Experimental Study of High Temperature Fracture Behavior of A286 Superalloy at 650°C

M. Hagh Panahi1, H. Pirali1
1Mechanical Engineering Department, Iran University of Science and Technology, Tehran, Iran

Tóm tắt

In this paper an experimental work is done for investigation of high temperature fracture properties of A286 superalloy at 650°C. Stress intensity factor K and parameter C* for this superalloy are determined experimentally. For estimation of these parameters, an instrument is developed for investigation of high temperature fracture properties. For estimation of stress intensity factor, compliance method is used. For this purpose four different compact tension specimens are tested and the parameter K is estimated. Creep tests are done for the selected specimens and parameter C* is determined by semiempirical relationships at 650°C. In these tests it is concluded that the specimens are placed near the plane stress condition. Crack growth behavior of this alloy is also studied. High incubation time (600 h) leads to overaging and therefore this alloy after this time showed very ductile creep properties, and fast creep crack growth was the major result of this overaging phenomenon. Finally the obtained results are compared with well-known nonexperimental methods for determination of these parameters. The obtained results showed that the results are in good agreement with each other.

Từ khóa


Tài liệu tham khảo

De Cicco, H., Luppo, M.I., and Gribaudo, L.M., and Ovejero-Garcia, J., Microstructural Development and Creep Behavior in A286 Superalloy, Mater. Character., 2004, vol. 52, pp. 85–92. De Cicco, H., Luppo, M.I., Raffaeli, H., Di Gaetano, J., Gribaudo, L.M., and Ovejero-Garcia, J., Creep Behavior of an A286 Type Stainless Steel, Mater. Character., 2005, vol. 55, pp. 97–105. Landes, J.D. and Begley, J.A., A Fracture Mechanics Approach to Creep Crack Growth, Mechanics of Crack Growth, ASTM STP 590, American Society for Testing and Materials, 1976, pp. 128–148. Nicholson, R.D. and Formby, C.L., The Validity of Various Fracture Mechanics Methods at Creep Temperatures, Int. J. Fract., 1975, vol. 11(4), pp. 595–604. Floreen, S., Mechanical Properties, Superalloys II. Chap. 9, Sims, C.T., Stoloff, N.S., and Hagel, W.C., Eds., New York: Wiley, 1987. Radhakrishnan, V.M. and Kamaraj, M., Effect of Temperature on Crack Growth in Type 304 Stainless Steel, Mater. Sci. Eng., 1987, vol. 96, pp. 89–98. Geng, M.-F., Di, S.-Z., and Zhang, X.-A., J. Mater. Eng., 1998, vol. 4, pp. 18–20. Geng, M.-F., An Idea for Predicting Crack Growth Time to Fracture under Creep-Fatigue Conditions, Mater. Sci. Eng. A, 1998, vol. 257, pp. 250–255. Seifollahi, M., Razavi, S.H., Kheirandish, Sh., and Abbasi, S.M., The Mechanism of n Phase Precipitation in A286 Superalloy during Heat Treatment, J. Mater. Eng. Perform., 2013, vol. 22, no. 10, pp. 3063–3069. Martin, O., De Tiedra, P., and San-Juan, M., Study of Influence ofY and n Phases on Corrosion Behaviour of A286 Superalloy by Using Electrochemical Potentiokinetic Techniques, Mater. Design., 2015, vol. 87, pp. 266–271. De Tiedra, P., Martin, O., and San-Juan, M., Potentiodynamic Study of the Influence of Y and n Phases on Pitting Corrosion of A286 Superalloy, J. Alloy. Compound., 2016, vol. 673, pp. 231–236. Standard Test Methodfor Measurement of Creep Crack Growth Rates in Metals, ASTM E1457, 2011. Saxena, A., Nonlinear Fracture Mechanics for Engineers, New York: CRC Press LLC, 1998. Tada, H., Paris, P.C., and Irwin, G.R., The Stress Analysis of Cracks Handbook, Hellrtown, PA: Del Research, 1975. https://www.atimetals.com/Products/Documents/datasheets/nickel-cobalt/nickel-based/ati_286_ludlum_version_tds_en_v1.pdf#search= 286 (access date: 12.02. 2018). Kumar, V., German, M.D., and Shih, M.D., An Engineering Approach for Elastic-Plastic Fracture Analysis. NP-1931, Palo Alto, CA, USA: Electric Power Research Institute, 1981.