Comparison of Various Solvent Media Efficiency in the Grinding of a Frit Containing Zirconium Oxide

Journal of the American Ceramic Society - Tập 86 Số 5 - Trang 864-866 - 2003
F. Andreola1, Maria Cristina D'Arrigo1, Cristina Leonelli1, Cristina Siligardi1, Gian Carlo Pellacani1,2
1Department of Environmental and Materials Engineering, Faculty of Engineering, University of Modena and Reggio Emilia, 41100 Modena, Italy
2*Member, American Ceramic Society.

Tóm tắt

In the present work thermal and chemical properties of a glass‐ceramic frit containing zirconium oxide are evaluated after milling in various polar and nonpolar solvents. Particle‐size distribution is one of the main variables investigated to evaluate the efficiency of several solvents. Milling in various solvents does not affect the thermal properties of the glass while the presence of polar groups in the solvent molecule increases the cation release from the glass.

Từ khóa


Tài liệu tham khảo

10.1016/S0955-2219(99)00155-7

Baldi G., 1994, Vetroceramici Appartenenti al Sistema CaO‐SiO2‐ZrO2 come Componenti di Smalti per Piastrelle, Ceramurgia, 24, 267

Andreola F., 1997, Wet Grinding Ceramic Frits: Effects of the Size of the Grinding Media, Grinding Time and Solid Content, Mater. Eng., 8, 171

Newton R. G., 1985, The Durability of Glass—A Review, Glass Technol., 26, 21

Povedano J. A. Hernandez, 1982, Reacciones de la Superficie del Vidrio con Soluciones Acuosas, Bol. Soc. Esp. Ceram. Vid., 21, 81

10.1002/9780470294420.ch46

Chiorboli P., 1987, Fondamenti di Chimica, 572

Weast R., 1976, Handbook of Chemistry and Physics, C75

Michalske T., 1988, The Fracture of Glass, Sci. Am., 234, 70

10.1016/S0022-3093(02)01421-7

Siligardi C., 2000, Sintering Criteria for Glass‐Ceramic Frits Belonging to CaO‐ZrO2‐SiO2 System, Am. Ceram. Soc. Bull, 78, 88

Buri A., 1990, Caratterizzazione e Reattivita di Materiali Speciali, 159

Thông tin
Thông tin xuất bản

Journal of the American Ceramic Society

Tập 86 Số 5

864-866

Thông tin tác giả