Effect of mould baffle technology on stray grain formation in single crystal blades by integral fabrication based on 3D printing
Tóm tắt
Stray grains, the most serious casting defect, mainly occur in the platform because of the abrupt transition of the cross-section in the directional solidification of superalloy single-crystal blades. A new mould baffle technology based on 3D printing and gelcasting is proposed herein to reduce the formation of stray grains in the platform. The influence of the proposed mould baffle technology on the temperature field in the platform during solidification was investigated by simulation and experiment. The numerical simulation results indicate that the proposed mould baffle technology can effectively hinder the radiation and heat dissipation at the platform extremities, and therefore, reduce undercooling in the platform and the formation of stray grains during directional solidification. Casting trials of a hollow turbine blade were conducted using CMSX-4 superalloy. The trial results demonstrate the potential of the proposed approach for manufacturing single-crystal superalloy blades.
Tài liệu tham khảo
Reed R C. The superalloy fundamental and applications. Cambridge: Cambridge University Press, 2006: 1–10.
Pollock T M, Tim S. Nickel-based superalloy for advanced turbine engines: Chemistry, microstructure, and properties. Journal of Propulsion and Power, 2006, 22(2): 358–361.
Sims C T, Stoloff N S, Hagel W C. Superalloys II: High-temperature materials for aerospace and industrial power. New York: John Wiley and Sons, 1987: 1–23.
Ma D and Bührig-Polaczek A. Avoiding grain defects in single crystal components by application of a heat conductor technique. International Journal of Materials Research, 2009, 100(8): 1145–1151.
Ma D and Bührig-Polaczek A. Development of heat-conductor technique for single crystal components of superalloys. International Journal of Cast Metals Research, 2013, 22: 422–429.
Ma D and Bührig-Polaczek A. Application of a heat conductor technique in the production of single crystal turbine blades. Metallurgical and Materials Transaction B, 2009, 40: 738–748.
Meyer T V M, Dedecke D, Paul U, et al. Undercooling related casting defects in single crystal turbine blades. Superalloys, 1996: 471–479.
Yang X L, Ness D, Lee P D, et al. Simulation of stray grain formation during single crystal seed melt-back and initial withdrawal in the Ni-base superalloy CMSX4. Materials Science & Engineering: A, 2005, 413–414: 571–577.
Backman D G and Williams J C. Advanced materials for aircraft engine applications. Science, 1992, 255(5048): 1082–1087.
Lu Z L, Zhao L, Li Y N, et al. Thermal behavior of integral Al2O3-based ceramic molds for fabricating gas turbine blades. Journal of Engineering Manufacture, 2014, 228(5): 695–703.
Wu H, Li D R, Tang Y, et al. Rapid casting of hollow turbine blades using integral ceramic moulds. Journal of Engineering Manufacture, 2009, 223(6): 695–702.
Tian G Q, Lu Z L, Miao K, et al. Formation mechanism of cracks during the freeze drying of gelcast ceramic parts. Journal of American Ceramic Society, 2015, 98(10): 3338–3345.
Wu H H, Li D C, Tang Y, et al. Rapid fabrication of alumina-based ceramic cores for gas turbine blades by stereolithography and gelcasting. Journal of Materials Processing Technology, 2009, 209(18–19): 5886–5891.
Cai K, Guo D, Huang Y, et al. Solid freeform fabrication of alumina ceramic parts through a lost mould method. Journal of European Ceramic Society, 2003, 23(6): 921–925.
Young A C, Omatete O O, Janney M A, et al. Gelcasting of Alumina. Journal of American Ceramic Society, 1991, 74(3): 612–618.
Neuer G. Spectral and total emissivity measurements of highly emitting materials. International Journal of Thermophysics, 1995, 16(1): 257–265.
Carter P, Cox D C, Gandin C A, et al. Process modelling of grain selection during the solidification of single crystal superalloy castings. Materials Science & Engineering: A, 2000, 280(2): 233–246.
Chapman L A. Application of high temperature DSC technique to nickel based superalloys. Journal of Materials Science, 2004, 39(24): 7229–7236.
Ma D, Wu Q, and Bührig-Polaczek A. Undercoolability of superalloy and solidification defects in single crystal components. Advanced Materials Research, 2011, 278: 417–422.
Ma D, Wang F, Wu Q, et al. Temperature evolution and grain defect formation during single crystal solidification of a blade cluster. China Foundry, 2017, 14(5): 456–460.
Szeliga D, Kubiak K, Sieniawski J. Control of liquidus isotherm shape during solidification of Ni-based superalloy of single crystal platforms. Journal of Materials Processing Technology, 2016, 234(1): 18–26.