Effect of UV irradiation on PAN precursor fibers and stabilization process
Tóm tắt
A low-cost rout for modification the polyacrylontrile(PAN) precursor fibers was developed. The approach involved pretreatment PAN precursor fibers with UV irradiation for various periods of time before the fibers were stabilized. The effect of UV irradiation on the chemical structure, orientation factor, density, crystallite size and morphology of the fibers in the process of stabilization was characterized by use of fourier transform infrared spectroscopy(FTIR), float-sink procedure, X-ray diffraction(XRD), scanning electron microscope(SEM), respectively. The results showed that UV irradiation could increase the density of the fibers in stabilization process. FTIR analysis indicated that the cyclization of nitrile groups was initiated at room temperature by UV irradiation. The transformation of C≡N groups to C=N ones was accelerated in the process of stabilization. The orientation factor of irradiated fibers was also increased. The crystallite size was decreased at first and increased later, and the better irradiation time of UV was 3 min according to the XRD test. SEM analysis indicated that irradiation could decrease the internal and surface defects of the stabilized fibers treated at 300 °C.
Tài liệu tham khảo
Rey W N, Sharp J V. Crystal Shear Limit to Carbon Fiber Strength[J]. Carbon, 1974, 12(2): 103–110
Mun G S, Kensuke S, Tetsuya T, et al. Application of a High Magnetic Field in the Carbonization Process to Increase the Strength of Carbon Fibers[J]. Carbon, 2002, 40(5): 2 013–2 020
Sung M G, Yusuke K. Strengthening of Carbon Fibers by a Magnetic Field Imposed in the Stabilization and Carbonization Process[J]. Materials Science and Engineering A, 2008, 488(1–2): 247–251
Fitzer E, Frohs W, Heine M. Optimization of Stabilization and Carbonization Treatment of PAN Fibers and Structural Characterization of the Resulting Carbon Fibers[J]. Carbon, 1986, 24(4): 387–395
Amit K N, Robert A W, Sarah P, et al. UV Assisted Stabilization Routes for Carbon Fiber Precursors Produced from Melt-processible Polyacrylonitrile Terpolymer[J]. Carbon, 2005, 43(5): 1 065–1 072
J Dietrich, P Hirt, H. Herlinger. Electron-beam-induced Cyclisation to Obtain C-fiber Precursors from Polyacrylonitrile Homopolymers[J]. European Polymer Journal, 1996, 32(5): 617–623
Aggour YA, Aziz M S. Degradation of Polyacrylonitrile by Low Energy Ion Beam and UV Radiation[J]. Polymer Testing, 2000, 19: 261–267
Cardoso Dos, Santos L G, Kawano Y. Degradation of Polyacrylonitrile by X-ray Radiation[J]. Polymer Degradation and Stabilization, 1994, 44(1): 27–32
Badawy S M, Dessouki A M. Cross-linked Polyacrylonitrile Prepared by Radiation-induced Polymerization Technique[J]. Journal of Physical Chemistry B, 2003, 107(41): 11 273–11 279
Hill DJT, Lang A P, O_Donnell J H, et al. The Effect of γ-radiation on Polyacrylonitrile[J]. Polymer Degradation and Stabilization, 1992, 38(3): 193–203
M C Paiva, P Kotasthane, D D Edie, et al. UV Stabilization Route for Melt-processible PAN-based Carbon Fibers[J]. Carbon, 2003, 41(7): 1 399–1 409
Zhang Wangxi, Liu Jie. Effect of Post-spinning Modification on the PAN Precursors and Resulting Carbon Fibers[J]. Journal of Wuhan University of Technology-Materials Science Edition, 2006, 21(3): 45–48
Takata T, Hiroi I. Coloration in Acrylonitrile Polymers[J]. Journal of Polymer Science Part A, 1964, 2(4): 1 567–1 585
Wang Yangxiang, Wang Chengguo, Ma Yong, et al, Study of Micro Structure Morphology of PAN-based Carbon Fiber[J]. Journal of Functional Polymers, 2003, 16(1): 85–90
Meijie Yu, Yujun Bai, Chengguo Wang, et al. A New Method for the Evaluation of Stabilization Index of Polyacrylonitrile Fibers[J]. Materials Letters, 2007, 61(11–12): 2 292–2 294
Xu Lianghua, Zhang Wei, Tong Yuanjian, et al, Study on PAN Precursor Fibers Process Crystallization Behavior[J]. New Carbon Materials, 1997, 12(3): 31–33