Tính không đồng nhất trong biến dạng trên các mặt cắt ngang của hợp kim magiê được chế biến bằng phương pháp xoắn áp lực cao

Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science - Tập 42 - Trang 3013-3021 - 2011
Roberto B. Figueiredo1, Maria Teresa P. Aguilar2, Paulo R. Cetlin3, Terence G. Langdon4,5
1Department of Metallurgical and Materials Engineering, Universidade Federal de Minas Gerais, Belo Horizonte, Brazil
2Department of Materials and Construction, Universidade Federal de Minas Gerais, Belo Horizonte, Brazil
3Department of Mechanical Engineering, Universidade Federal de Minas Gerais, Belo Horizonte, Brazil
4Departments of Aerospace & Mechanical Engineering and Materials Science, University of Southern California, Los Angeles, USA
5Materials Research Group, School of Engineering Sciences, University of Southampton, Southampton, United Kingdom

Tóm tắt

Các đĩa của hợp kim magiê AZ31 được ép đùn đã được xử lý bằng phương pháp xoắn áp lực cao (HPT) ở áp suất 6.0 GPa qua 1/4, 1 và 5 vòng quay, ở cả nhiệt độ phòng (296 K (23 °C)) và ở nhiệt độ cao hơn là 463 K (190 °C). Các mặt cắt ngang của các đĩa đã được kiểm tra sau khi chế biến, và cho thấy có một mức độ không đồng nhất cao trong tất cả các mẫu. Sự không đồng nhất này được thể hiện qua tính chất của các mẫu chảy, qua sự phân bố kích thước hạt, và qua các phép đo độ cứng vi mô toàn diện. Các kết quả cho thấy có thể tăng gấp đôi độ bền của hợp kim ở một số vùng của đĩa sau khi chế biến qua 5 vòng quay ở nhiệt độ phòng.

Từ khóa


Tài liệu tham khảo

R.Z. Valiev, R.K. Islamgaliev, and I.V. Alexandrov: Progr. Mater. Sci., 2000, vol. 45, pp. 103–89. Y. Saito, H. Utsunomiya, N. Tsuji, and T. Sakai: Acta Mater., 1999, vol. 47, pp. 579–83. R.Z. Valiev and T.G. Langdon: Progr. Mater. Sci., 2006, vol. 51, pp. 881–981. A.P. Zhilyaev and T.G. Langdon: Progr. Mater. Sci., 2008, vol. 53, pp. 893–979. Z. Horita, T. Fujinami, and T.G. Langdon: Mater. Sci. Eng. A, 2001, vol. A318, pp. 34–41. A.P. Zhilyaev, B.K. Kim, J.A. Szpunar, M.D. Baró, and T.G. Langdon: Mater. Sci. Eng. A, 2005, vol. A391, pp. 377–89. R.Z. Valiev, Y. Estrin, Z. Horita, T.G. Langdon, M.J. Zehetbauer, and Y.T. Zhu: JOM 2006, vol. 58 (4), pp. 33–39. G. Sakai, K. Nakamura, Z. Horita, and T.G. Langdon: Mater. Sci. Eng. A, 2005, vol. A406, pp. 268–73. R. Pippan, S. Scheriau, A. Hohenwarter, and M. Hafok: Mater. Sci. Forum, 2008, vols. 584–586, pp. 16–21. A. Yamashita, Z. Horita, and T.G. Langdon: Mater. Sci. Eng. A, 2001, vol. A300, pp. 142–47. R.B. Figueiredo, P.R. Cetlin, and T.G. Langdon: Acta Mater., 2007, vol. 57, pp. 4769–79. F. Kang, J.T. Wang, and Y. Peng: Mater. Sci. Eng. A, 2008, vol. A487, pp. 68–73. R.B. Figueiredo, P.R. Cetlin, and T.G. Langdon: Metall. Mater. Trans. A, 2010, vol. 41A, pp. 778–86. P.R. Cetlin, M.T.P. Aguilar, R.B. Figueiredo, and T.G. Langdon: J. Mater. Sci., 2010, vol. 45, pp. 4561–70. J. Čížek, I. Procházka, B. Smola, I. Stulíková, R. Kužel, Z. Matěj, V. Cherkaska, R.K. Islamgaliev, and O. Kulyasova: Mater. Sci. Eng. A, 2007, vol. A462, pp. 121–26. B.J. Bonarski, E. Schafler, B. Mingler, W. Skrotzki, B. Mikulowski, and M.J. Zehetbauer: J. Mater. Sci., 2008, vol. 45, pp. 7513–18. R.Z. Valiev, Yu.V. Ivanisenko, E.F. Rauch, and B. Baudelet: Acta Mater., 1996. vol. 44, pp. 4705–12. F. Wetscher, A. Vorhauer, R. Stock, and R. Pippan: Mater. Sci. Eng. A, 2004, vols. A387–A389, pp. 809–16. F. Wetscher, R. Pippan, S. Sturm, F. Kauffmann, C. Scheu, and G. Dehm: Metall. Mater. Trans. A, 2006, vol. 37A, pp. 1963–68. M. Kawasaki, B. Ahn, and T.G. Langdon: Acta Mater., 2010, vol. 58, pp. 919–30. M. Kawasaki, B. Ahn, and T.G. Langdon: Mater. Sci. Eng. A, 2010, vol. A527, pp. 7008–16. Y. Cao, Y.B. Wang, S.N. Alhajeri, X.Z. Liao, W.L. Zheng, S.P. Ringer, T.G. Langdon, and Y.T. Zhu: J. Mater. Sci., 2010, vol. 45, pp. 765–70. Y. Cao, M. Kawasaki, Y.B. Wang, S.N. Alhajeri, X.Z. Liao, W.L. Zheng, S.P. Ringer, Y.T. Zhu, and T.G. Langdon: J. Mater. Sci., 2010, vol. 45, pp. 4545–53. Y. Cao, Y.B. Wang, R.B. Figueiredo, L. Chang, X.Z. Liao, M. Kawasaki, W.L. Zheng, S.P. Ringer, T.G. Langdon, and Y.T. Zhu: unpublished research (2010). Y.Z. Tian, X.H. An, S.D. Wu, Z.F. Zhang, R.B. Figueiredo, N. Gao, and T.G. Langdon: Scripta Mater., 2010, vol. 63, pp. 65–68. A. Hohenwarter, A. Bachmaier, B. Gludovatz, S. Scheriau, and R. Pippan: Int. J. Mater. Res., 2009, vol. 100, pp. 1653–61. M. Kawasaki, R.B. Figueiredo, and T.G. Langdon: Acta Mater., 2011, vol. 59, pp. 308–16. R.B. Figueiredo and T.G. Langdon: unpublished research (2010). R.B. Figueiredo and T.G. Langdon: J. Mater. Sci., 2009, vol. 44, pp. 4758–62. R.B. Figueiredo and T.G. Langdon: Int. J. Mater. Res., 2009, vol. 100, pp. 1638–46. R.B. Figueiredo and T.G. Langdon: J. Mater. Sci., 2010, vol. 45, pp. 4827–36.
Thông tin
Thông tin xuất bản

Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

Tập 42

3013-3021

Thông tin tác giả