Dental Composites/Glass Ionomers: the Materials

Advances in dental research - Tập 6 Số 1 - Trang 44-49 - 1992
R.L. Bowen1, William A. Marjenhoff1
1American Dental Association Health Foundation Paffenbarger Research Center National Institute of Standards and Technology Gaithersburg, Maryland 20899

Tóm tắt

Most commercial dental composites contain liquid dimethacrylate monomers (including BIS-GMA or variations of it) and silica-containing compositions as inorganic reinforcing filler particles coated with methacrylate-functional silane coupling agents to bond the resin to the filler. They also contain initiators, accelerators, photo-initiators, photosensitizers, polymerization inhibitors, and UV absorbers.Durability is a major problem with posterior composites. The typical life-span of posterior composites is from three to 10 years, with large fillings usually fewer than five years. Polymerization shrinkage and inadequate adhesion to cavity walls are remaining problems. Some pulp irritation can occur if deep restorations are not placed over a protective film. Some have advocated the use of glass-ionomer cement as a lining under resin composite restorations in dentin.The concept of glass-ionomer cements (GICs) was introduced to the dental profession in the early 1970's. Current GICs may contain poly(acrylic acid) or a copolymer. Higher-molecular-weight copolymers may also be used to improve the physical properties of some GICs. Stronger and less-brittle hybrid materials have been produced by the addition of watersoluble compatible polymers to form light-curing GIC formulations.The ion-leachable aluminosilicate glass powder, in an aqueous solution of a polymer or copolymer of acrylic acid, is attacked by the hydrated protons of the acid, causing the release of aluminum and calcium ions. Salt bridges are formed, and a gel matrix surrounds the unreacted glass particles. The matrix is adhesive to mineralized tissues. Provisions must be made for maintenance of the water balance of restorations for the first 24 hours. A varnish to seal newly-placed restorations is provided by most manufacturers. The introduction of metal powder to GICs significantly improved abrasion resistance.

Từ khóa


Tài liệu tham khảo

Antonucci JM, Trans 13th Ann Meeting

Antonucci JM, 1989, J Dent Res, 68, 555, 10.1177/00220345890680040401

Arnold J., 1990, Aust Dent J, 35, 185, 10.1111/j.1834-7819.1990.tb05887.x

10.1038/sj.bdj.4805723

Bergman M., 1990, Int Dent J, 40, 4

10.1016/0022-3913(89)90325-9

Blagojevic B., 1989, Aust Dent J, 33, 320

10.1177/00220345560350030501

Bowen RL, 1962, Dental filling material comprising vinyl silane treated fused silica and a binder consisting of the reaction product of bis phenol and glycidyl acrylate

Bowen RL, 1965, Silica-resin direct filling material and method of preparation

Bowen RL, 1965, Method of preparing a monomer having phenoxy and methacrylate groups linked by hydroxy glyceryl groups

10.1016/S0022-3913(68)80020-4

10.1016/0022-3913(90)90196-J

10.14219/jada.archive.1953.0212

10.1016/0022-3913(89)90278-3

10.1177/00220345760550060501

10.14219/jada.archive.1990.0016

Croll TP, 1986, Quint Int, 17, 607

10.1016/0109-5641(89)90113-9

10.14219/jada.archive.1990.0240

10.1177/00220345890680080401

10.1016/0022-3913(88)90176-X

Goldstein RE, 1989, Dent Clin North Am, 33, 305, 10.1016/S0011-8532(22)01195-8

10.1259/dmfr.18.1.2599234

Guelmann M., 1989, J Dent Child, 56, 277

Henschel Cjl, 1949, J Dent Res, 28, 528

10.14219/jada.archive.1990.0011

10.3109/10408368109105861

10.1111/j.1834-7819.1989.tb00705.x

McKinney JE, 1986, J Dent Res, 66, 1134, 10.1177/00220345870660060801

10.1038/sj.bdj.4804525

10.1038/sj.bdj.4805511

McLean JW, 1985, Powdered dental material and process for the preparation thereof

McLean JW, 1985, Quint Int, 16, 1055

Mertz-FairhurstEJ,, 1991, Am J Dent, 4, 43

10.1111/j.1365-2591.1987.tb00582.x

Mitra SB, 1991, JDentRes, 70, 72

10.1177/00220345910700011301

Mjör IA, Wennberg A. (1985). Biocompatibility considerations of composite resins. A discussion paper. In: Vanherle G, Smith DC, editors. Posterior Composite Resin Dental Restorative Materials. Amsterdam (The Netherlands): Peter Szulc Publishing, 83-90.

10.1177/00220345900690100601

10.1111/j.1834-7819.1989.tb04623.x

Mount GJ, 1990, Quint Int, 21, 93

10.14219/jada.archive.1990.0015

10.1177/00220345880670120201

10.14219/jada.archive.1953.0215

Paffenbarger GC, 1938, J Am Dent Assoc, 25, 32

10.1016/0022-3913(90)90166-A

10.1177/00220345860650021101

Reeves GW, 1990, Am J Dent, 3, 195

10.1177/00220345550340041501

10.1177/00220345550340041401

Ruyter E., 1984, Tandlakartidningen, 76, 1207

10.3109/00016357809027569

10.1016/S0109-5641(88)80100-3

10.1111/j.1365-2842.1990.tb01423.x

Saunders WP, 1990, J Dent Child, 57, 433

Schmitt WP, 1985, Mixing component for dental glass ionomer cements

Shortall AC, 1989, Int J Prosthodont, 2, 217

10.14219/jada.archive.1990.0018

10.1111/j.1834-7819.1990.tb05885.x

10.1016/0300-5712(90)90021-6

10.1016/0022-3913(78)90091-4

Smith DC, 1968, Br Dent J, 125, 381

Smith DC, 1971, J Can Dent Assoc, 37, 22

10.14219/jada.archive.1990.0002

10.1016/0022-3913(90)90209-U

Suzuki M., 1976, Dental cement composition

10.14219/jada.archive.1990.0001

Tezuka C., 1978, Setting solution for dental glass ionomer cements

Tylman SC, 1946, Acrylic and other synthetic resins used in dentistry

10.3109/00016358909004809

10.1177/00220345900690081701

10.1111/j.1365-2842.1990.tb01404.x

Wendt, SL Jr, 1991, Am J Dent, 4, 10

10.1016/0300-5712(77)90070-7

10.1002/jctb.5020211101

10.1038/sj.bdj.4802810

Wilson AD, 1988, Glass ionomer cement

10.1038/sj.bdj.4805517

Wilson EG, 1990, Dent Clin North Am, 34, 27, 10.1016/S0011-8532(22)01161-2

10.1111/j.1834-7819.1985.tb02526.x

Thông tin
Thông tin xuất bản

Advances in dental research

Tập 6 Số 1

44-49

Thông tin tác giả