Crack Initiation in a Coated and an Uncoated Nickel-Base Superalloy Under TMF Conditions

Journal of Engineering for Gas Turbines and Power - Tập 120 Số 4 - Trang 792-795 - 1998
Peter K. Johnson1, M. Arana1, K. Ostolaza1, J. Bressers1
1Joint Research Centre, European Commission, P.O. Box 2, 1755 ZG, Petten, The Netherlands

Tóm tắt

A thermomechanical fatigue (TMF) cycle, intended to represent aeroengine blade working conditions, was selected for carrying out tests on uncoated and aluminide coated SRR99 samples until test piece failure. Optical images of the surface of test pieces were collected during testing to monitor surface crack initiation and accompanying transformations. Using these images, surface changes were quantified as a function of time. Post test each sample was taken through an incremental polishing procedure to allow damage in the tested material to be studied as a function of depth, using optical microscope-based quantitative metallography and scanning electron microscopy (SEM). The relationship between the observed surface changes and the damage built-up subsurface was examined. Differences in damage density on the surface and subsurface planes between coated and uncoated samples could accommodate the observed life reductions.

Từ khóa


Tài liệu tham khảo

Bain, K. R., 1985, “The Effects of Coatings on the Thermal Mechanical Fatigue Life of a Single Crystal Turbine Blade Material,” American Institute of Aeronautics and Astronautics, paper AIAA-85-1366.

Bressers, J., Estevas-Guilmain, J., De Cat, R., Knight, S., and Ridge, J., 1993,“An Automated Computer Vision System for Monitoring the Initiation and Growth of Microcracks,” R. A. Ainsworth and R. P. Skelton, eds., Behaviour of Defects at High Temperature, ESIS 15, Mechanical Engineering Publications, London.

Bressers, J., Timm, J., Williams, S., Bennett, A., Affeldt, E., 1996, “Effects of Cycle Type and Coating on the TMF Lives of a Single Crystal Nickel-Based Gas Turbine Alloy,” Thermomechanical Fatigue Behavior of Materials, M. J. Verrilli and M. J. Castelli, eds., ASME STP 1263, American Society for Testing and Materials, Philadelphia, pp. 82–95.

Christian, J. W., 1975, The Theory of Transformation in Metals and Alloys, Part I, second edition, Pergamon Press, Ltd, Oxford, England, p. 20.

Heine, J. E., Warren, J. R., and Cowles, B. A., 1986, “Thermal Mechanical Fatigue of Coated Blade Materials,” Report WRDC-TR-89-4027, Wright Research Development Centre, Wright-Patterson Air Force Base, OH.

Johnson, P. K., and Bressers, J., 1996, “Characteristics of a Population of Naturally Initiated Cracks That Evolves During the Thermomechanical Fatigue Testing of SRR99,” Proceedings International Symposium on Fatigue Under Thermal and Mechanical Loading, J. Bressers, L. Re´my, M. Steen, and J. L. Valle´s, eds., Kluwer Academic Publisher, Boston, MA, pp. 315-320.

Ostolaza, K., Johnson, P. K., Arana, M., and Bressers, J., 1996, “Effect of the Cycle Type on the Damage of a Diffusion Aluminide Coating on a Ni-Based Monocrystalline Superalloy Tested Under TMF Conditions,” Proceedings of the III Iberical workshop in Fracture, Luso (Portugal), Anales de la Meca´nica de la Fractura, Vol. 13, pp. 297–292.

Wood M. I. , 1989, “Mechanical Interactions Between Coatings and Super-alloys Under Conditions of Fatigue,” Surface and Coatings Technology, Vol. 39/40, pp. 29–42.

Wright, P. K., 1988, “Oxidation-Fatigue Interactions in Single-Crystal Superalloy,” Low Cycle Fatigue, ASTM STP 942, H. D. Solomon, G. R. Halford, L. B. Kaisan, and B. N. Leis, eds., American Society for Testing and Materials, Philadelphia, PA, pp. 558-575.

Thông tin
Thông tin xuất bản

Journal of Engineering for Gas Turbines and Power

Tập 120 Số 4

792-795

Thông tin tác giả