Effect of processing parameters on the microstructure and mechanical behavior of silica-calcium phosphate nanocomposite
Tóm tắt
Silica-calcium phosphate nanocomposite (SCPC) is a bioactive ceramic characterized by superior bone regenerative capacity and resorbability when compared to traditional bioactive ceramics. The aim of the present study is to evaluate the effect of processing parameters on the microstructure and mechanical properties of SCPC. Cylinders were prepared by pressing the ceramic powder at 200, 300 or 400 MPa and sintering at 900, 1000 or 1100°C for 3 h, respectively. XRD results indicate that the crystalline structure of the material is made of β-NaCaPO4 and α-cristobalite solid solutions. The increase in sintering temperature results in an increase in the grain size and the formation of a melting phase that coats the grains. TEM analyses reveal that the melting phase is amorphous and rich in silicon. The mechanical properties of SCPC cylinders are dependent on the content of the melting phase and the microstructure of the material. The ranges of compressive strength and modulus of elasticity of the SCPC are 62–204 MPa and 6–14 GPa, respectively, which are comparable to those of cortical bone. The results suggest that the interaction between crystalline and amorphous phases modulated the mechanical behavior of SCPC. It is possible to engineer the mechanical properties of SCPC by controlling the processing parameters to synthesize various fixation devices for orthopedic and cranio-maxillofacial applications.
Tài liệu tham khảo
Alliot-Licht B, Delange GL, Gregoire M. Effects of hydroxyapatite particles on periodontal ligament fibroblast-like cell behavior. J Periodontol. 1997;68:158–65.
Den Hollander W, Patka P, Klein CP, Heidendal GA. Macroporous calcium phosphate ceramics for bone substitution: a trace study on biodegradation with 45Ca trace. Biomaterials. 1991;12:569–73.
Gan Y, Dai KR, Zhang P, Tang T, Zhu Z, Lu J. The clinical use of enriched bone marrow stem cells combined with porous beta-tricalcium phosphate in posterior spinal fusion. Biomaterials. 2008;29:3973–82.
Clavel-Sainz, Lopez-Prats F, Meseguer-Ortiz CL. In vitro behavior of adult mesenchyamal stem cells seeded on a bioactive glass ceramic in the SiO2–CaO–P2O5 system. Acta Biomaterialia. 2008;4:1104–13.
Ohtsuki C, Kokubo T, Takatsuka K. Compositional dependence of bioactivity of glasses in the system CaO–SiO2–P2O5: its in vitro evaluation. J Ceram Soc Jpn. 1991;99:1–6.
Sugawara A, Fujikawa K, Takagi S, Chow LC, Nishiyama M, Murai S. Histopathological and cell enzyme studies of calcium phosphate cements. Dent Mater J. 2004;23:613–20.
Costantino PD, Frendman CD. Synthetic bone graft substitutes. Otolaryngol Clin North Am. 1994;27:1037–74.
Suchanec W, Yoshimura M. Processing and properties of hydroxyapatite-based biomaterials for use as hard tissue replacement implants. J Mater Res. 1998;13:94–117.
Bagambisa FB, Joos U, Schilli W. Mechanisms and structure of the bond between bone and hydroxyapatite ceramics. J Biomed Mater Res. 1993;27:1047–55.
Eggli PS, Muller W, Schenk RK. Porous hydroxyapatite and tri-calcium phosphate cylinders with two different pore size ranges implanted in the cancellous bone of rabbits. Clin Orthop. 1988;232:127–37.
Kim HM, Miyaji F, Kokubo T. Bioactivity of Na2O–CaO–SiO2 glasses. J Am Ceram Soc. 1995;78:2405–11.
Ambard AJ, Mueninghoff L. Calcium phosphate cement: review of mechanical and biological properties. J Prosthodont. 2006;15:321–8.
EI-Ghannam AR. Advanced bioceramic composite for bone tissue engineering design principles and structure–bioactivity relationship. J Biomed Mater Res. 2004;69A:490–501.
Gupta G, Kirakodu S, EI-Ghannam AR. Dissolution kinetics of a Si-rich nanocomposite and its effect on osteoblast gene expression. J Biomed Mater Res. 2007;80A:486–96.
Kokubo T, Kim HM, Kawashita M. Novel bioactive materials with different mechanical properties. Biomaterials. 2003;24:2161–75.
