Effect of hydrofluoric acid etching duration on the roughness and flexural strength of a lithium disilicate-based glass ceramic

Brazilian Dental Journal - Tập 22 Số 1 - Trang 45-50 - 2011
Lucas Villaça Zogheib1, Álvaro Della Bona2, Estevão Tomomitsu Kimpara3, J.F. McCabe4
1Department of Restorative Dentistry, Dental School, University of Passo Fundo, RS, Brazil.
2University of Passo Fundo, Passo Fundo, Brazil
3Univ. Estadual Paulista, Brazil
4Newcastle University

Tóm tắt

The aim of this study was to examine the effect of different acid etching times on the surface roughness and flexural strength of a lithium disilicate-based glass ceramic. Ceramic bar-shaped specimens (16 mm x 2 mm x 2 mm) were produced from ceramic blocks. All specimens were polished and sonically cleaned in distilled water. Specimens were randomly divided into 5 groups (n=15). Group A (control) no treatment. Groups B-E were etched with 4.9% hydrofluoric acid (HF) for 4 different etching periods: 20 s, 60 s, 90 s and 180 s, respectively. Etched surfaces were observed under scanning electron microscopy. Surface profilometry was used to examine the roughness of the etched ceramic surfaces, and the specimens were loaded to failure using a 3-point bending test to determine the flexural strength. Data were analyzed using one-way ANOVA and Tukey's test (?=0.05). All etching periods produced significantly rougher surfaces than the control group (p<0.05). Roughness values increased with the increase of the etching time. The mean flexural strength values were (MPa): A=417 ± 55; B=367 ± 68; C=363 ± 84; D=329 ± 70; and E=314 ± 62. HF etching significantly reduced the mean flexural strength as the etching time increased (p=0.003). In conclusion, the findings of this study showed that the increase of HF etching time affected the surface roughness and the flexural strength of a lithium disilicate-based glass ceramic, confirming the study hypothesis.

Từ khóa


Tài liệu tham khảo

Hooshmand T, 2008, Effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics, J Prosthodont, 17, 415, 10.1111/j.1532-849X.2008.00319.x

Addison O, 2007, The impact of hydrofluoric acid surface treatments on the performance of a porcelain laminate restorative material, Dent Mater, 23, 461, 10.1016/j.dental.2006.03.002

Guler AU, 2006, Effect of acid etching time and a self-etching adhesive on the shear bond strength of composite resin to porcelain, J Adhes Dent, 8, 21

Klosa K, 2009, The effect of storage conditions, contamination modes and cleaning procedures on the resin bond strength to lithium disilicate ceramic, J Adhes Dent, 11, 127

Chen JH, 1998, Effect of etchant, etching period, and silane priming on bond strength to porcelain of composite resin, Oper Dent, 23, 250

Chen JH, 1998, Effect of different etching periods on the bond strength of a composite resin to a machinable porcelain, J Dent, 26, 53, 10.1016/S0300-5712(96)00078-4

Jardel V, 1999, Surface energy of etched ceramic, Int J Prosthodont, 12, 415

Wolf DM, 1993, Bond strength of composite to etched and sandblasted porcelain, Am J Dent, 6, 155

Magne P, 1999, Crack propensity of porcelain laminate veneers: a simulated operatory evaluation, J Prosthet Dent, 81, 327, 10.1016/S0022-3913(99)70277-5

Yen TW, 1993, Effect of acid etching on the flexural strength of a feldspathic porcelain and a castable glass ceramic, J Prosthet Dent, 70, 224, 10.1016/0022-3913(93)90056-T

Wiedhahn K, 2007, From blue to white: new high-strength material for Cerec-IPS e.max CAD LT, Int J Comput Dent, 10, 79

Della Bona A, 2009

Stewart GP, 2002, Shear bond strength of resin cements to both ceramic and dentin, J Prosthet Dent, 88, 277, 10.1067/mpr.2002.128034

Canay S, 2001, Effect of different acid treatments on a porcelain surface, J Oral Rehabil, 28, 95, 10.1046/j.1365-2842.2001.00626.x

Della Bona A, 2002, Effect of ceramic surface treatment on tensile bond strength to a resin cement, Int J Prosthodont, 15, 248

Della Bona A, 1995, Shear vs. tensile bond strength of resin composite bonded to ceramic, J Dent Res, 74, 1591, 10.1177/00220345950740091401

Addison O, 2004, The influence of cement lute, thermocycling and surface preparation on the strength of a porcelain laminate veneering material, Dent Mater, 20, 286, 10.1016/S0109-5641(03)00105-2

Della Bona A, 2002, Microstructure, composition, and etching topography of dental ceramics, Int J Prosthodont, 15, 159

Chaiyabutr Y, 2008, The effect of hydrofluoric acid surface treatment and bond strength of a zirconia veneering ceramic, J Prosthet Dent, 100, 194, 10.1016/S0022-3913(08)60178-X

Naves LZ, 2010, Surface/interface morphology and bond strength to glass ceramic etched for different periods, Oper Dent, 35, 420, 10.2341/09-152-L

Thông tin
Thông tin xuất bản

Brazilian Dental Journal

Tập 22 Số 1

45-50

Thông tin tác giả