Electrophoretic Deposition of Hydroxyapatite Coatings on Metal Substrates: A Nanoparticulate Dual-Coating Approach
Tóm tắt
Hydroxyapatite coatings can be readily deposited on metal substrates by electrophoretic deposition. However, subsequent sintering is highly problematic owing to the fact that temperatures in excess of 1100°C are required for commercial hydroxyapatite powders to achieve high density. Such temperatures damage the metal and induce metal-catalysed decomposition of the hydroxyapatite. Furthermore, the firing shrinkage of the hydroxyapatite coating on a constraining metal substrate leads to severe cracking. The present study has overcome these problems using a novel approach: the use of aged nanoparticulate hydroxyapatite sols (lower sintering temperature) and a dual coating strategy that overcomes the cracking problem. Dual layers of uncalcined hydroxyapatite (HAp) powder were electrophoretically coated on Ti, Ti6Al4V and 316L stainless steel metal substrates, sintered at 875–1000°C, and characterised by SEM and XRD, and interfacial shear strength measurement. Dual coatings on stainless steel had an average high bond strength (about 23 MPa), and dual coatings on titanium and titanium alloy had moderate strengths (about 14 and 11 MPa, respectively), in comparison with the measured shear strength of bone (35 MPa). SEM and XRD demonstrated that the second layer blended seamlessly with the first and filled the cracks in the first. The superior result on stainless steel is attributed to a more appropriate thermal expansion match with hydroxyapatite, the thinner oxide layer, or a combination of these factors.
Tài liệu tham khảo
E.C. Shors and R.E. Holmes, in An Introduction to Bioceramics, edited by L.L. Hench and J. Wilson (World Scientific, Singapore, 1993), p. 181.
D.R. Carter and D.M. Spengler, Clinical Orthopaedics and Related Research (135), 192 (1978).
J.B. Park and R.S. Lakes, Biomaterials: An Introduction (Plenum Press, New York, 1992), p. 193.
A.J. Ruys, M. Wei, A.A. Brandwood, B.K. Milthorpe, and C.C. Sorrell, in Ceramics: Adding the Value, Proceedings of the International Ceramic Conference, Vol. 1, edited by M.J. Bannister (CSIRO Publication, Melbourne, 1992), p. 586.
J.D. Santos, S. Morrey, G.W. Hastings, and F.J. Monteiro, in Bioceramics, Vol. 4: Proceedings of the 4th International Symposium on Ceramics in Medicine, edited by W. Bonfield, G.W. Hastings, and K.E. Tanner (Butterworth Heinemann, London, 1991), p. 71.
M.J. Filaggi, N.A. Coombs, and R.M. Pilliar, Journal of Biomedical Materials Research 25, 1211 (1991).
D.S. Patil, K.P. Sreekumar, N. Venkataramani, R.K. Iyer, R. Prasad, R.S. Koppilar, and K.R. Munim, Proceedings of the International Ceramics Conference, Austcerm 94. Bulletin of Materials Science 19, 115 (1996), Australian Ceramic Society.
L.M. Boulton, P.J. Gregson, M. Tuke, and T. Baldwin, Materials Letters 12, 1 (1991).
W.R. Lacefield, Annals of the New York Academy of Science 523, 73 (1988).
T. Kokubo, Acta Materials 46, 2519 (1998).
T. Yano, K. Budiyanto, K. Yoshida, and T. Iseki, Fusion Engineering and Design 41, 157 (1998).
P. Ducheyne, S. Radin, M. Heughebaert, and J.C. Heughebaert, Biomaterials 11, 244 (1990).
S.J. Yankee, B.J. Pletka, H.A. Luckey, and W.A. Johnson, in Thermal Spray Research and Application, Proceedings of the Third National Thermal Spray Conference (Long Beach, CA, 1990), p. 433.
R.T. Bothe, K.E. Beaton, and H.A. Davenport, Surgery, Gynecology & Obstetrics 71, 598 (1940).
H.M. Kim, F. Miyaji, T. Kokubo, and T. Nakamura, Journal of Ceramic Society Japan 105, 111 (1997).
S.N. Heavens, in Advanced Ceramic Processing and Technology, Vol. 1, edited by J.G.P. Binner (Noyes Publications, Park Ridge, 1990), p. 255.
M. Wei, A.J. Ruys, A. Brandwood, B.K. Milthorpe, and C.C. Sorrell, in International Ceramic Monograph 1, 701 (1994).
J.B. Birks, in Progress in Dielectrics, Vol. 1, edited by J.B. Birks and J.H. Schulman (Heywood & Company Ltd., London, 1959), p. 31.
A.J. Ruys, M. Wei, A. Brandwood, B.K. Milthorpe, and C.C. Sorrell, Journal of Materials Science Letters 14, 744 (1995).
M. Asada, K. Oukami, S. Nakamura, and K. Takahashi, Journal of the Ceramic Society of Japan 95, 703 (1987).
P. Ducheyne, W.V. Raemdonch, J.C. Heughebaert, and M. Heughebaert, Biomaterials 7, 97 (1986).
J. Weng, X. Liu, X. Zhang, and K. de Groot, Journal of Biomedical Materials Research 30, 5 (1996).
M. Wei, A.J. Ruys, M.V. Swain, S.H. Kim, B.K. Milthorpe, and C.C. Sorrell, Journal of Materials Science, Materials in Medicine 10, 401 (1999).
M. Jarcho and C.H. Bolen, Journal of Materials Science 11, 2027 (1976).
M. Wei, A.J. Ruys, B.K. Milthorpe, and C.C. Sorrell, Journal of Biomedical Materials Research 45, 11 (1999).
M. Wei, Electrophoresis of Hydroxyapatite on Metal Substrates, Ph.D. Thesis, University of New South Wales, Sydney, Australia, 1998.
ASTM F 1044-87, 1993.
A.J. Ruys, A. Brandwood, B.K. Milthorpe, M.R. Dickson, K.A. Zeigler, and C.C. Sorrell, J. Mat. Sci. Med. 6, 297 (1995).
A.J. Ruys, N. Ehsani, B.K. Milthorpe, and C.C. Sorrell, J. Aust. Ceram. Soc. 29, 65 (1993).