Effect of air gap interval on polyvinylidene fluoride hollow fiber membrane spinning for CO2 and CH4 gas separation
Tóm tắt
Improper control of air gap interval during hollow fiber membranes (HFMs) spinning may lead to structural defects such as inner lumen deformations and macrovoids. In the current work, PVDF HFMs were prepared by manipulating air gap intervals at 5, 10, 15, 20, and 25 cm, using dry-wet spinning mechanism. The changes in its properties, including contact angle, mechanical strength, and most importantly the morphological structure that is usually crucial for gas separation performance have been determined. The morphology was evaluated using SEM, and the inner lumen defects of HFMs were reduced with the increment of air gap interval during the spinning process. Subsequently, the CO2 gas permeance was observed to increase from 5 to 15 cm air gap distance and almost constant at 20 cm air gap interval, then increase tremendously beyond this point. Furthermore, CO2/CH4 ideal selectivity was observed to be improved and reached the highest end at PVDF-AG15 and dropped beyond this point. Therefore, varying air gap distance is considered as a practical approach for better gas separation. However, macrovoids will form if the air gap length is overlong. Thus, optimum air gap length during PVDF HFMs spinning is vital for morphology and gas separation performance.
Tài liệu tham khảo
A. Awad and I. H. Aljundi, Korean J. Chem. Eng., 35, 1700 (2018).
M. Mubashir, Y. F. Yeong, T. L. Chew and K. K. Lau, Sep. Purif. Technol., 215, 32 (2019).
L. Ma, F. Svec, T. Tan and Y. Lv, ACS Appl. Nano Mater., 1, 2808 (2018).
L. Meng, X. Zou, S. Guo, H. Ma, Y. Zhao and G. Zhu, ACS Appl. Mater. Interfaces, 7, 15561 (2015).
M. Mubashir, Y. Y. Fong, C. T. Leng and L. K. Keong, Chem. Eng. Technol., 41, 235 (2018).
Z. Qiao, Q. Xu and J. Jiang, J. Membr. Sci., 551, 47 (2018).
A. Jamil, O. P. Ching, T. Iqbal, S. Rafiq, M. Zia-Ul-Haq, M. Z. Shahid, M. Mubashir, S. Manickam and P. L. Show, J. Hazard. Mater., 41, 126000 (2021).
S. Shahid, G. V. Baron, J. F. M. Denayer, J. A. Martens, L. H. Wee and I. F. J. Vankelecom, J. Membr. Sci., 620, 118943 (2021).
A. Shakoor, A. L. Khan, P. Akhter, M. Aslam, M. R. Bilad, I. M. Maafa, K. Moustakas, A. S. Nizami and M. Hussain,, Environ. Sci. Pollut. Res., 28, 12397 (2021).
X. Chen, Asian Philos, 27, 1 (2017).
L. Hu, J. Cheng, Y. Li, J. Liu, J. Zhou and K. Cen, J. Appl. Polym. Sci., 135, 45765 (2018).
H. Pang, H. Gong, M. Du, Q. Shen and Z. Chen, Sep. Purif. Technol., 191, 38 (2018).
Y. Tang, Y. Lin, H. Lin, C. Li, B. Zhou and X. Wang, Membranes (Basel), 10, 1 (2020).
W. Li, Prog. Mater. Sci., 100, 21 (2019).
N. Peng, N. Widjojo, P. Sukitpaneenit, M. M. Teoh, G. G. Lipscomb, T.-S. Chung and J.-Y. Lai, Prog. Polym. Sci., 37, 1401 (2012).
L. Shi, R. Wang, Y. Cao, C. Feng, D. T. Liang and J. H. Tay, J. Membr. Sci., 305, 215 (2007).
W. Li, P. Su, G. Zhang, C. Shen and Q. Meng, J. Membr. Sci., 495, 384 (2015).
S. Bonyadi, T. S. Chung and W. B. Krantz, J. Membr. Sci., 299, 200 (2007).
X. Zhang, Y. Wen, Y. Yang and L. Liu, J. Macromol. Sci. B, 47, 1039 (2008).
A. L. Ahmad and Z. M. H. Mohd Shafie, J. Phys. Sci., 28, 185 (2017).
M. Mubashir, Y. F. Yeong, K. K. Lau and T. L. Chew, Polym. Test., 73, 1 (2019).
S.-H. Pak, Y.-W. Jeon, M.-S. Shin and H. C. Koh, Environ. Eng. Sci., 33, 17 (2016).
S. S. Hosseini, N. Peng and T. S. Chung, J. Membr. Sci., 349, 156 (2010).
A. Huang and B. Feng, J. Membr. Sci., 548, 59 (2018).
Y.-w. You, C.-f. Xiao, Q.-l. Huang, Y. Huang, C. Wang and H.-l. Liu, RSC Adv., 8, 102 (2018).
H. Zhu, X. Jie, L. Wang, G. Kang, D. Liu and Y. Cao, RSC Adv., 6, 69124 (2016).
C. H. Loh and R. Wang, J. Membr. Sci., 466, 130 (2014).
M. Rahbari-Sisakht, A. F. Ismail, D. Rana and T. Matsuura, J. Membr. Sci., 415, 221 (2012).
Z. Wang and J. Ma, Desalination, 286, 69 (2012).
F. Korminouri, M. Rahbari-Sisakht, D. Rana, T. Matsuura and A. F. Ismail, Sep. Purif. Technol., 132, 601 (2014).
E. Anuar, S. M. Saufi and H. W. Yussof, Korean J. Chem. Eng., 36, 1124 (2019).
F. Korminouri, M. Rahbari-Sisakht, T. Matsuura and A. F. Ismail, Chem. Eng. J., 264, 453 (2015).
S. M. Rosid, H. Hasbullah, Y. Raharjo, A. F. Ismail, M. H. D. Othman, S. H. S. A. Kadir, F. Kamal, M. S. Abdullah and B. C. Ng, Mater. Today: Proc., 46, 1929 (2021).
Y.-H. Zhao, B.-K. Zhu, X.-T. Ma and Y.-Y. Xu, J. Membr. Sci., 290, 222 (2007).
F. L. Huang, Q. Q. Wang, Q. F. Wei, W. D. Gao, H. Y. Shou and S. D. Jiang, Express. Polym. Lett., 4, 551 (2010).
M. Chan and S. Ng, AIP Conf. Proc., 2016, 20035 (2018).
H. S. Zakria, M. H. D. Othman, R. Kamaludin and A. Jilani, IOP Conf. Ser.: Mater. Sci. Eng., 1142, 12014 (2021).
H. A. Tsai, D. H. Huang, S. C. Fan, Y. C. Wang, C. L. Li, K.-R. Lee and J.-Y. Lai, J. Membr. Sci., 198, 245 (2002).
M. Khayet, Chem. Eng. Sci., 58, 3091 (2003).
M. R. M. Abed, S. C. Kumbharkar, A. M. Groth and K. Li, J. Membr. Sci., 407, 145 (2012).
B. Maity, R. K. R. A. L. Kanasan and S. Abdul Rahman, Mater. Today Proc., 41, 136 (2021).
A. R. Kamble, C. M. Patel and Z. V. P. Murthy, Sep. Sci. Technol., 54, 311 (2018).