Gupta G, EI-Ghannam A, Kirakodu S, Khraisheh M, Zbib H. Enhancement of osteoblast gene expression by mechanically compatible porous Si-rich nanocomposite. J Biomed Mater Res. 2007;81B:387–96.
EI-Ghannam A, Ning CQ. Effect of bioactive ceramic dissolution on the mechanism of bone mineralization and guided tissue growth in vitro. J Biomed Mater Res. 2006;76A:386–97.
Altamirano-Juárez DC, Carrera-Figueiras C, Garnica-Romo MG, Mendoza-López ML, Ortuño-López MB, et al. Effects of metals on the structure of heat-treated sol–gel SiO2 glasses. J Phys Chem Solids. 2001;62:1911–7.
de G, Tapfer L, Catalano M, Battaglin G, Caccavale F, Gonella F, et al. Formation of copper and silver nanometer dimension clusters in silica by the sol–gel process. Appl Phys Lett. 1996;68:3820–2.
Brückner R. Properties and structure of vitreous silica. J Non-Cryst Solids. 1970;5:123–75.
Ma L. Comparison of different sample preparation techniques in TEM observation of microstructure of INCONEL alloy 783 subjected to prolonged isothermal exposure. Micron. 2004;35:273–9.
Beia H, Shim S, Miller MK, Pharr GM, George EP. Effects of focused ion beam milling on the nanomechanical behavior of a molybdenum-alloy single crystal. Appl Phys Lett. 2007;91:111915.
Holzer L, Muench B, Wegmann M, Gasser P, Flatt RJ. FIB nanotomography of particulate systems-part I: particle shape and topology of interfaces. J Am Ceram Soc. 2006;89(8):2577–85.
Wilson JR, Kobsiriphat W, Mendoza R, Chen H-Y, Hiller JM, Miller DJ, et al. Three-dimensional reconstruction of a solid oxide fuel cell anode. Nat Mater. 2006;5(7):541–4.
Wu HZ, Roberts SG, Mobus G, Inkson BJ. Subsurface damage analysis by TEM and 3D FIB crack mapping in alumina and alumina/5 vol.% SiC nanocomposite. Acta Mater. 2003;51(1):149–63.
Yamahara K, Okazaki K, Kawamura K. Molecular dynamics study of the thermal behaviour of silica glass/melt and cristobalite. J Non-Cryst Solids. 2001;291:32–42.
de Groot K. Bioceramics consisting of calcium phosphate salts. Biomaterials. 1980;1:47–50.
Du C, Cui FZ, Zhu XD, de Groot K. Three-dimensional nano-HAP/collagen matrix loading osteogenic cells in organ culture. J Biomed Mater Res. 1999;44:407–15.
Bandyopadhyay A, Bernard S, Xue W, Bose S. Calcium phosphate based resorbable ceramics: influence of MgO, ZnO, SiO2 dopants. J Am Ceram Soc. 2006;89:2675–88.
Kannan S, Lemos A, Rocha JHG, Ferreira JMF. Characterization and mechanical performance of the Mg-stabilized β-Ca3(PO4)2 prepared from Mg-substituted Ca-deficient apatite. J Am Ceram Soc. 2006;89:2757–61.
Dantas ACS, Greil P, Müller FA. Effect of CO3 2− incorporation on the mechanical properties of wet chemically synthesized β-tricalcium phosphate (TCP) ceramics. J Am Ceram Soc. 2008;91:1030–3.
Rodriguez-Lorenzo LM, Vallet-Regi M, Ferreira JMF. Fabrication of hydroxyapatite bodies by uniaxial pressing from a precipitated powder. Biomaterials. 2001;22:583–8.
Wiltfang J, Merten HA, Shlegel KA, Kloss FR, Rupprecht S, Lessler P. Degradation characterization of α and β tri-calcium-phosphate (TCP) in minipigs. J Biomed Mater Res. 2002;63:115–21.
Kalita SJ, Bhardwaj A, Bhatt HA. Nanocrystalline calcium phosphate ceramics in biomedical engineering. Mater Sci Eng C. 2007;27:441–9.
Lu J, Descaps M, Dejou J, Koubi G, Hardouin P, Lemaitre J, et al. The biodegradation mechanism of calcium phosphate biomaterials in bone. J Biomed Mater Res. 2002;63B:408–12.
EI-Ghannam A, Ning CQ, Mehta J. Cyclosilicate nanocomposite: a novel resorbable bioactive tissue engineering scaffold for BMP and bone-marrow cell delivery. J Biomed Mater Res. 2004;71A:377–90.