Experimental and modeling investigation of the failure resistance of Advanced High Strength Steels spot welds
Tóm tắt
Từ khóa
Tài liệu tham khảo
ISO 18278-2. Resistance welding – weldability. Part 2: alternative procedures for the assessment of sheet steels for spot welding. ISO standard; 2004.
ISO 14272. Specimen dimensions and procedure for cross tension testing resistance spot and embossed projection welds. ISO standard; 2001.
ISO 14273. Specimen dimensions and procedure for shear testing resistance spot, seam and embossed projection welds. ISO standard; 2002.
Nishi, 1982, Evaluation of spot weldability of high-strength sheet steels for automobile use, Nippon Steel Tech Rep, 20, 37
Williams, 1979, Spot weld size and fracture mode in low carbon mild steel, Metal Construct, 11, 541
Gould J, Workman D. Fracture morphologies of resistance spot welds exhibiting hold time sensitivity behavior. In: AWS detroit section (Ed.), Sheet metal welding conference VIII, 1998.
Dancette S. Comportement mécanique des soudures par points : mécanismes et stratégies de prédiction dans le cas des tôles en acier pour automobile. Ph.D. thesis, INSA-Lyon, Lyon; 2009.
Zuniga, 1997, Resistance spot weld failure loads and modes in overload conditions, vol. 27, 469
Chao, 2003, Ultimate strength and failure mechanism of resistance spot weld subjected to tensile, shear, or combined tensile/shear loads, J Engng Mater Technol, 125, 125, 10.1115/1.1555648
Moore, 1989, Failure mechanisms in rephosphorised sheet steel spot welds, Mater Sci Technol, 5, 492, 10.1179/mst.1989.5.5.492
Nait-Oultit B, Lens A, Klocker H. Mechanical behaviour of advanced high-strength steel resistance spot welds. In: AWS detroit section (Ed.), Sheet metal welding conference XIII, Livonia, MI, 2008.
Pouranvari, 2007, Effect of weld nugget size on overload failure mode of resistance spot welds, Sci Technol Weld Join, 12, 217, 10.1179/174329307X164409
Hernandez, 2008, Influence of microstructure and weld size on the mechanical behaviour of dissimilar AHSS resistance spot welds, Sci Technol Weld Join, 13, 769, 10.1179/136217108X325470
Khan, 2008, Effects of weld microstructure on static and impact performance of resistance spot welded joints in advanced high strength steels, Sci Technol Weld Join, 13, 49, 10.1179/174329308X271733
Marya, 2006, Tensile–shear forces and fracture modes in single and multiple weld specimens in dual-phase steels, J Manuf Sci Engng, 128, 287, 10.1115/1.2137751
Marya, 2005, Development of requirements for resistance spot welding dual-phase (DP600) steels. Part 1 – the causes of interfacial fracture, Weld J, 84-s, 172
Milititsky, 2003, On characteristics of DP600 resistance spot welds, Soc Automot Engng, 01, 244
Tao, 2008, Joint strength and failure mechanism of laser spot weld of mild steel sheets under lap shear loading, Sci Technol Weld Join, 13, 754, 10.1179/136217108X338917
Ferrasse, 1998, Resistance spot weldability of high strength steels for use in car industry, Weld World, 41, 177
Peterson W, Accorsi I, Coon T. Review of weld mechanical property specification requirements in AWS D8.1 (proposed). In: AWS detroit section (Ed.), Sheet metal welding conference XII, Livonia, MI, 2006.
