Electrochemical performance of SnO–V2O5–SiO2 glass anode for Na-ion batteries
Tóm tắt
SnO–V2O5–SiO2 glass anode sample prepared by simple a mechanical milling technique. The amorphous nature of sample identified using with XRD technique. This glass anode has an initial charge capacity of 560 mAhg−1 and discharge capacity of 483 mAhg−1. After 20 charge–discharge cycles, charge and discharge capacities achieved to be 389 and 379 mAhg−1 at 0.1C, respectively. The loss in discharge capacity is up to ~ 45.22% even at high rate 5C.
Tài liệu tham khảo
Bruce, P.G., Scrosati, B., Tarascon, J.M.: Nanomaterials for rechargeable lithium batteries. Angew. Chem. Int. Ed. 47(16), 2930–2946 (2008)
Idota, Y., Kubota, T., Matsufuji, A., Maekawa, Y., Miyasaka, T.: Tin-based amorphous oxide: a high-capacity lithium-ion-storage material. Science 276(5317), 1395–1397 (1997)
Goodenough, J.B., Kim, Y.: Challenges for rechargeable Li batteries. Chem. Mater. 22(3), 587–603 (2009)
Sawicki, M., Shaw, L.L.: Advances and challenges of sodium ion batteries as post lithium ion batteries. RSC Advances 5(65), 53129–53154 (2015)
Massé, R.C., Liu, C., Li, Y., Mai, L., Cao, G.: Energy storage through intercalation reactions: electrodes for rechargeable batteries. Nat. Sci. Rev. 4(1), 26–53 (2017)
Kim, S.W., Seo, D.H., Ma, X., Ceder, G., Kang, K.: Electrode materials for rechargeable Sodium-Ion batteries: potential alternatives to current Lithium-Ion batteries. Adv. Energy Mater 2, 710–721 (2012)
Morinaga, K., Fujino, S.: Preparation and properties of SnO–SnCl2–P2O5 glass. J. Non Cryst. Solids 282(1), 118–124 (2001)
Hwang, J.Y., Myung, S.T., Sun, Y.K.: Sodium-ion batteries: present and future. Chem. Soc. Rev. 46(12), 3529–3614 (2017)
Lu, Y.C., Ma, C., Alvarado, J., Kidera, T., Dimov, N., Meng, Y.S., Okada, S.: Electrochemical properties of tin oxide anodes for sodium-ion batteries. J. Power Sour. 284, 287–295 (2015)
Kim, Y., Ha, K.H., Oh, S.M., Lee, K.T.: High-capacity anode materials for Sodium-Ion Batteries. Chem. Eur. J. 20(38), 11980–11992 (2014)
Kang, H., Liu, Y., Cao, K., Zhao, Y., Jiao, L., Wang, Y., Yuan, H.: Update on anode materials for Na-ion batteries. J. Mater. Chem. A 3(35), 17899–17913 (2015)
Yamauchi, H., Park, G., Nagakane, T., Honma, T., Komatsu, T., Sakai, T., Sakamoto, A.: Performance of lithium-ion battery with tin-phosphate glass anode and its characteristics. J. Electrochem. Soc. 160(10), A1725–A1730 (2013)
Hayashi, A., Konishi, T., Tadanaga, K., Minami, T., Tatsumisago, M.: All-solid-state rechargeable lithium batteries using SnX–P2X5 (X = S and O) amorphous negative electrodes. Res. Chem. Intermed. 32(5), 497–506 (2006)
Sakurai, Y., Yamaki, J.I.: Correlation between microstructure and electrochemical behavior of amorphous V2O5–P2O5 in Lithium cells. J. Electrochem. Soc. 135(4), 791–796 (1988)
Sakurai, Y., Okada, S., Yamaki, J., Okada, T.: Electrochemical behaviour of amorphous V2O5–(P2O5) cathodes for lithium secondary batteries. J. Power Sour. 20(3–4), 173–177 (1987)
Leech, A.C., Owen, J.R., Steele, B.C.H.: Lithium insertion into a vanadium boron oxide glass. Solid State Ionics 9–10(1), 645–648 (1983)
Levy, M., Rousseau, F., Duclot, M.: Electrochemical properties of glasses in the TeO2−V2O5 system. Solid State Ionics 28, 736–738 (1988)
Ravuri, B.R., Suman, G., Srinivasa Rao, C.: Zn–Ge–Sb glass composite mixed with Ba2+ ions: a high capacity anode material for Na-ion batteries. Appl. Nanosci. (2018). https://doi.org/10.1007/s13204-018-0822-9
Honma, T., Togashi, T., Kondo, H., Komatsu, T., Yamauchi, H., Sakamoto, A., Sakai, T.: Tin-phosphate glass anode for sodium ion batteries. Apl Materials 1(5), 052101 (2013)