Effect of Isothermal Temperature on Microstructure and Mechanical Properties of High Al–Low Si TRIP Steel
Tóm tắt
In this study, the effect of isothermal temperature on microstructure and mechanical properties of a high Al–low Si TRIP steel was investigated using scanning electron microscopy, transmission electron microscopy, X-ray diffraction, electron back scattered diffraction, and tensile test. The results show that typical microstructure containing ferrite, bainite, and retained austenite can be obtained when two-stage heat treatment process was utilized. When annealing temperature is 840 °C and austempering temperature is 400 °C, the tensile strength is 542 MPa and the product of strength and elongation is 17,685 MPa%. The morphologies and stability of the retained austenite in low silicon/high aluminum TRIP steel were finally discussed.
Tài liệu tham khảo
E.P. Kwon, S. Fujieda, K. Shinoda, S. Suzuki, Mater. Sci. Eng. A 528, 5007 (2011)
B.C. de Cooman, Curr. Opin. Solid State Mater. Sci. 8, 285 (2004)
G.K. Tirumalasetty, M.A. van Huis, C. Kwakernaak, J. Sietsma, W.G. Sloof, H.W. Zandbergen, Acta Mater. 60, 1311 (2012)
E. Girault, A. Martens, P. Jacques, Y. Houbaert, B. Verlinden, J. van humbeeck, Scr. Mater. 44, 885 (2001)
S. Zhang, K.O. Findley, Acta Mater. 61, 1895 (2013)
S. Lee, S.J. Lee, B.C. de Cooman, Scr. Mater. 65, 225 (2011)
H.K.D.H. Bhadeshia, ISIJ Int. 42, 1059 (2002)
M. Gomez, C.I. Garca, D.M. Haezebrouck, A.I. Deardo, ISIJ Int. 49, 302 (2009)
H.T. Jiang, W. Ding, D. Tang, J. Iron Steel Res. Int. 19, 29 (2012)
N. Imai, N. Komatsubara, K. Kunishige, CAMP ISIJ 8, 572 (1995)
L. Li, B.C. De Cooman, P. Wollants, Y.L. He, X.D. Zhou, J. Mater. Sci. Technol. 20, 135 (2004)
E.M. Bellhouse, J.M. McDermid, Mater. Sci. Eng. A 491, 39 (2008)
E.M. Bellhouse, A.I.M. Mertens, J.R. McDermid, Mater. Sci. Eng. A 463, 147 (2007)
J. Mahieu, B.C. de Cooman, J. Maki, S. Claessens, Ironmak. Steelmak. 29, 29 (2002)
J. Maki, J. Mahieu, B.C. de Cooman, S. Claessens, Mater. Sci. Technol. 19, 125 (2003)
J. Kobayashi, D. Ina, N. Yoshikawa, K. Sugimoto, ISIJ Int. 52, 1894 (2012)
A. Kammouni, W. Saikaly, M. Dumont, C. Marteau, X. Bano, A. Charai, Mater. Sci. Eng. A 518, 89 (2009)
S. Kim, C.G. Lee, I. Choi, S. Lee, Metall. Mater. Trans. A 32, 505 (2001)
Y. Sakuma, D. Matlock, G. Krauss, Metall. Mater. Trans. A 23, 1221 (1992)
Q.X. Feng, L.F. Li, W.Y. Yang, Z.Q. Sun, Mater. Sci. Eng. A 603, 169 (2014)
I.B. Timokhina, P.D. Hodgson, E.V. Pereloma, Metall. Mater. Trans. A 34, 1599 (2003)
J. Chiang, B. Lawrence, J.D. Boyd, A.K. Pilkey, Mater. Sci. Eng. A 528, 4516 (2011)
A. Mark, M. Westphal, D. Boyd, J. McDermid, D. Embury, Can. Metall. Q. 48, 237 (2009)
I.B. Timokhina, P.D. Hodgson, E.V. Pereloma, Metall. Mater. Trans. A 35, 2331 (2004)
X.C. Xiong, B. Chen, M.X. Huang, J.F. Wang, L. Wang, Scr. Mater. 68, 321 (2013)
Q. Furnémont, M. Kempf, P.J. Jacques, M. Göken, F. Delannay, Mater. Sci. Eng. A 328, 26 (2002)