Yamazaki, 2000, Static and fatigue strength of spot welded joints in ultra-high- strength, cold rolled steel sheets, Weld Int, 14, 533, 10.1080/09507110009549225
Kabasawa, 1996, Estimation of tensile shear strength of spot welded joint of steel sheets, Yosetsu Gakkai Ronbunshu, 14, 754
Bhadeshia, 1995, Impact toughness of C–Mn steel arc welds – Bayesian neural network analysis, Mater Sci Technol, 11, 1046, 10.1179/mst.1995.11.10.1046
Chao, 2003, Failure mode of spot welds: interfacial versus pullout, Sci Technol Weld Join, 8, 133
Sakuma, 2003, Factors to determine static strengths of spot weld for high strength steel sheets and developments of high strength steel sheets with strong and stable welding characteristics, Nippon Steel Tech Rep, 88, 33
Kuo, 2004, Weldability study of resistance spot welds and minimum weld button size methodology development for DP steel, Int J Mater Manuf, 113, 67
Satonaka, 2004, Prediction of tensile–shear strength of spot welds based on fracture modes, Weld World, 48, 39, 10.1007/BF03266430
Lin, 2002, Failure loads of spot welds under combined opening and shear static loading conditions, Int J Solids Struct, 39, 19, 10.1016/S0020-7683(01)00187-1
Lin, 2003, A general failure criterion for spot welds under combined loading conditions, Int J Solids Struct, 40, 5539, 10.1016/S0020-7683(03)00341-X
Rokhlin, 1984, Ultrasonic method for shear strength prediction of spot welds, J Appl Phys, 56, 726, 10.1063/1.334000
Sevim, 2006, Effect of hardness to fracture toughness for spot welded steel sheets, Mater Des, 27, 21, 10.1016/j.matdes.2004.09.008
Lee, 2005, Overload analysis and fatigue life prediction of spot-welded specimens using an effective J-integral, Mech Mater, 37, 19, 10.1016/j.mechmat.2003.12.006
Kong, 2008, Numerical study of strengths of spot-welded joints of steel, Mater Des, 29, 1554, 10.1016/j.matdes.2007.12.001
Yang, 2008, Integrated computational model to predict mechanical behaviour of spot weld, Sci Technol Weld Join, 13, 232, 10.1179/174329308X283901
Nielsen, 2008, 3D modelling of plug failure in resistance spot welded shear-lab specimens (DP600-steel), Int J Fract, 153, 125, 10.1007/s10704-008-9305-4
Markiewicz, 2003, Exprimentation et simulation numrique locale/globale de la tenue mcanique des assemblages souds par points, Mécanique Industries, 4, 17, 10.1016/S1296-2139(02)00004-0
E. Lamouroux, Modélisation détaillée des soudures par point et Laser pour simuler la rupture des assemblages automobiles, Ph.D. thesis, Univ. Valenciennes Et Du Hainaut-Cambrésis, Valenciennes, 2007.
Wang J, Xia Y, Zhou Q, et al. Simulation of spot weld pullout by modeling failure around nugget. In: SAE (Ed.), SAE 2006 world congress and exhibition, Detroit, MI.
Niordson, 2001, Analysis of steady-state ductile crack growth along a laser weld, Int J Fract, 111, 53, 10.1023/A:1010951331590
Cavalli, 2005, Cohesive-zone modelling of the deformation and fracture of spot-welded joints, Fatigue Fract Engng Mech, 28, 861, 10.1111/j.1460-2695.2005.00919.x
Zhou, 2005, Determining mode-I cohesive parameters for nugget fracture in ultrasonic spot welds, Int J Fracture, 136, 309, 10.1007/s10704-005-6036-7
Zhou, 2006, Predicting the failure of ultrasonic spot welds by pull-out from sheet metal, Int J Solids Struct, 43, 7482, 10.1016/j.ijsolstr.2006.03.009
Needleman, 1999, A micromechanical analysis of the ductile–brittle transition at a weld, Engng Fract Mech, 62, 317, 10.1016/S0094-114X(98)00094-9
Dancette, 2011, HAZ microstructures and local mechanical properties of high strength steels resistance spot welds, ISIJ Int, 51, 99, 10.2355/isijinternational.51.99
Babout, 2001, Characterization by X-ray computed tomography of decohesion, porosity growth and coalescence in model metal matrix composites, Acta Mater, 49, 2055, 10.1016/S1359-6454(01)00104-5
Maire, 2008, Initiation and growth of damage in a dual-phase steel observed by X-ray microtomography, Acta Mater, 56, 4954, 10.1016/j.actamat.2008.06.015
Sorpas version 9.0 – user manual, SWANTEC Software and Engineering ApS, edition; 2008.
Dancette, 2010, Investigations on the mechanical behavior of advanced high strength steels resistance spot welds in cross tension and tensile shear, Adv Mater Res, 89–91, 130, 10.4028/www.scientific.net/AMR.89-91.130
Bouzekri, 2010, An investigation of failure types in high strength steel resistance spot welds, Weld World, 54, 3, 10.1007/BF03263485
AWS D8.1, Specification for automotive weld quality – resistance spot welding of steel. American Welding Society; 2007.
Dancette, 2011, A finite element model for the prediction of advanced high strength steels spot welds fracture, submitted for publication to Engng Fract Mech, 10.1016/j.engfracmech.2011.04.013
Lemoine, 2007, Behavior laws and their influences on numerical prediction, 269
Abaqus users manual version 6.7, Hibbit, Karlsson and Sorensen, edition; 2007.