Effect of heat treatments on In-Situ Al2O3/TiAl3 composites produced from squeeze casting of TiO2/A356 composites
Tóm tắt
In-situ Al2O3/TiAl3 intermetallic matrix composites were fabricated via squeeze casting of TiO2/A356 composites heated in the temperature range from 700 °C to 780 °C for 2 hours. The phase transformation in TiO2/A356 composites employing various heat-treatment temperatures (700 °C to 780 °C) was studied by means of differential thermal analysis (DTA), microhardness, scanning electron microscopy (SEM), electron probe microanalysis (EPMA), and X-ray diffraction (XRD). From DTA, two exothermic peaks from 600 °C to 750 °C were found in the TiO2/A356 composites. The XRD showed that Al2O3 and TiAl3 were the primary products after heat treatment of the TiO2/A356 composite. The fabrication of in-situ Al2O3/TiAl3 composites required 33 vol pct TiO2 in Al and heat treatment in the range from 750 °C to 780 °C. The hardness (HV) of the in-situ Al2O3/TiAl3 composites (1000 HV) was superior to that of nonreacted TiO2/A356 composites (200 HV). However, the bending strength decreased from 685 MPa for TiO2/A356 composites to 250 MPa for Al2O3/TiAl3 composites. It decreased rapidly because pores occurred during the formation of Al2O3 and TiAl3. The activation energy of the formation of Al2O3 and TiAl3 from TiO2 and A356 was determined to be about 286 kJ/mole.
Tài liệu tham khảo
citation_journal_title=Adv. Mater. Proc.; citation_author=Terence M.F. Ronald; citation_volume=135; citation_issue=5; citation_publication_date=1989; citation_pages=29-37; citation_id=CR1
citation_journal_title=JOM; citation_author=Y.W. Kim, D.M. Dimiduk; citation_volume=43; citation_issue=8; citation_publication_date=1991; citation_pages=40-47; citation_id=CR2
citation_journal_title=Iron Steel Inst. Jpn. Int.; citation_author=F.H. Froes, C. Suryanarayana, D. Eliezer; citation_volume=31; citation_issue=10; citation_publication_date=1991; citation_pages=1235-48; citation_id=CR3
citation_journal_title=J. Mater. Res.; citation_author=M.S. DiPietro, K.S. Kumar, J.D. Whittenberger; citation_volume=6; citation_issue=3; citation_publication_date=1991; citation_pages=530-38; citation_id=CR4
citation_journal_title=Mater. Sci. Engr.; citation_author=S. Mitao, S. Tsuyama, K. Minakawa; citation_volume=A143; citation_issue=1–2; citation_publication_date=1991; citation_pages=51-62; citation_doi=10.1016/0921-5093(91)90725-3; citation_id=CR5
citation_journal_title=Scripta Metall. Mater.; citation_author=D.G. Morris, M.A. Morris, S. Guenter, M. Leboeuf, G. Hollrigl; citation_volume=27; citation_issue=11; citation_publication_date=1992; citation_pages=1645-50; citation_doi=10.1016/0956-716X(92)90159-C; citation_id=CR6
citation_journal_title=Scripta Mater.; citation_author=A.O. Kunrath, T.R. Strohaecker, J.J. Moore; citation_volume=34; citation_issue=2; citation_publication_date=1996; citation_pages=183-88; citation_doi=10.1016/1359-6462(95)00448-3; citation_id=CR7
citation_journal_title=Scripta Mater.; citation_author=H.X. Peng, D.Z. Wang, L. Geng, C.K. Yao, J.F. Mao; citation_volume=37; citation_issue=2; citation_publication_date=1997; citation_pages=199-204; citation_doi=10.1016/S1359-6462(97)00073-0; citation_id=CR8
citation_journal_title=Intermetallics; citation_author=N.J. Welham; citation_volume=6; citation_issue=5; citation_publication_date=1998; citation_pages=363-68; citation_doi=10.1016/S0966-9795(97)00087-3; citation_id=CR9
citation_journal_title=J. Mater. Sci. Lett.; citation_author=H. Fukunaga, X. Wang, Y. Aramaki; citation_volume=10; citation_issue=1; citation_publication_date=1991; citation_pages=23-35; citation_doi=10.1007/BF00724421; citation_id=CR10
citation_journal_title=J. Jpn. Inst. Light Met.; citation_author=I. Tsuchitori, H. Fukunaga; citation_volume=43; citation_issue=1; citation_publication_date=1993; citation_pages=26-32; citation_id=CR11
citation_journal_title=J. Jpn. Inst. Met.; citation_author=I. Tsuchitori, N. Morinaga, H. Fukunaga; citation_volume=59; citation_issue=3; citation_publication_date=1995; citation_pages=331-38; citation_id=CR12
citation_journal_title=Metall. Mater. Trans. A; citation_author=K.C. Chen, C.G. Chao; citation_volume=26A; citation_publication_date=1995; citation_pages=1035-43; citation_id=CR13
ASM Handbook Committee: Metals Handbook, 9th ed., vol. 8, Mechanical Testing, ASM, Metals Park, OH, 1985, p. 136.
citation_journal_title=J. Mater. Sci. Lett.; citation_author=K. Suganuma, T. Fujita, K. Niihara, N. Suzuki; citation_volume=8; citation_issue=7; citation_publication_date=1989; citation_pages=808-10; citation_doi=10.1007/BF01730145; citation_id=CR15
citation_journal_title=J. Jpn. Inst. Met.; citation_author=I. Tsuchitori, H. Fukunaga; citation_volume=56; citation_issue=3; citation_publication_date=1992; citation_pages=333-41; citation_id=CR16
citation_journal_title=Scripta Metall. Mater.; citation_author=P.C. Maity, S.C. Panigrahi, P.N. Chakroborty; citation_volume=28; citation_issue=5; citation_publication_date=1993; citation_pages=549-52; citation_doi=10.1016/0956-716X(93)90194-W; citation_id=CR17
citation_journal_title=J. Mater. Sci. Lett.; citation_author=D.Z. Wang, Z.R. Liu, C.K. Yao, M. Yao; citation_volume=12; citation_issue=18; citation_publication_date=1993; citation_pages=1420-21; citation_doi=10.1007/BF00591594; citation_id=CR18
citation_title=Alloy Phase Diagrams; citation_publication_date=1993; citation_id=CR19; citation_author=Hugh Baker; citation_publisher=ASM INTERNATIONAL
citation_journal_title=J. Jpn. Inst. Met.; citation_author=H. Okabe; citation_volume=49; citation_issue=10; citation_publication_date=1985; citation_pages=891-98; citation_id=CR20
citation_journal_title=J. Jpn. Inst. Met.; citation_author=I. Tsuchitori, H. Fukunaga; citation_volume=58; citation_issue=9; citation_publication_date=1994; citation_pages=1029-35; citation_id=CR21
Ira N. Levine: Physical Chemistry, 4th ed, McGraw-Hill, 1995, pp. 516–21.
citation_title=The Theory of the Transformations in Metals and Alloys; citation_publication_date=1965; citation_id=CR23; citation_author=J. Christian; citation_publisher=Pergamon
citation_journal_title=J. Mater. Sci.; citation_author=J.H. Li, X.G. Ning, H.Q. Ye, J. Pan, H. Fukunaga; citation_volume=32; citation_issue=2; citation_publication_date=1997; citation_pages=543-47; citation_doi=10.1023/A:1018502811169; citation_id=CR24