Direct Preparation of Nanoscale Thin Films of Poly(vinylidene fluoride) Containing β‐Crystalline Phase by Heat‐Controlled Spin Coating

Macromolecular Chemistry and Physics - Tập 209 Số 24 - Trang 2516-2526 - 2008
Subramaniyan Ramasundaram1, Sun Yoon1, Kap Jin Kim2, Jong Soon Lee3
1Department of Advanced Polymer and Fiber Materials, College of Environment and Applied Chemistry, Kyung Hee University, Yongin‐si, Gyeonggi‐do 446‐701, South Korea
2Department of Advanced Polymer & Fiber Materials, College of Environment and Applied Chemistry, Kyung Hee University, Yongin‐si, Gyeonggi‐do 446‐701, South Korea. Fax: +82 31 204‐8114
3Analytical Research Center, Hyosung R&DB Labs, Anyang‐si, Gyeonggi‐do 431‐080, South Korea

Tóm tắt

AbstractNanoscale thin films of PVDF containing the β‐crystalline phase were directly prepared by heat‐controlled spin coating without the influence of external stimuli either in the form of additives or post‐treatments. Sample preparation was carried out at different temperatures, ranging from 10 to 70 °C. At elevated temperatures (40, 50, 60 and 70 °C), PVDF was crystallized into the β‐phase, while at near‐ambient conditions (20 and 30 °C) it was crystallized into the α‐phase. Some samples exhibited a phase‐segregated morphology, with varying particle sizes depending on the preparation temperature. The ferroelectric nature of a typical sample, prepared at 40 °C, was visualized by piezoresponse imaging studies.magnified image

Từ khóa


Tài liệu tham khảo

10.1063/1.1533844

10.1126/science.220.4602.1115

10.1080/01411598908206863

10.1016/0032-3861(81)90058-6

10.1002/pol.1966.150040420

10.1002/pol.1972.160100613

10.1007/BF01739296

10.1002/pol.1978.180160516

10.1002/adma.200304911

10.1002/app.24135

10.1002/polb.10223

10.1002/cvde.200606505

10.1016/0040-6090(91)90269-4

Park S. H., 1999, J. Korean Phys. Soc., 35, 431

10.1016/0040-6090(91)90090-K

10.1016/0040-6090(90)90198-M

Chung M. Y., 2001, J. Korean Phys. Soc., 38, 117

10.1063/1.371279

10.1007/s10854-006-0010-7

10.1143/JJAP.39.6358

10.1063/1.2740117

10.1063/1.1540231

10.1038/nmat1269

10.1109/JPROC.2005.851235

10.1038/nmat1443

10.1038/nature02498

10.1002/adma.200601474

10.1063/1.2723678

10.1080/00222346808212449

10.1080/10584580601098530

10.1021/ma011744f

10.1002/marc.200800108

10.1063/1.2352799

10.1143/JJAP.46.6976

10.1063/1.2830701

10.1021/ma000094x

10.1016/j.orgel.2003.12.007

10.1002/1439-2054(20020601)287:6<412::AID-MAME412>3.0.CO;2-V

S.Ramasundaram S.Yoon C. W.Choi A. A.Prabu K. J.Kim Proceedings of the Korean Polymer Society Conference Ilsan Korea Sep.2007 p.84.

10.1002/polb.1988.090260405

10.1063/1.2710277

10.1016/j.jcis.2007.05.019

10.1002/(SICI)1521-4095(200004)12:7<498::AID-ADMA498>3.0.CO;2-H

10.1021/ma010240e

10.1007/BF00486309

10.1016/j.vibspec.2005.11.005

10.1016/j.eurpolymj.2004.11.022

10.1002/polb.20223

10.1590/S0103-50532002000500027

10.1039/b408857n

10.1016/S0167-9317(04)00100-5

10.1021/la011728b

10.1016/j.apsusc.2005.10.038

10.1016/S0014-3057(01)00183-5

10.1143/JJAP.37.3834

10.1002/masy.200750303

Thông tin
Thông tin xuất bản

Macromolecular Chemistry and Physics

Tập 209 Số 24

2516-2526

Thông tin tác giả