Development of a new rapid, relevant and reliable (R3) test method to evaluate the pozzolanic reactivity of calcined kaolinitic clays

Cement and Concrete Research - Tập 85 - Trang 1-11 - 2016
François Avet1, Ruben Snellings1,2, Adrián Alujas Díaz3, Mohsen Ben Haha4, Karen Scrivener1
1Laboratory of Construction Materials, EPFL STI IMX LMC Station 12, CH-1015, Lausanne, Switzerland
2Sustainable Materials Management, VITO, 2400 Mol, Belgium
3Centro de Estudios de Quimica Aplicada, Universidad Central de Las Villas, 54830 Santa Clara, Cuba
4Heidelberg Technology Center GmbH, Rohrbacher Str. 95, 69181 Leimen, Germany

Tóm tắt

Từ khóa


Tài liệu tham khảo

Fernandez, 2011, The origin of the pozzolanic activity of calcined clay minerals: a comparison between kaolinite, illite and montmorillonite, Cem. Concr. Res., 41, 113, 10.1016/j.cemconres.2010.09.013

He, 1995, Pozzolanic reactions of six principal clay minerals: activation, reactivity assessments and technological effects, Cem. Concr. Res., 25, 1691, 10.1016/0008-8846(95)00165-4

Chen, 2000, Microstructural evolution of mullite during the sintering of kaolin powder compacts, Ceram. Int., 26, 715, 10.1016/S0272-8842(00)00009-2

Antoni, 2012, Cement substitution by a combination of metakaolin and limestone, Cem. Concr. Res., 42, 1579, 10.1016/j.cemconres.2012.09.006

Alujas, 2015, Pozzolanic reactivity of low grade kaolinitic clays: influence of calcination temperature and impact of calcination products on OPC hydration, Appl. Clay Sci., 108, 94, 10.1016/j.clay.2015.01.028

Antoni, 2013

Silva, 1990, Hydration of cements based on metakaolin: thermochemistry, Adv. Cem. Res., 167, 10.1680/adcr.1990.3.12.167

Frattini, 1949, Ricerche sulla calce di idrolisi nelle paste di cemento, Ann. Chim., 39, 616

Tironi, 2013, Assessment of pozzolanic activity of different calcined clays, Cem. Concr. Compos., 37, 319, 10.1016/j.cemconcomp.2013.01.002

Donatello, 2010, Comparison of test methods to assess pozzolanic activity, Cem. Concr. Compos., 32, 121, 10.1016/j.cemconcomp.2009.10.008

Hanna, 1974, Evaluation of the activity of pozzolanic materials, J. Appl. Chem. Biotech., 24, 751, 10.1002/jctb.5020241206

Shvarzman, 2003, The effect of dehydroxylation/amorphization degree on pozzolanic activity of kaolinite, Cem. Concr. Res., 33, 405, 10.1016/S0008-8846(02)00975-4

EN196–1, 2006

Lothenbach, 2007, Effect of temperature on the pore solution, microstructure and hydration products of Portland cement pastes, Cem. Concr. Res., 37, 483, 10.1016/j.cemconres.2006.11.016

Lothenbach, 2008, Thermodynamic modelling of the effect of temperature on the hydration and porosity of Portland cement, Cem. Concr. Res., 38, 1, 10.1016/j.cemconres.2007.08.017

Gallucci, 2013, Effect of temperature on the microstructure of calcium silicate hydrate (C-S-H), Cem. Concr. Res., 53, 185, 10.1016/j.cemconres.2013.06.008

N. P18-513, 2012

Snellings, 2014, Use of X-ray diffraction to quantify amorphous supplementary cementitious materials in anhydrous and hydrated blended cements, Cem. Concr. Res., 64, 89, 10.1016/j.cemconres.2014.06.011

Perkins, 1999, Solubility of ettringite (Ca6[Al(OH)6]2(SO4)3·26H2O) at 5–75°C, Geochim. Cosmochim. Acta, 63, 1969, 10.1016/S0016-7037(99)00078-2

Li, 1996, The U phase formation in cement-based systems containing high amounts of Na2SO4, Cem. Concr. Res., 26, 27, 10.1016/0008-8846(95)00189-1

Pöllmann, 2006, Syntheses, properties and solid solution of ternary lamellar calcium aluminate hydroxi salts (AFm-phases) containing SO4 2-, CO3 2-, and OH-, Neues Jahrbuch für Mineralogie - Abhandlungen, J. Min. Geol., 182, 173

Deschner, 2013, Effect of temperature on the hydration of Portland cement blended with siliceous fly ash, Cem. Concr. Res., 52, 169, 10.1016/j.cemconres.2013.07.006

Snellings, 2015, Rapid screening tests for supplementary cementitious materials: past and future, Mater. Struct.