Compressive strength and creep properties of Ir-Nb-Zr alloys between 1473 and 2073 K
Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science - Tập 34 - Trang 2207-2215 - 2003
Tóm tắt
The microstructure and strength at 1473 and 2073 K and creep properties at 2073 K were investigated in three Ir-Nb-Zr alloys with the fcc and L12 two-phase structure. The microstructure and lattice misfit were investigated using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffractometry (XRD). Compression and creep tests were performed, and their deformation structures were observed using SEM and TEM. At 1473 K, the strength of the Ir-Nb-Zr alloys was higher than that of the binary Ir-Nb and Ir-Zr alloys, but they were almost equivalent at 2073 K. However, the ternary alloys showed great improvement on creep at 2073 K. The time for the 2 pct creep strain of the Ir-Nb-Zr alloy was about 100 hours, while it was 1 hour for the binary alloys. The deformation mechanisms for compressive strength and creep resistance in these Ir-Nb-Zr alloys are discussed in terms of the deformation structure.
Tài liệu tham khảo
N. Tanatsugu, T. Sato, Y. Naruo, T. Kashiwagi, T. Mizutani, T. Monji, and K. Hamabe: Acta Astronautica, 1997, vol. 40, pp. 165–70.
N.S. Stoloff: in Superalloys II, C.T. Sims, N.S. Stoloff, and W.C. Hagel, eds., John Willey & Sons, New York, NY, 1987.
Y. Yamabe, Y. Koizumi, H. Murakami, Y. Ro, T. Maruko, and H. Harada: Scripta Mater., 1996, vol. 35(2), pp. 211–15.
Y. Yamabe-Mitarai, Y. Ro, T. Maruko, and H. Harada: Metall. Mater. Trans. A, 1998, vol. 29A, pp. 537–49.
Y. Yamabe-Mitarai, Y. Ro, S. Nakazawa, T. Maruko, and H. Harada: Def. Diffus. Forum, 2001, vols. 188–190, pp. 171–84.
Y. Yamabe-Mitarai, S. Nakazawa, and H. Harada: Scripta Mater., 2000, vol. 43, pp. 1059–64.
Y. Yamabe-Mitarai, S. Nakazawa, and H. Harada: JSME Int. J. Ser. A, 2002, vol. 45(1), pp. 2–7.
A.M. Gyurko and J.M. Sanchez: Mater. Sci. Eng. A, 1993, vol. 170, pp. 169–75.
G.A. Miller: Master’s Thesis, University of Texas at Austin, Austin, TX, 1994.
C.A. Freitas and J.M. Sanchez: Proc. THERMEC ’97, TMS, Warrendale, PA, 1997, pp. 1567–73.
Y. Yamabe-Mitarai and H. Harada: J. Alloy and Comp., in press.
Y. Yamabe-Mitarai and H. Harada: Phil. Mag. Lett., 2002, vol. 82(3), pp. 109–18.
Y. Yamabe-Mitarai and H. Harada: Mater. Sci. Eng. A, in press.
Y. Yamabe-Mitarai and H. Harada: unpublished research, 2001.
T.M. Pollock and A.S. Argon: Acta Metall. Mater., 1992, vol. 40(1), pp. 1–30.
S. Tian, J. Zhang, X. Wu, H. Yang, Y. Xu, and Z. Hu: Metall. Mater. Trans. A, 2001, vol. 32A, pp. 2947–57.
R.D. Field, T.M. Pollock, and W.H. Murphy: Superalloys 1992, 1992, pp. 57–66.
A. Lasalmonie and J.L. Strudel: Phil. Mag., 1976, vol. 32(5), pp. 937–49.
M.V. Natahl, R.A. Mackay, and R.V. Miner: Metall. Trans. A, 1989, vol. 20A, pp. 133–41.
Y.F. Gu, Y. Yamabe-Mitarai, S. Nakazawa, and H. Harada: Scripta Mater., 2002, vol. 46, pp. 137–42.
Y. Yamabe-Mitarai, S. Nakazawa, and H. Harada: Material Science Forum, in press.
Y.F. Gu, Y. Yamabe-Mitarai, Y. Ro, and H. Harada: Key Eng. Mater., 2000, vols. 171–174, pp. 669–76.