Effect of Synthesis Conditions on the Structure and Phase Composition of Magnesium Diboride
Tóm tắt
Abstract—The effect of synthesis conditions exerted on the phase composition of MgB2 samples synthesized in a temperature range from 650 to 900°C and the features of the microstructure thereof are studied. It is shown that the maximum processing level of the initial boron and magnesium mixture into magnesium boride MgB2 with a minimum content of impurity phases of magnesium oxide and higher magnesium borides can be achieved in the samples after annealing in a temperature range from 650 to 750°C for 1 h upon a preliminary compaction pressure amounting to 630–640 MPa.
Tài liệu tham khảo
Abrahamsen, A.B., Magnusson, N., Jensen, B.B., and Runde, M., Large superconducting wind turbine generators, Energy Procedia, 2012, vol. 24, pp. 60–67.
Bruce, R. and Baudouy, B., Cryogenic design of a large superconducting magnet for astroparticle shielding on deep space travel missions, Phys. Procedia, 2015, vol. 67, pp. 264–269.
Naito, T., Sasaki, T., and Fujishiro, H., Trapped magnetic field and vortex pinning properties of MgB2 superconducting bulk fabricated by a capsule method, Supercond. Sci. Tehnol., 2012, vol. 25, pp. 29–38.
Fujishiro, H., Naito, T., Oyama, M., Arayashiki, T., et al., Numerical simulation of trapped field and temperature rise in MgB2 bulks magnetized by pulsed field, IEEE Trans. Appl. Supercond., 2013, vol. 23, no. 3, pp. 185–191.
Bhagurkar, A.G., Yamamoto, A., Hari Babu, N., et al., Synthesis of dense bulk MgB2 by an infiltration and growth process, Supercond. Sci. Technol., 2015, vol. 28, pp. 18–32.
Kuznetsova, E.I., Sudareva, S.V., Krinitsina, T.P., et al., Mechanism of the formation and specific features of the structure of massive samples of compound MgB2, Phys. Met. Metallogr., 2014, vol. 115, no. 2, pp. 175–185.
Kuznetsova, E.I., Akshentsev, Y.N., Esin, V.O., et al., Mechanisms of the formation of a bulk superconducting phase MgB2 at high temperatures, Phys. Solid State, 2015, vol. 57, no. 5, pp. 873–879.