analyzer, and atomic force microscopy are applied to characterize the physical structure, morphology, and size distribution. Furthermore, the as-prepared composite abrasive is used to perform chemical mechanical polishing (CMP) experiment on K9 glass to identify the impact of different mass fraction of SiO2 on the CMP property of work materials. The results show that the composite abrasive contained 0.5% SiO2 has the best polishing property, the surface roughness, and material removal rate of glass after polishing can reach at 1.3157 nm and 22.6 nm/min, respectively.
Từ khóa
Tài liệu tham khảo
Armini S, Whelan CM, Maex K et al (2007) Composite polymer-core silica-shell abrasive particles during oxide CMP: a defectivity study. J Electrochem Soc 154(154):H667
Belkhir N, Bouzid D, Herold V (2009) Wear behavior of the abrasive grains used in optical glass polishing. J Mater Process Technol 209(20):6140–6145
Chai MX, Zhou XZ (2011) Evaluation of polishing property for silicon wafer of SiO2-CeO2 mixed oxides. J Chin Soc Rare Earths 29(3):365–370
Chen Y, Long RW, Chen ZG (2010) Preparation and polishing performance of CeO2@SiO2 composite abrasives. Mater Rev 24(18):35–38
Chen Y, Li ZN, Song ZT, Min GQ (2014) Effect of the core size of the core /shell structured PS/SiO2 composite abrasives on oxide-CMP behavior. J Funct Mater 45(19):19121–19127
Chen Y, Li Z, Miao N (2015) Polymethylmethacrylate (PMMA)/CeO2, Hybrid particles for enhanced chemical mechanical polishing performance. Tribol Int 82(82):211–217
Gao Q (2016) Polishing characteristics of fixed-abrasive pad by using nano-aggregate silica. Opt Precis Eng 24(10):2490–2497
Lu JX, Chen ZG, Long RW (2011) Preparation, characterization and performance of core-shell PS-CeO2 composite abrasives with different particle sizes. Chin J Nonferrous Metal 21(7):1777–1784
Savio G, Meneghello R, Concheri G (2009) A surface roughness predictive model in deterministic polishing of ground glass moulds. Int J Mach Tools Manuf 49(1):1–7
Shi YB (2013) The synthesis of cerium oxide based composite rare earth polishing powder and study of its performance. Dissertation, East China University of Science and Technology
Shi YB, Qiu-Fang WU, Yi H (2013) Preparation of SiO2@CeO2 composite abrasive and its polishing performance. Chin Rare Earths 34(1):53–58
Zhang Q, Huang G, Zhao Y (2014) Research on polishing performances and mechanisms of CeO2/ SiO2 composite abrasives. Lubr Eng 39(1):59–63