Cubic Phase Stabilization of Translucent Yttria‐Zirconia at Very Low Temperatures

Journal of the American Ceramic Society - Tập 50 Số 10 - Trang 532-537 - 1967
K. S. Mazdiyasni1, C. T. Lynch1, James S. Smith1
1Air Force Materials Laboratory, Wright‐Patterson Air Force Base, Ohio 45433

Tóm tắt

Simultaneous decomposition of yttrium and zirconium alkozides was used to obtain an almost ideal mixture of powders of high surface activity. From this powder a translucent body, “Zyttrite,” was made with a grain size of less than 1μ. The mixed oxide was consolidated into a stabilized body by firing at 1000°C for 30 min. This is indicative of a phenomenal increase in solid state reactivity. High‐density fully stabilized cubic solid solutions of 6 mole % Y2O3‐ZrO2 were obtained on sintering at 1450°C. A typical specimen had a density of 5.9 g/cm3, a coefficient of thermal expansion of 11 × 10−6 in./in.°C, and a grain size of 2 to 4μ. Test pieces withstood 2200°C firings in air for 262 hr with grain growth of 35 to 50μ and virtually no change in composition, density, or stabilization.

Từ khóa


Tài liệu tham khảo

1959, General Electric Announces New Type of Ceramic Material, Am. Ceram. Soc. Bull., 38, 507

R. L.Coble “Transparent Al2O3and Method of Preparation ”U. S. Pat. No. 3 026 210 March 20 1962.

10.1149/1.2778219

E. I.Ryschkewitsch “Stabilization of Zirconia ”U. S. Pat. No. 2 910 371 October 27 1959.

Fu‐K'ang A. K., 1963, Phase Relations in the System Y2O3‐ZrO2: II, Izv. Akad. Nauk SSSR, Old. Khim. Nauk, 601

10.6028/jres.035.028

Dietzel A., 1953, Zirconium Dioxide and Binary Systems with Zirconia as Component, Ber. Deut. Keram. Ges., 30, 47

10.1111/j.1151-2916.1964.tb14368.x

D. C.BradleyandW.Wardlaw “Zirconium Alkoxides ”J. Chem. Soc. 1951 280–85.

10.1021/ja01637a080

10.1021/ic50037a003

K. S.Mazdiyasni C. T.Lynch andJ. S.Smith “Yttrium Dysprosium and Ytterbium Alkoxides and Process for Making Same ”U. S. Pat. Xo. 3 278 571 October 11 1966.

10.1111/j.1151-2916.1965.tb14764.x

K. S.Mazdiyasni C. T.Lynch andJ. J.Krochmal “Method for Making High Purity Fine Particle Oxides ”U. S. Pat. No. 3 297 414 January 10 1967.

K. S.MazdiyasniandC. T.Lynch “Synthesis and Pyrolysis of Metal Alkoxides as Potential Refractory Oxide Coatings for Graphite ”Rept. No. ASD‐TDR‐63–322 May 1963.

Pauling Linus, 1960, Nature of the Chemical Bond and Structure of Molecules and Crystals

Mazdiyasni K. S., 1964, Special Ceramics, 115

G.Denman “Automatic Recording Dilatometer for Thermal Expansion Measurements to 2000°F ”Rept. No. ASD‐TDR‐62–315 May 1962.

Burke J., General Electric Research Laboratories

L. L.Fehrenbacher L. A.Jacobson andC. T.Lynch “Sintering Behavior of Stabilized ZrO2Compositions ”Rept. No. AFML‐TR‐65–394 20pp. December 1965.

Fehrenbacher L. L., 1965, Proceedings of the Fourth Conference on Rare Earth Research, 687

Thông tin
Thông tin xuất bản

Journal of the American Ceramic Society

Tập 50 Số 10

532-537

Thông tin tác giả